Hydrogeochemical characterization of Seehausen territory - Bremen

The aim of this thesis is to provide a geochemical characterization of the Seehausen territory (a neighborhood) of Bremen, Germany. In this territory it is hosted a landfill of dredged sediments coming both from Bremerhaven (North See) and Bremen harbor (directly on the river Weser). For this reason this work has been focused also on possible impacts of the landfill on the groundwaters (shallow and deep aquifer). The Seehausen landfill uses the dewatering technique to manage the dredged sediments: incoming sediments are put into dewatering fields until they are completely dried (it takes almost a year). Then they are randomly sampled and analyzed: if the pollutants content is acceptable, sediments are treated with other materials and used instead of raw material for embankment, bricks, etc., otherwise they are disposed in the landfill. During this work it has been made a study of the natural geology and hydrogeology of the whole area of interest, especially because it is characterized by ancient natural salt deposits. Then, together with the Geological Survey of Bremen and the Harbor Authority of Bremen there have been identified all useful piezometers for a monitoring net around the landfill. During the sampling campaign there have been collected data of the principal anions and cations, physical parameters and stable water isotopes. Data analysis has been focused particularly on Cl, Na, SO4 and EC because these parameters might be helpful to attribute geochemical trends to the landfill or to a natural background. Furthermore dataloggers have been installed for a month in some piezometers and EC, pressure, dissolved oxygen and temperature data have been collected. Finally there has been made a deep comparison between current and historical data (1996 – 2011) and between old interpolation maps and current ones in order to see time trends of the aquifer geochemistry.

Synthesis, characterization and formulation of a cathode active material: Copper nitroprusside

Nowadays, rechargeable Li-ion batteries play an important role in portable consumer devices. Formulation of such batteries is improvable by researching new cathodic materials that present higher performances of cyclability and negligible efficiency loss over cycles. Goal of this work was to investigate a new cathodic material, copper nitroprusside, which presents a porous 3D framework. Synthesis was carried out by a low-cost and scalable co-precipitation method. Subsequently, the product was characterized by means of different techniques, such as TGA, XRF, CHN elemental analysis, XRD, Mössbauer spectroscopy and cyclic voltammetry. Electrochemical tests were finally performed both in coin cells and by using in situ cells: on one hand, coin cells allowed different formulations to be easily tested, on the other operando cycling led a deeper insight to insertion process and both chemical and physical changes. Results of several tests highlighted a non-reversible electrochemical behavior of the material and a rapid capacity fading over time. Moreover, operando techniques report that amorphisation occurs during the discharge.

Novel materials for direct X-ray detectors based on semiconducting organic polymers

Conventional inorganic materials for x-ray radiation sensors suffer from several drawbacks, including their inability to cover large curved areas, me- chanical sti ffness, lack of tissue-equivalence and toxicity. Semiconducting organic polymers represent an alternative and have been employed as di- rect photoconversion material in organic diodes. In contrast to inorganic detector materials, polymers allow low-cost and large area fabrication by sol- vent based methods. In addition their processing is compliant with fexible low-temperature substrates. Flexible and large-area detectors are needed for dosimetry in medical radiotherapy and security applications. The objective of my thesis is to achieve optimized organic polymer diodes for fexible, di- rect x-ray detectors. To this end polymer diodes based on two different semi- conducting polymers, polyvinylcarbazole (PVK) and poly(9,9-dioctyluorene) (PFO) have been fabricated. The diodes show state-of-the-art rectifying be- haviour and hole transport mobilities comparable to reference materials. In order to improve the X-ray stopping power, high-Z nanoparticle Bi2O3 or WO3 where added to realize a polymer-nanoparticle composite with opti- mized properities. X-ray detector characterization resulted in sensitivties of up to 14 uC/Gy/cm2 for PVK when diodes were operated in reverse. Addition of nanoparticles could further improve the performance and a maximum sensitivy of 19 uC/Gy/cm2 was obtained for the PFO diodes. Compared to the pure PFO diode this corresponds to a five-fold increase and thus highlights the potentiality of nanoparticles for polymer detector design. In- terestingly the pure polymer diodes showed an order of magnitude increase in sensitivity when operated in forward regime. The increase was attributed to a different detection mechanism based on the modulation of the diodes conductivity.

Experimental characterization of carbon-fiber-reinforced polymer laminates

The goal of this thesis is to make static tensile test on four Carbon Fiber Reinforced Polymer laminates, in such a way as to obtain the ultimate tensile strength of these laminates; in particular, the laminates analyzed were produced by Hand Lay-up technology. Testing these laminates we have a reference point on which to compare other laminates and in particular CFRP laminate produced by RTM technology.

Bionanocomposites based on Plla, Pcl and montmorillonite: synthesis, characterization and crystallization

Poly(lactide) is one of the best candidate to replace conventional petroleum-based polymers, since it is biobased, biocompatible and biodegradable. However, commercial PLA materials typically have low crystallization rate resulting in long processing time and low production efficiency. In this work the effects of two nanofillers MMT30B and MMT30B-g-P(LA-co-CL) on the crystallization rate of neat PLA and PLA/PCL blend were investigated. MMT30B-g-P(LA-co-CL) was synthetized by in situ grafting reaction. The synthesis was carried in xylene at 140°C, upon the results of a screening. The grafted copolymers were evaluated by 1H-NMR ,ATR–IR and TGA. Solvent casted films were obtained by mixing MMT30B-g-P(LA-co-CL) at 5% (w/w) with neat PLA and PLA/PCL blend, comparing the properties with the corresponding blends with and without a 5% of (w/w) unmodified clay. SEM images on PLA based blends shows that MMT30B is aggregated into larger particles compared to MMT30B-g-P(LLA-co-CL). This behavior is correlated to the better exfoliation of MMT30B-g-P(LA-co-CL) clay layers. SEM images on PLA/PCL based blends exhibit the typical sea-island morphology, characteristic of immiscible blends. PLA is the matrix while PCL is finely dispersed in droplets. MMT30B does not reduce PCL droplets size, while MMT30B-g-P(LA-co-CL) reduces the size of PCL droplets. This means that MMT30B-g-P(LA-co-CL) can migrate to the PLA-PCL interface, acting as a compatibilizer. Non-isothermal DSC cooling scans show a fractionated crystallization of the PCL phase in PLA/PCL/MMT30B-g-P(LA-co-CL), confirming the compatibilizer effect of MMT30B-g-P(LA-co-CL). At the same timeMMT30B-g-P(LA-co-CL) can better nucleate the PLA phase, both in neat PLA and PLA/PCL blend, promoting the crystallization during the heating scans. In isothermal condition, both the nanofillers increase the crystallization rate of PLA phase in neat PLA, while in PLA/PCL blends the effect is covered by the nucleating effect of PCL.