Damping and Thermomechanical behaviour of CFRP laminates modified with rubbery nanofibers

Nanofibrous membranes are a promising material for tailoring the properties of laminated CFRP composites by embedding them into the structure. This project aimed to understand the effect of number, position and thickness of nanofibrous modifications specifically on the damping behaviour of the resulting nano-modified CFRP composite with an epoxy matrix. An improvement of damping capacity is expected to improve a composites lifetime and fatigue resistance by prohibiting the formation of microcracks and consequently hindering delamination, it also promises a rise in comfort for a range of final products by intermission of vibration propagation and therefore diminution of noise. Electrospinning was the technique employed to produce nanofibrous membranes from a blend of polymeric solutions. SEM, WAXS and DSC were utilised to evaluate the quality of the obtained membranes before they were introduced, following a specific stacking sequence, in the production process of the laminate. A suitable curing cycle in an autoclave was applied to mend the modifications together with the matrix material, ensuring full crosslinking of the matrix and therefore finalising the production process. DMA was exercised in order to gain an understanding about the effects of the different modifications on the properties of the composite. During this investigation it became apparent that a high number of modifications of laminate CFRP composites, with an epoxy matrix, with thick rubbery nanofibrous membranes has a positive effect on the damping capacity and the temperature range the effect applies in. A suggestion for subsequent studies as well as a recommendation for the production of nano-modified CFRP structures is included at the end of this document.

Development of a novel heat treatment for high performances L-PBF Ti6Al4V alloy: microstructural and mechanical characterization

This work presents the experimental development of a novel heat treatment for a high performance Laser Powder Bed Fusion Ti6Al4V alloy. Additive manufacturing production processes for titanium alloys are particularly of interest in cutting-edge engineering fields, however, high frequency laser induced thermal cycles generate a brittle as built microstructure. For this reason, heat treatments compliant with near net shape components are needed before their homologation and usage. The experimental campaign focused on the development of a multi-step heat treatment leading to a bilamellar microstructure. In fact, according to literature, such a microstructure should be promising in terms of mechanical properties both under static and cyclic loads. The heat treatment development has asked for the preliminary analyses of samples annealed and aged in laboratory, implementing several cycles, differing for what concerns temperatures, times and cooling rates. Such a characterization has been carried out through optical and electron microscopy analyses, image analyses, hardness and tensile tests. As a result, the most suitable thermal cycle has been selected and performed using industrial equipment on mini bending fatigue samples with different surface conditions. The same tests have been performed on a batch of traditionally treated samples, to provide with a comparison. This master thesis activity has finally led to the definition of a heat treatment resulting into a bilamellar microstructure, promising in terms of fatigue performances with respect to the traditionally treated alloy ones. The industrial implementation of such a heat treatment will require further improvements, particularly for what concerns the post annealing water quench, in order to prevent any surface alteration potentially responsible for the fatigue performances drop. Further development of the research may also include push-pull fatigue tests, crack grow propagation and residual stresses analyses.

Assessing the impact of ammonia content in VFA-rich streams on the PHA-storing MMC acclimatization and the PHA production stage

The use of environmentally friendly products increased the interest in renewable resources as alternatives to petrochemical products. Polyhydroxyalkanoates (PHAs) are examples of such promising products, as they are biodegradable polymers with numerous potential applications. PHA production approach consists of using an open mixed microbial culture (MMC) and inexpensive feedstocks (waste or industry byproducts feedstock). The PHA process generally comprises three stages: (1) acidogenic fermentation (AF) stage (conversion of organic carbon into fermentation products); (2) culture selection stage (enrichment in PHA-storing organisms by applying Feast and Famine regime); and (3) PHA production stage (PHA accumulation up to the culture’s maximum capacity). AF of protein-rich residues results in ammonia-rich fermented streams, which can be presented as a challenge for the PHA production stage. The presence of ammonia during this stage may induce organisms to grow instead of producing PHAs. For this reason, the assessment of the effect of a high content of ammonia on PHA production it is the utmost importance. The main goal of the current project is to select a MMC enriched in PHA-accumulating organisms in conditions of high ammonia content and to evaluate the effects of ammonia presence during PHA accumulation. The culture was selected applying the Feast & Famine strategy, and fed, firstly, using a synthetic mixture of VFAs and later using a fermented stream obtained from the fermentation of protein-rich raw materials. The selected culture could accumulate up to 24% PHA per VSS with the synthetic mixture of VFAs and up to 29% for the real fermented stream. The PHA accumulation resulted in different production in the presence and absence of ammonia. Regarding to the synthetic feed, 59%wt. PHA (VSS basis) in the absence of ammonia, and 55%wt. (VSS basis) in the presence, were obtained. For the real feed, the PHA content was about 40%wt. (VSS basis) in both reactors.

Debonding and crack propagation in cracked steel beams strengthened with CFRP and subjected to cyclic loads.

The reinforcement methods used to restore or increase the bearing capacity of metal structures are based on the application of steel plates to be bolted or welded to the original structure, which can cause problems to the integrity of the original structure. These difficulties can be overcome with the introduction of fiber-reinforced composite materials. FRPs are characterized by high strength to weight ratio, and they are very resistant to corrosion. In this dissertation a cracked steel I-beam reinforced with Carbon Fiber-Reinforced Polymer will be studied by performing a numerical evaluation of the structure with the commercial Finite Element Method software ABAQUS. The crack propagation will be computed using XFEM, while the debonding of the reinforcement layer will be found by considering a cohesive contact interface between the beam and the CFRP plate. The results will show the efficiency of the strengthening method in increasing the load carrying capacity of the cracked beam, and in reducing the crack opening of the initial notch.