Study of Co-based hydrotalcite-derived mixed metal oxides partially modified with silver as potential catalysts for N2O decomposition

Co-Al-Ox mixed metal oxides partially modified with Cu or Mg, as well as Ag were successfully prepared, characterized and evaluated as potential catalysts for the N2O decomposition. The materials were characterized by the following techniques: X-Ray Diffraction, Thermogravimetric Analysis (TGA), N2 Physisorption, Hydrogen Temperature-Programmed Reduction (H2-TPR), and X-ray photoelectron spectroscopy (XPS). Ag-modified HT-derived mixed oxides showed enhanced activity compared to the undoped materials, the optimum composition was found for (1 wt.% Ag)CHT-Co3Al. The catalyst characterization studies suggested that the improved catalytic activity of Ag-promoted catalysts were mainly because of the altered redox properties of the materials.

Produzione di idrogeno mediante reforming ciclico dell'etanolo

This work deals with a study on the feasibility of a new process, aimed at the production of hydrogen from water and ethanol (a compound obtained starting from biomasses), with inherent separation of hydrogen from C-containing products. The strategy of the process includes a first step, during which a metal oxide is contacted with ethanol at high temperature; during this step, the metal oxide is reduced and the corresponding metallic form develops. During the second step, the reduced metal compound is contacted at high temperature with water, to produce molecular hydrogen and with formation of the original metal oxide. In overall, the combination of the two steps within the cycle process corresponds to ethanol reforming, where however COx and H2 are produced separately. Various mixed metal oxides were used as electrons and ionic oxygen carriers, all of them being characterized by the spinel (inverse) structure typical of Me ferrites: MeFe2O4 (Me=Co, Ni, Fe or Cu). The first step was investigated in depth; it was found that besides the generation of the expected CO, CO2 and H2O, the products of ethanol anaerobic oxidation, also a large amount of H2 and coke were produced. The latter is highly undesired, since it affects the second step, during which water is fed over the pre-reduced spinel at high temperature. The behavior of the different spinels was affected by the nature of the divalent metal cation; magnetite was the oxide showing the slower rate of reduction by ethanol, but on the other hand it was that one which could perform the entire cycle of the process more efficiently. Still the problem of coke formation remains the greater challenge to solve.

Ex situ X-­Ray absorption study of Li-­rich layered cathode material Li[Li0.2Mn0.56Ni0.16Co0.08]O2

The Li-rich layered transition metal oxides (LLOs) Li2MnO3-LiMO2 (M=Mn, Co, Ni, etc.) have drawn considerable attention as cathode materials for rechargeable lithium batteries. They generate large reversible capacities but the fundamental reaction mechanism and structural perturbations during cycling remain controversial. In the present thesis, ex situ X-ray absorption spectroscopy (XAS) measurements were performed on Li[Li0.2Mn0.56Ni0.16Co0.08]O2 at different stage of charge during electrochemical oxidation/reduction. K-edge spectra of Co, Mn and Ni were recorded through a voltage range of 3.7-4.8V vs. Li/Li+, which consist of X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS). Oxidation states during initial charge were discussed based on values from literature as well as XANES analysis. Information about bond distance, coordination number as well as corresponding Debye-Waller factor were extracted from Gnxas analysis of raw data in the EXAFS region. The possibility of oxygen participation in the initial charge was discussed. Co and Ni prove to take part in the oxidation/reduction process while Mn remain in the tetravalent state. The cathode material appears to retain good structural short-range order during charge-discharge. A resemblance of the pristine sample and sample 4 was discovered which was firstly reported for similar compounds.

Reforming dell'etanolo con processo ciclico: studio della reattività di ossidi misti con struttura spinello

This work deals with a study on the feasibility of a new process, aimed at the production of hydrogen from water and ethanol (a compound obtained starting from biomasses), with inherent separation of hydrogen from C-containing products. The strategy of the process includes a first step, during which a metal oxide is contacted with ethanol at high temperature; during this step, the metal oxide is reduced and the corresponding metallic form develops. During the second step, the reduced metal compound is contacted at high temperature with water, to produce molecular hydrogen and with formation of the original metal oxide. In overall, the combination of the two steps within the cycle process corresponds to ethanol reforming, where however COx and H2 are produced separately. Various mixed metal oxides were used as electrons and ionic oxygen carriers, all of them being characterized by the spinel structure typical of M-modified non-stoichiometric ferrites: M0,6Fe2,4O4 (M = Co, Mn or Co/Mn). The first step was investigated in depth; it was found that besides the generation of the expected CO, CO2 and H2O, the products of ethanol anaerobic oxidation, also a large amount of H2 and coke were produced. The latter is highly undesired, since it affects the second step, during which water is fed over the pre-reduced spinel at high temperature. The behavior of the different spinels was affected by the nature of the divalent metal cation. The new materials were tested in terms of both redox proprieties and catalytic activity to generate hydrogen. Still the problem of coke formation remains the greater challenge to solve.

Anaerobic oxidation of ethanol over spinel mixed oxides: the first step in the steam-iron process for H2 production

The future hydrogen demand is expected to increase, both in existing industries (including upgrading of fossil fuels or ammonia production) and in new technologies, like fuel cells. Nowadays, hydrogen is obtained predominantly by steam reforming of methane, but it is well known that hydrocarbon based routes result in environmental problems and besides the market is dependent on the availability of this finite resource which is suffering of rapid depletion. Therefore, alternative processes using renewable sources like wind, solar energy and biomass, are now being considered for the production of hydrogen. One of those alternative methods is the so-called “steam-iron process” which consists in the reduction of a metal-oxide by hydrogen-containing feedstock, like ethanol for instance, and then the reduced material is reoxidized with water to produce “clean” hydrogen (water splitting). This kind of thermochemical cycles have been studied before but currently some important facts like the development of more active catalysts, the flexibility of the feedstock (including renewable bio-alcohols) and the fact that the purification of hydrogen could be avoided, have significantly increased the interest for this research topic. With the aim of increasing the understanding of the reactions that govern the steam-iron route to produce hydrogen, it is necessary to go into the molecular level. Spectroscopic methods are an important tool to extract information that could help in the development of more efficient materials and processes. In this research, ethanol was chosen as a reducing fuel and the main goal was to study its interaction with different catalysts having similar structure (spinels), to make a correlation with the composition and the mechanism of the anaerobic oxidation of the ethanol which is the first step of the steam-iron cycle. To accomplish this, diffuse reflectance spectroscopy (DRIFTS) was used to study the surface composition of the catalysts during the adsorption of ethanol and its transformation during the temperature program. Furthermore, mass spectrometry was used to monitor the desorbed products. The set of studied materials include Cu, Co and Ni ferrites which were also characterized by means of X-ray diffraction, surface area measurements, Raman spectroscopy, and temperature programmed reduction.