Measurement of LSP-induced residual stresses and fatigue life on thin-walled aluminium alloys specimens

This thesis work encloses activities carried out in the Laser Center of the Polytechnic University of Madrid and the laboratories of the University of Bologna in Forlì. This thesis focuses on the superficial mechanical treatment for metallic materials called Laser Shock Peening (LSP). This process is a surface enhancement treatment which induces a significant layer of beneficial compressive residual stresses underneath the surface of metal components in order to improve the detrimental effects of the crack growth behavior rate in it. The innovation aspect of this work is the LSP application to specimens with extremely low thickness. In particular, after a bibliographic study and comparison with the main treatments used for the same purposes, this work analyzes the physics of the operation of a laser, its interaction with the surface of the material and the generation of the surface residual stresses which are fundamentals to obtain the LSP benefits. In particular this thesis work regards the application of this treatment to some Al2024-T351 specimens with low thickness. Among the improvements that can be obtained performing this operation, the most important in the aeronautic field is the fatigue life improvement of the treated components. As demonstrated in this work, a well-done LSP treatment can slow down the progress of the defects in the material that could lead to sudden failure of the structure. A part of this thesis is the simulation of this phenomenon using the program AFGROW, with which have been analyzed different geometric configurations of the treatment, verifying which was better for large panels of typical aeronautical interest. The core of the LSP process are the residual stresses that are induced on the material by the interaction with the laser light, these can be simulated with the finite elements but it is essential to verify and measure them experimentally. In the thesis are introduced the main methods for the detection of those stresses, they can be mechanical or by diffraction. In particular, will be described the principles and the detailed realization method of the Hole Drilling measure and an introduction of the X-ray Diffraction; then will be presented the results I obtained with both techniques. In addition to these two measurement techniques will also be introduced Neutron Diffraction method. The last part refers to the experimental tests of the fatigue life of the specimens, with a detailed description of the apparatus and the procedure used from the initial specimen preparation to the fatigue test with the press. Then the obtained results are exposed and discussed.

Numerical evaluation of material model and thickness effect on LSP induced residual stresses

Laser Shock Peening (LSP) is a technological process used to improve mechanical properties in metallic components. When a short and intense laser pulse irradiates a metallic surface, high pressure plasma is generated on the treated surface; elasto-plastic waves, then, propagate inside the target and create plastic strain. This surface treatment induces a deep compressive residual stresses field on the treated area and through the thickness; such compressive residual stress is expected to increase the fatigue resistance, and reduce the detrimental effects of corrosion and stress corrosion cracking.

Fatigue Design Challenges of Transition Pieces from Decommissioned Platforms for Offshore Wind Energy

All structures are subjected to various loading conditions and combinations. For offshore structures, these loads include permanent loads, hydrostatic pressure, wave, current, and wind loads. Typically, sea environments in different geographical regions are characterized by the 100-year wave height, surface currents, and velocity speeds. The main problems associated with the commonly used, deterministic method is the fact that not all waves have the same period, and that the actual stochastic nature of the marine environment is not taken into account. Offshore steel structure fatigue design is done using the DNVGL-RP-0005:2016 standard which takes precedence over the DNV-RP-C203 standard (2012). Fatigue analysis is necessary for oil and gas producing offshore steel structures which were first constructed in the Gulf of Mexico North Sea (the 1930s) and later in the North Sea (1960s). Fatigue strength is commonly described by S-N curves which have been obtained by laboratory experiments. The rapid development of the Offshore wind industry has caused the exploration into deeper ocean areas and the adoption of new support structural concepts such as full lattice tower systems amongst others. The optimal design of offshore wind support structures including foundation, turbine towers, and transition piece components putting into consideration, economy, safety, and even the environment is a critical challenge. In this study, fatigue design challenges of transition pieces from decommissioned platforms for offshore wind energy are proposed to be discussed. The fatigue resistance of the material and structural components under uniaxial and multiaxial loading is introduced with the new fatigue design rules whilst considering the combination of global and local modeling using finite element analysis software programs.