Inkjet-printed poly(N-isopropylacrylamide)/graphene electrodes for selective electroanalytical sensing

The main research topic of the present master thesis consisted in the modification and electrochemical testing of inkjet printed graphene electrodes with a thin polymeric hydrogel layer made of cross-linked poly(N-isopropylacrylamide) (PNIPAAM) acting as a functional layer to fabricate selective sensors. The first experimental activities dealt with the synthesis of the polymeric hydrogel and the modification of the active surface of graphene sensors through photopolymerization. Simultaneous inkjet printing and photopolymerization of the hydrogel precursor inks onto graphene demonstrated to be the most effective and reproducible technique for the modification of the electrode with PNIPAAM. The electrochemical performance of the modified electrodes was tested through cyclic voltammetry. Voltammograms with standard redox couples with either positive, neutral or negative charges, suggested an electrostatic filtering effect by the hydrogel blocking negatively charged redox species in near neutral pH electrolyte solutions from reaching the electrode surface. PNIPAAM is a known thermo-responsive polymer, but the variation of temperature did not influence the filtering properties of the hydrogels for the redox couples studied. However, a variation of the filter capacity of the material was observed at pH 2 in which the PNIPAAM hydrogel, most likely in protonated form, became impermeable to positively charged redox species and permeable to negatively charged species. Finally, the filtering capacity of the electrodes modified with PNIPAAM was evaluated for the electrochemical determination of analytes in presence of negatively charge potential interferents, such as antioxidants like ascorbic acid. The outcome of the final experiments suggested the possibility to use the inkjet-printed PNIPAAM thin layer for electroanalytical applications as an electrostatic filter against interferents of opposite charges, typically present in complex matrices, such as food and beverages.

Defects in thermosensitive colloidal crystals

Poly-N-Isopropylacrylamide (PNIPAM) colloidal particles form crystal phases that show a thermosensitive behaviour and can be used as atomic model systems. This polymer has both hydrophilic and hydrophobic character and has interesting stimuli-responsive properties in aqueous solution, of which the most important is the temperature response. Above a certain temperature, called Lower Critical Solution Temperature (LCST), the system undergoes a volume phase transition (VPT). Above the LCST, the water is expelled from the polymer network and the swollen state at low temperature transforms into a shrunken state at high temperature. The thermoresponsive behaviour of PNIPAM can be influenced by pH and ionic strength, as well as by the presence of copolymers, such as acrylic acid. In a system formed both by particles of PNIPAM and PNIPAM doped with acrylic acid, one can control the size ratio of the two components by changing the temperature of the mixture, while keeping particle interactions relatively the same. It is therefore possible to obtain thermoresponsive colloidal crystal in which temperature changes induce defects whose formation processes and dynamics can be analysed in an optical microscope at a convenient spatial and temporal scale. The goal of this thesis project was to find the conditions in which such a system could be formed, by using characterization techniques such as Static Light Scattering, Dynamic Light Scattering and Confocal Laser Scanning Microscopy. Two PNIPAM-AAc systems were available, and after characterization it was possible to select a suitable one, on the basis of its low polydispersity and the lack of a VPT, regardless of the external conditions (system JPN_7). The synthesis of a PNIPAM system was attempted, with particles of dimensions matching the JPN_7 system and, unlike JPN_7, displaying a VPT, and one suitable candidate for the mixed system was finally found (system CB_5). The best conditions to obtain thermoresponsive crystal were selected, and the formation and healing of defects were investigated with CLSM temperature scans. The obtained results show that the approach is the correct one and that the present report could represent a useful start for future developments in defect analysis and defect dynamics studies.

Crystallization and morphology of the PLLA phase within random poly (L-lactide-ran-ɛ-caprolactone)

This work has mainly focused on the poly (L-lactide) (PLLA) which is a material for multiple applications with performances comparable to those of petrochemical polymers (PP, PS, PET, etc. ...), readily recyclable and also compostable. However, PLLA has certain shortcomings that limit its applications. It is a brittle, hard polymer with a very low elongation at break, hydrophobic, exhibits low crystallization kinetics and takes a long time to degrade. The properties of PLLA may be modified by copolymerization (random, block, and graft) of L-lactide monomers with other co-monomers. In this thesis it has been studied the crystallization and morphology of random copolymers poly (L-lactide-ran-ε-caprolactone) with different compositions of the two monomers since the physical, mechanical, optical and chemical properties of a material depend on this behavior. Thermal analyses were performed by differential scanning calorimetry (DSC) and thermogravimetry (TGA) to observe behaviors due to the different compositions of the copolymers. The crystallization kinetics and morphology of poly (L-lactide-ran-ε-caprolactone) was investigated by polarized light optical microscopy (PLOM) and differential scanning calorimetry (DSC). Their thermal behavior was observed with crystallization from melt. It was observed that with increasing amounts of PCL in the copolymer, there is a decrease of the thermal degradation. Studies on the crystallization kinetics have shown that small quantities of PCL in the copolymer increase the overall crystallization kinetics and the crystal growth rate which decreases with higher quantities of PCL.

The effect of poly(lactide)-poly(carbonate) based block copolymers on the morphology and crystallization of double crystalline poly(lactide)/poly(ε-caprolactone) blends

Block copolymers of poly(lactide) and poly(carbonate) were synthetized in three different compositions and characterized by 1H-NMR and ATR analyses. The compatibilization effect of this copolymers on 80/20 (w/w%) PLA/PCL blend was evaluated. SEM micrographs show that all the blends exhibit the typical sea-island morphology characteristic of immiscible blends with PCL finely dispersed in droplets on a PLA matrix. Upon the addiction of the copolymers a reduction on PCL droplets size is observable. At the same time, a Tg depression of the PLA phase is detected when the copolymers are added in the blend. These results indicate that these copolymers are effective as compatibilizers. The copolymer that acts as the best compatibilizer is the one characterized by the same amount of PLA and PC as repeating units. As result, in the blend containing this copolymer PLA phase exhibits the highest spherulitic growth rate. An analyses on PLA phase crystallization behaviour from the glassy state within the blends was evaluated by DSC experiments. Isothermal cold crystallization of the PLA phase is enhanced up an order of magnitude upon the blending with PCL. Annealing experiments demonstrated that the crystallization of the PCL phase induces the formation of active nuclei in PLA when cooled above cooled below Tg. When the crystallization rate of PCL is retarded, a reduction on PLA nucleation is observed.