Oxodiperoxomolybdenum catalyzed olefin epoxidation: the role of Ionic Liquids

Ionic Liquids (ILs) constituted by organic cations and inorganic anions are particular salts with a melting point below 100°C. Their physical properties such as melting point and solubility can be tuned by altering the combination of their anions and cations. In the last years the interest in ILs has been centered mostly on their possible use as “green” alternatives to the traditional volatile organic solvents (VOCs) thanks to their low vapour pressure and the efficient ability in catalyst immobilization. In this regard, the subject of the present thesis is the study of the oxodiperoxomolybdenum catalyzed epoxidation of olefins in ILs media with hydrogen peroxide as the oxidant. In particular N-functionalized imidazolium salts, such as 1-(2-t-Butoxycarbonylamino-ethyl)-3-methylimidazolium (1), were synthesized with different counterions [I]-, [PF6]-, [NO3]-, [NTf2]- and [ClO4]– and tested as reaction solvents. The counterion exchange with [Cl]-, [NTf2]- and [NO3]- was also performed in unfuctionalized imidazolium salts such as 3-butyl-1-methylimidazol-3-ium (3). All the prepared ILs were tested in catalytic epoxidation of olefins exploiting oxodiperoxomolybdenum complexes [MoO(O2)2(C4H6N2)2] (4) and [MoO(O2)2(C5H8N2)2] (5) as catalysts. The IL 3[NTf2] and the catalysts 5 give rise to the best results leading to the selective formation of the epoxide of cis-cyclooctene avoiding hydrolysis side reaction. A preliminary study on the synthesis of novel NHC oxodiperoxomolybdenum complexes starting from imidazolium salts was also developed.

Oxidative properties of the Iron - Thymine-1-acetic acid - Hydrogen peroxide catalytic system

The oxidation of alcohols and olefins is a pivotal reaction in organic synthesis. However, traditional oxidants are toxic and they often release a considerable amounts of by-products. Here, two IronIII-based systems are shown as oxidative catalyst, working in mild conditions with hydrogen peroxide as primary oxidant. An efficient catalytic system for the selective oxidation of several alcohols to their corresponding aldehydes and ketones was developed and characterized, [Fe(phen)2Cl2]NO3 (phen=1,10-Phenantroline). It was demonstrated that the adoption of a buffered aqueous solution is of crucial importance to ensure both considerable activity and selectivity.The Iron - Thymine-1-acetic acid in-situ complex was studied as catalyst in alcohol oxidations and C-H oxidative functionalization, involving hydrogen peroxide as primary oxidant in mild reaction conditions. The catalytic ability in alcohol oxidations was investigated by Density Functional Theory calculations, however the catalyst still has uncertain structure. The system shows satisfactory activity in alcohol oxidation and aliphatic rings functionalization. The Fe-THA system was studied in cyclohexene oxidation and oxidative halogenations. Halide salts such as NBu4X and NH4X were introduced in the catalytic system as halogens source to obtain cyclohexene derivatives such as halohydrins, important synthetic intermediates.The purpose of this dissertation is to contribute in testing new catalytic systems for alcohol oxidations and C-H functionalization. In particular, most of the efforts in this work focus on studying the Iron - Thymine-1-acetic acid (THA) systems as non-heme oxidative model, which present: •an iron metal centre(s) as a coordinative active site, •hydrogen peroxide as a primary oxidant, •THA as an eco-friendly, biocompatible, low cost coordinating ligand.

Corrosione atmosferica in area urbana-costiera di un acciaio Cor-Ten: studio del rilascio in ambiente dei metalli di lega

Cor-Ten is a particular kind of steel, belonging to low-alloyed steel; thanks to his aesthetic features and resistance to atmospheric corrosion, this material is largely used in architectural, artistic and infrastructural applications. After environmental exposure, Cor-Ten steel exhibits the characteristic ability to self-protect from corrosion, by the development of a stable and adherent protective layer. However, some environmental factors can influence the formation and stability of the patina. In particular, exposure of Cor-Ten to polluted atmosphere (NOx, SOx, O3) or coastal areas (marine spray) may cause problems to the protective layer and, as a consequence, a release of alloying metals, which can accumulate near the structures. Some of these metals, such as Cr and Ni, could be very dangerous for soils and water because of their large toxicity. The aim of this work was to study the corrosion behavior of Cor-Ten exposed to an urban-coastal site (Rimini, Italy). Three different kinds of commercial surface finish (bare and pre-patinated, with or without a beeswax covering) were examined, both in sheltered and unsheltered exposure conditions. Wet deposition brushing the specimens surface (leaching solutions) are monthly collected and analyzed to evaluate the extent of metal release and the form in which they leave the surface, for example, as water-soluble compounds or non-adherent corrosion products. Five alloying metals (Fe, Cu, Cr, Mn and Ni) and nine ions (Cl-, NO3-, NO2-, SO42-, Na+, Ca2+, K+, Mg2+, NH4+) are determined through Atomic Absorption Spectroscopy and Ion Chromatography, respectively. Furthermore, the evolution and the behaviour of the patina are periodically followed by surface investigations (SEM-EDS and Raman Spectroscopy). After two years of exposure, the results show that Bare Cor-Ten, cheaper than the other analyzed specimens, even though undergoes the greater mass variation, his metal release is comparable to the release of the pre-patinated samples. The behavior of pre-patinated steel, with or without beeswax covering, do not show particular difference. This exposure environment doesn’t allow a completely stabilization of the patina; nevertheless an estimate of metal release after 10 years of exposure points out that the environmental impact of Cor-Ten is very low: for example, the release of chromium in the soluble fraction is less than 10 mg if we consider an exposed wall of 10 m2.

Elettrosintesi di catalizzatori Rh-Al2O3 su schiume FeCrAl per la produzione di syngas

La preparazione di catalizzatori attivi nella reazione di ossidazione parziale catalitica del metano a base di Rh, è stata condotta utilizzando tecniche di sintesi elettrochimiche su schiume metalliche a base di FeCrAlY. Sono stati depositati precursori a base di Rh/Al (Al2O3) e successivamente comparati ai catalizzatori a base idrotalcitica Rh/Mg/Al, precedentemente studiati. La precipitazione dei composti di Al ed idrotalciti sono stati ottenute tramite la tecnica di elettrogenerazione di basi. Sono state svolte prove di Linear Sweep Voltammetry (LSV) in soluzioni di KNO3 per determinare i potenziali ai quali si ottiene la riduzione dei nitrati, individuando il potenziale di sintesi a -1,2V. Tramite la tecnica potenziostatica (CronoAmperometria, CA) è stato possibile ottenere indicazioni sulle correnti in gioco durante la riduzione dei nitrati per tutto il tempo di reazione. Sono state eseguite successivamente cronoamperometrie in soluzione di Al(NO3)3 0,06M nelle condizioni -1,2V per tempi variabili, per poter determinare il grado di ricoprimento e l’adesione dei rivestimenti in ossoidrossido di alluminio su differenti supporti, partendo da geometrie semplici, come lamine metalliche in lega FeCrAlY, e passando mano a mano a geometrie più complesse, come fibre metalliche e schiume dello stesso materiale. La sintesi dei precursori catalitici è stata ottenuta su schiume di FeCrAlY in cronoamperometria utilizzando come specie in soluzione i nitrati dei metalli da depositare sottoforma di osso idrossidi. la sintesi viene effettuata successivamente su una cella in flusso più innovativa che da risultati migliori sia di ricoprimento che sulle percentuali di Rh depositato. Le schiume ottenute sono state successivamente caratterizzate, tramite analisi SEM-EDS, per poi essere calcinate a 900°C e provate, per determinarne l’attività nella reazione di ossidazione parziale catalitica del metano ad una temperatura di 750°C.

Idrochimica delle acque interstiziali e scambi acqua / sedimento nell'invaso di Ridracoli

Uno degli aspetti più influenti sulla qualità chimica e biologica dell’acqua di laghi e invasi, caratteristico del bacino di Ridracoli, è rappresentato dalla stratificazione termica, un processo di formazione di volumi d’acqua a diversa densità che può verificarsi allorquando, in alcune circostanze e, nello specifico, durante la stagione estiva, si instauri una condizione stabile in cui l’acqua riscaldata dalla radiazione solare sovrasta quella più fredda e densa del fondo. Una delle conseguenze di tali variazioni termiche è che esse inducono cambiamenti nei livelli di ossigeno disciolto, favorendo l’instaurarsi di processi di degradazione anaerobica della materia organica e determinando la formazione di un chimismo ostile per l’attività biologica. I cicli stagionali, redox-dipendenti, di Ferro e Manganese tra la colonna d’acqua e i sedimenti sono caratteristici di questi ambienti ed una loro risospensione in forma disciolta è stato rilevato nell’ipolimnio dell’invaso di Ridracoli, stagionalmente anossico. Questo studio, collocato all’interno di un ampio progetto finanziato da Romagna Acque Società delle Fonti S.p.A. con la Facoltà di Scienze Ambientali – Campus di Ravenna ed il CNR-ISMAR, si è posto come obiettivo l’individuazione dei fattori che controllano la distribuzione e la mobilità degli elementi chimici all’interno del sistema acqua-sedimento dell’invaso di Ridracoli ed è articolato in tre diverse fasi: • Indagine della composizione chimica del sedimento; • Analisi ed interpretazione della composizione chimica delle acque interstiziali • Stima del flussi attraverso l’interfaccia acqua-sedimento mediante l’utilizzo di una camera bentica e l’applicazione della prima legge di Fick sulla diffusione. Al termine del lavoro è stato possibile ricostruire un quadro diagenetico generale contraddistinto da una deplezione degli accettori di elettroni principali (O2 e NO3-) entro i primi millimetri di sedimento, da un consumo immediato di SO42- e da una graduale riduzione degli ossidi di Mn (IV) e Fe (III), con formazione di gradienti negativi ed il rilascio di sostanze disciolte nella colonna d’acqua.