This thesis is the result of the study of two reactions leading to the formation of important heterocyclic compounds of potential pharmaceutical interest. The first study concerns the reaction of (1,3)-dipolar cycloaddition between nitrones and activated olefins by hydrogen bond catalysis of thioureas derivatives leading to the formation of a five-membered cyclic adducts, an interesting and strategic synthetic intermediate, for the synthesis of benzoazepine. The second project wants to explore the direct oxidative C(sp3)-H α-alkylation of simple amides with subsequent addition of an olefin and cyclization in order to obtain the corresponding oxazine. Both reactions are still under development.

Bionanocomposites based on Plla, Pcl and montmorillonite: synthesis, characterization and crystallization

Poly(lactide) is one of the best candidate to replace conventional petroleum-based polymers, since it is biobased, biocompatible and biodegradable. However, commercial PLA materials typically have low crystallization rate resulting in long processing time and low production efficiency. In this work the effects of two nanofillers MMT30B and MMT30B-g-P(LA-co-CL) on the crystallization rate of neat PLA and PLA/PCL blend were investigated. MMT30B-g-P(LA-co-CL) was synthetized by in situ grafting reaction. The synthesis was carried in xylene at 140°C, upon the results of a screening. The grafted copolymers were evaluated by 1H-NMR ,ATR–IR and TGA. Solvent casted films were obtained by mixing MMT30B-g-P(LA-co-CL) at 5% (w/w) with neat PLA and PLA/PCL blend, comparing the properties with the corresponding blends with and without a 5% of (w/w) unmodified clay. SEM images on PLA based blends shows that MMT30B is aggregated into larger particles compared to MMT30B-g-P(LLA-co-CL). This behavior is correlated to the better exfoliation of MMT30B-g-P(LA-co-CL) clay layers. SEM images on PLA/PCL based blends exhibit the typical sea-island morphology, characteristic of immiscible blends. PLA is the matrix while PCL is finely dispersed in droplets. MMT30B does not reduce PCL droplets size, while MMT30B-g-P(LA-co-CL) reduces the size of PCL droplets. This means that MMT30B-g-P(LA-co-CL) can migrate to the PLA-PCL interface, acting as a compatibilizer. Non-isothermal DSC cooling scans show a fractionated crystallization of the PCL phase in PLA/PCL/MMT30B-g-P(LA-co-CL), confirming the compatibilizer effect of MMT30B-g-P(LA-co-CL). At the same timeMMT30B-g-P(LA-co-CL) can better nucleate the PLA phase, both in neat PLA and PLA/PCL blend, promoting the crystallization during the heating scans. In isothermal condition, both the nanofillers increase the crystallization rate of PLA phase in neat PLA, while in PLA/PCL blends the effect is covered by the nucleating effect of PCL.

Towards NIR emission: 2-(1H-tetrazol-1-yl)pyridine as versatile ligand for the synthesis of two new families of cationic and neutral Ir(III) complexes.

In the last decades, cyclometalated Ir(III) complexes have drawn a large interest for their unique properties: they are excellent triplet state emitters, thus the emission is phosphorescent in nature; typically high quantum yields and good stability make them good candidates for luminescent materials. Moreover, through an opportune choice of the ligands, it is possible to tune the emission along the whole visible spectra. Thanks to these interesting features, Ir(III) complexes have found different applications in several areas of applied science, from OLEDs to bioimaging. In particular, regarding the second application, a remarkable red-shift in the emission is required, in order to minimize the problem of the tissue penetration and the possible damages for the organisms. With the aim of synthesizing a new family of NIR emitting Ir(III) complexes, we envisaged the possibility to use for the first time 2-(1H-tetrazol-1-yl)pyridine as bidentate ligand able to provide the required red-shift of the emission of the final complexes. Exploiting the versatility of the ligand, I prepared two different families of heteroleptic Ir(III) complexes. In detail, in the first case the 2-(1H-tetrazol-1-yl)pyridine was used as bis-chelating N^N ligand, leading to cationic complexes, while in the second case it was used as cyclometalating C^N ligand, giving neutral complexes. The structures of the prepared molecules have been characterised by NMR spectroscopy and mass spectrometry. Moreover, the neutral complexes’ emissive properties have been measured: emission spectra have been recorded in solution at both room temperature and 77K, as well as in PMMA matrix. DFT calculation has then been performed and the obtained results have been compared to experimental ones.

Synthesis of Metal-Binding Ligand-Containing Copolymers, Nanoparticles and Blends

In this thesis we developed three copper-containing systems. Copper shows intriguing abilities in photocatalysis, however, one of the major limitations of many copper complexes is that photochemical properties might be quenched in solution caused by π-interactions between solvent and solute, due to Jahn-Teller distortion in the excited state. As such, we herein seek to synthesise copper heteroleptic complexes that will subsequently be nanoprecipitated with a polymer. This will allow the polymer to encase the complex and prevent the solvent-induced quenching. Subsequently, the preparation of blends of polymer with the aforementioned copper complexes, at different weight ratios is sought. The preparation of the blend is particularly interesting as the catalytic properties are anticipated to be inferior on account of the low surface area. However, owing to the polymer matrix better, mechanical properties are anticipated. The blends can combine the mechanical properties of the polymer and the luminescence of the complex, with the advantage that the polymer matrix can also prevent quenching from oxygen. As final task, we developed a copper-containing monomer. The synthesis of a monomer that contains copper and can be excited under ultraviolet (UV) light is particularly interesting.

Synthesis of Na-PSS geopolymers and analysis of the H2O/Na2O molar ratio influence over their mechanical properties

Geopolymers are solid aluminosilicate material made by mixing an activating solution and a solid precursor. This work studied the mechanisms of synthesis of metakaolin-based geopolymers and the influence of water content, described by the molar ratio H2O/Na2O, on the final product. The samples were tested using a Uniaxial Compressive Test (UCT) to define their compressive resistance. Two geopolymers series were synthetized and let them rest for 7- days and 28-days, each of them composed by six different sets. 7-day rest series showed that water addition had no relevant effect over its resistance while the 28-day rest series almost doubled the compressive resistance, although those with the highest H2O/Na2O molar ratio showed instead a drastic reduction. Two other series were synthesized by adding silt aggregate, a waste material obtained in the production of aggregate for concrete, corresponding to 10wt% and 20wt%of the metakaolin used. After 28 days of aging, these samples were tested via UCT to measure the variation of the compressive resistance after the silt addition. The aggregate has disruptive effects over the compressive resistance, but the 20wt% samples achieved a higher compressive resistance. Samples with highest and lowest compressive resistance have been chosen to carry out an XRD analysis. In all the samples it has been recognized the presence of Anatase (TiO2), a titanium oxide found in the metakaolin and Thermonatrite, a hydrated sodium carbonate [Na2CO3 • (H2O)]. Scanning Electron Microscopy was carried out on the samples with the highest compressive resistance and showed that the samples with lower water content developed a homogeneous geopolymeric texture, while those with higher water content showed instead a spongy-like texture and a higher air or pore solution bubbles presence. Silt/geopolymer composites showed a fracture system developing across the interstitial transition zone between the geopolymer matrix and the aggregate particle.

Kinetic modeling for the synthesis of ethyl levulinate

This work is focused on studying the kinetics of esterification of levulinic acid in an isothermal batch reactor using ethanol as a reactant and as a protic polar solvent at the same time and in the presence of an acid catalyst (sulfuric acid). The choice of solvent is important as it affects the kinetics and thermodynamics of the reaction system moreover, the knowledge of the reaction kinetics plays an important role in the design of the process. This work is divided into two stages; The first stage is the experimental part in which the experimental matrix was developed by changing the process variables one at a time (temperature, molar ratio between reactants, and catalyst concentration) in order to study their influence on the kinetics; the second stage is using the obtained data from the experiments to build the modeling part in order to estimate the thermodynamics parameters.