Analysis of retrieved shoulder prostheses

In the last years the number of shoulder arthroplasties has been increasing. Simultaneously the study of their shape, size and strength and the reasons that bring to a possible early explantation have not yet been examined in detail. The research carried out directly on explants is practically nonexistent, this means a poor understanding of the mechanisms leading the patient and so the surgeon, to their removal. The analysis of the mechanisms which are the cause of instability, dislocation, broken, fracture, etc, may lead to a change in the structure or design of the shoulder prostheses and lengthen the life of the implant in situ. The idea was to analyze 22 explants through three methods in order to find roughness, corrosion and surface wear. In the first method, the humeral heads and/or the glenospheres were examined with the interferometer, a machine that through electromagnetic waves gives information about the roughness of the surfaces under examination. The output of the device was a total profile containing both roughness and information on the waves (representing the spatial waves most characteristic on the surface). The most important value is called "roughness average" and brings the average value of the peaks found in the local defects of the surfaces. It was found that 42% of the prostheses had considerable peak values in the area where the damage was caused by the implant and not only by external events, such as possibly the surgeon's hand. One of the problems of interest in the use of metallic biomaterials is their resistance to corrosion. The clinical significance of the degradation of metal implants has been the purpose of the second method; the interaction between human body and metal components is critical to understand how and why they arrive to corrosion. The percentage of damage in the joints of the prosthetic components has been calculated via high resolution photos and the software ImageJ. The 40% and 50% of the area appeared to have scratches or multiple lines due to mechanical artifacts. The third method of analysis has been made through the use of electron microscopy to quantify the wear surface in polyethylene components. Different joint movements correspond to different mechanisms of damage, which were imprinted in the parts of polyethylene examined. The most affected area was located mainly in the side edges. The results could help the manufacturers to modify the design of the prostheses and thus reduce the number of explants. It could also help surgeons in choosing the model of the prosthesis to be implanted in the patient.

Geometrical optimization of a short-stem hip implant for the reduction of proximal stress shielding (ottimizzazione geometrica di uno stelo corto di protesi d?anca per la riduzione della schermatura del carico prossimale)

Nowadays the number of hip joints arthroplasty operations continues to increase because the elderly population is growing. Moreover, the global life expectancy is increasing and people adopt a more active way of life. For this reasons, the demand of implant revision operations is becoming more frequent. The operation procedure includes the surgical removal of the old implant and its substitution with a new one. Every time a new implant is inserted, it generates an alteration in the internal femur strain distribution, jeopardizing the remodeling process with the possibility of bone tissue loss. This is of major concern, particularly in the proximal Gruen zones, which are considered critical for implant stability and longevity. Today, different implant designs exist in the market; however there is not a clear understanding of which are the best implant design parameters to achieve mechanical optimal conditions. The aim of the study is to investigate the stress shielding effect generated by different implant design parameters on proximal femur, evaluating which ranges of those parameters lead to the most physiological conditions.