Teos-based consolidants for stone conservation: evaluation of the effects and testing by x-ray imaging

Natural stones have been widely used in the construction field since antiquity. Building materials undergo decay processes due to mechanical,chemical, physical and biological causes that can act together. Therefore an interdisciplinary approach is required in order to understand the interaction between the stone and the surrounding environment. Utilization of buildings, inadequate restoration activities and in general anthropogenic weathering factors may contribute to this degradation process. For this reasons, in the last few decades new technologies and techniques have been developed and introduced in the restoration field. Consolidants are largely used in restoration and conservation of cultural heritage in order to improve the internal cohesion and to reduce the weathering rate of building materials. It is important to define the penetration depth of a consolidant for determining its efficacy. Impregnation mainly depends on the microstructure of the stone (i.e. porosity) and on the properties of the product itself. Throughout this study, tetraethoxysilane (TEOS) applied on globigerina limestone samples has been chosen as object of investigation. After hydrolysis and condensation, TEOS deposits silica gel inside the pores, improving the cohesion of the grains. X-ray computed tomography has been used to characterize the internal structure of the limestone samples,treated and untreated with a TEOS-based consolidant. The aim of this work is to investigate the penetration depth and the distribution of the TEOS inside the porosity, using both traditional approaches and advanced X-ray tomographic techniques, the latter allowing the internal visualization in three dimensions of the materials. Fluid transport properties and porosity have been studied both at macroscopic scale, by means of capillary uptake tests and radiography, and at microscopic scale,investigated with X-ray Tomographic Microscopy (XTM). This allows identifying changes in the porosity, by comparison of the images before and after the treatment, and locating the consolidant inside the stone. Tests were initially run at University of Bologna, where characterization of the stone was carried out. Then the research continued in Switzerland: X-ray tomography and radiography were performed at Empa, Swiss Federal Laboratories for Materials Science and Technology, while XTM measurements with synchrotron radiation were run at Paul Scherrer Institute in Villigen.

Frost heave testing of norwegian materials for road infrastructure

In areas of seasonal frost, frost susceptibility composed by frost heaving during the winter and thaw softening during the spring is one of the most dangerous phenomenon for transportation, road and railway infrastructure. Therefore, the need for frost protection layer becomes imperative. The purpose of frost protection layer is to prevent frost from penetrating down through the pavement and into the sub-soils. Frost susceptible soils under the road can be cause damages on the roads or other structures due to frost heave or reduced capacity characteristics thaw period. "Frost heave" is the term given to the upwards displacement of the ground surface caused by the formation of ice within soils or aggregates (Rempel et al., 2004). Nowadays in Scandinavia the most common material used in frost protection layer in the pavement structure of roads and in the ballast of the railway tracks are coarse-grain crushed rocks aggregates. Based on the capillary rise, the mechanics of frost heave phenomenon is based on the interaction between aggregates and water, as suggested by Konrad and Lemieux in 2005 that said that the fraction of material below the 0.063 mm sieve for coarse-grained soils must be controlled so as to reduce the sensitivity to frost heave. The study conducted in this thesis project is divided in two parts: - the analysis of the coarse grained aggregates used in frost protection layer in Norway; - the analysis of the frost heave phenomenon in the laboratory under known boundary conditions, through the use of the most widely used method, the frost heave test, in” closed system” (without access of water).