New catalysts for the water gas shift reaction at middle-temperature

H2 demand is continuously increasing since its many relevant applications, for example, in the ammonia production, refinery processes or fuel cells. The Water Gas Shift (WGS) reaction (CO + H2O = CO2 + H2 DeltaH = -41.1 kJ.mol-1) is a step in the H2 production, reducing significantly the CO content and increasing the H2 one in the gas mixtures obtained from steam reforming. Industrially, the reaction is carried out in two stages with different temperature: the first stage operates at high temperature (350-450 °C) using Fe-based catalysts, while the second one is performed at lower temperature (190-250 °C) over Cu-based catalysts. However, recently, an increasing interest emerges to develop new catalytic formulations, operating in a single-stage at middle temperature (MTS), while maintaining optimum characteristics of activity and stability. These formulations may be obtained by improving activity and selectivity of Fe-based catalysts or increasing thermal stability of Cu-based catalysts. In the present work, Cu-based catalysts (Cu/ZnO/Al2O3) prepared starting from hydrotalcite-type precursors show good homogeneity and very interesting physical properties, which worsen by increasing the Cu content. Among the catalysts with different Cu contents, the catalyst with 20 wt.% of Cu represents the best compromise to obtain high catalytic activity and stability. On these bases, the catalytic performances seem to depend on both metallic Cu surface area and synergetic interactions between Cu and ZnO. The increase of the Al content enhances the homogeneity of the precursors, leading to a higher Cu dispersion and consequent better catalytic performances. The catalyst with 20 wt.% of Cu and a molar ratio M(II)/M(III) of 2 shows a high activity also at 250 °C and a good stability at middle temperature. Thus, it may be considered an optimum catalyst for the WGS reaction at middle temperature (about 300 °C). Finally, by replacing 50 % (as at. ratio) of Zn by Mg (which is not active in the WGS reaction), better physical properties were observed, although associate with poor catalytic performances. This result confirms the important role of ZnO on the catalytic performances, favoring synergetic interactions with metallic Cu.

Defects in thermosensitive colloidal crystals

Poly-N-Isopropylacrylamide (PNIPAM) colloidal particles form crystal phases that show a thermosensitive behaviour and can be used as atomic model systems. This polymer has both hydrophilic and hydrophobic character and has interesting stimuli-responsive properties in aqueous solution, of which the most important is the temperature response. Above a certain temperature, called Lower Critical Solution Temperature (LCST), the system undergoes a volume phase transition (VPT). Above the LCST, the water is expelled from the polymer network and the swollen state at low temperature transforms into a shrunken state at high temperature. The thermoresponsive behaviour of PNIPAM can be influenced by pH and ionic strength, as well as by the presence of copolymers, such as acrylic acid. In a system formed both by particles of PNIPAM and PNIPAM doped with acrylic acid, one can control the size ratio of the two components by changing the temperature of the mixture, while keeping particle interactions relatively the same. It is therefore possible to obtain thermoresponsive colloidal crystal in which temperature changes induce defects whose formation processes and dynamics can be analysed in an optical microscope at a convenient spatial and temporal scale. The goal of this thesis project was to find the conditions in which such a system could be formed, by using characterization techniques such as Static Light Scattering, Dynamic Light Scattering and Confocal Laser Scanning Microscopy. Two PNIPAM-AAc systems were available, and after characterization it was possible to select a suitable one, on the basis of its low polydispersity and the lack of a VPT, regardless of the external conditions (system JPN_7). The synthesis of a PNIPAM system was attempted, with particles of dimensions matching the JPN_7 system and, unlike JPN_7, displaying a VPT, and one suitable candidate for the mixed system was finally found (system CB_5). The best conditions to obtain thermoresponsive crystal were selected, and the formation and healing of defects were investigated with CLSM temperature scans. The obtained results show that the approach is the correct one and that the present report could represent a useful start for future developments in defect analysis and defect dynamics studies.