Deposizione elettrochimica di esacianoferrato di rame tramite un metodo "a due step"; caratterizzazione e valutazione delle prestazioni

In this thesis we have identified two electrochemical procedures for preparing two compounds of copper hexacyanoferrate (CuHCF) films with different compositions and structures. The deposition were carried out using a “two steps” method consisting in electrochemical oxidation of previously deposited metallic copper on carbon substrates (glassy carbon and graphite foil electrodes) in K3[Fe(CN)6] solution. Both films, CuHCF-methodA and CuHCF-methodB, were characterized by cyclic voltammetry (GC) and their study using XANES spectroscopy revealed evidence of different structures. Additionally, insertion and extraction of different cations (Na+, K+, Mg2+, Al3+ and Cs+) were performed and the results indicate that CuHCF-methodA has slightly better performances and operational stability than CuHCF-methodB. Data from galvanostatic charge-discharge tests confirme the latter observation. An application for amperometric detection of H2O2 and SEM micrographs are also reported for both films (method A and B). Comparing these results with a previous work of our research group, seems that the deposition of two different compounds using methodA and methodB is due to the different stoichiometry of ions Cu2+ e [Fe(CN)6]3– created near electrode surface during the dissolution step.

The effect of poly(lactide)-poly(carbonate) based block copolymers on the morphology and crystallization of double crystalline poly(lactide)/poly(ε-caprolactone) blends

Block copolymers of poly(lactide) and poly(carbonate) were synthetized in three different compositions and characterized by 1H-NMR and ATR analyses. The compatibilization effect of this copolymers on 80/20 (w/w%) PLA/PCL blend was evaluated. SEM micrographs show that all the blends exhibit the typical sea-island morphology characteristic of immiscible blends with PCL finely dispersed in droplets on a PLA matrix. Upon the addiction of the copolymers a reduction on PCL droplets size is observable. At the same time, a Tg depression of the PLA phase is detected when the copolymers are added in the blend. These results indicate that these copolymers are effective as compatibilizers. The copolymer that acts as the best compatibilizer is the one characterized by the same amount of PLA and PC as repeating units. As result, in the blend containing this copolymer PLA phase exhibits the highest spherulitic growth rate. An analyses on PLA phase crystallization behaviour from the glassy state within the blends was evaluated by DSC experiments. Isothermal cold crystallization of the PLA phase is enhanced up an order of magnitude upon the blending with PCL. Annealing experiments demonstrated that the crystallization of the PCL phase induces the formation of active nuclei in PLA when cooled above cooled below Tg. When the crystallization rate of PCL is retarded, a reduction on PLA nucleation is observed.