Study of the mechanisms of shear transfer in fiber-reinforced concrete elements

matlab functions for the validation of push-off tests results

Data analysis of collapse mechanisms of a 3D printed groin vault in shaking table testing

The aim of this novel experimental study is to investigate the behaviour of a 2m x 2m model of a masonry groin vault, which is built by the assembly of blocks made of a 3D-printed plastic skin filled with mortar. The choice of the groin vault is due to the large presence of this vulnerable roofing system in the historical heritage. Experimental tests on the shaking table are carried out to explore the vault response on two support boundary conditions, involving four lateral confinement modes. The data processing of markers displacement has allowed to examine the collapse mechanisms of the vault, based on the arches deformed shapes. There then follows a numerical evaluation, to provide the orders of magnitude of the displacements associated to the previous mechanisms. Given that these displacements are related to the arches shortening and elongation, the last objective is the definition of a critical elongation between two diagonal bricks and consequently of a diagonal portion. This study aims to continue the previous work and to take another step forward in the research of ground motion effects on masonry structures.

Amplification mechanisms of inflationary spectra in induced gravity

Inflation is the primordial stage of accelerated expansion of the Universe which solves the issues of the initial conditions of a decelerating Universe (horizon, flatness and entropy problems). Moreover, it is supposed that quantum fluctuations originated during the first moments after the Big Bang gave rise to the formation of galaxies and other structures of the Universe when inflation ends. Among these structures also primordial black holes (PBHs) may have been generated. The interest in PBHs relies on their possible connection with dark matter: they could constitute a portion or even the whole dark matter content of our Universe.\\ In this work we consider inflation in the Induced Gravity (IR) context and study possible mechanisms of amplification of the curvature perturbations generated during the cosmic acceleration. In particular we consider the possibility of a period of Constant Roll (CR). Starting from the previous work of Starobinsky et al. Our final purpose is to analyse the power spectrum of the scalar perturbations and to find in which conditions there is an enhancement of the power spectrum possibly leading to PBHs formation.

Analysis of retrieved shoulder prostheses

In the last years the number of shoulder arthroplasties has been increasing. Simultaneously the study of their shape, size and strength and the reasons that bring to a possible early explantation have not yet been examined in detail. The research carried out directly on explants is practically nonexistent, this means a poor understanding of the mechanisms leading the patient and so the surgeon, to their removal. The analysis of the mechanisms which are the cause of instability, dislocation, broken, fracture, etc, may lead to a change in the structure or design of the shoulder prostheses and lengthen the life of the implant in situ. The idea was to analyze 22 explants through three methods in order to find roughness, corrosion and surface wear. In the first method, the humeral heads and/or the glenospheres were examined with the interferometer, a machine that through electromagnetic waves gives information about the roughness of the surfaces under examination. The output of the device was a total profile containing both roughness and information on the waves (representing the spatial waves most characteristic on the surface). The most important value is called "roughness average" and brings the average value of the peaks found in the local defects of the surfaces. It was found that 42% of the prostheses had considerable peak values in the area where the damage was caused by the implant and not only by external events, such as possibly the surgeon's hand. One of the problems of interest in the use of metallic biomaterials is their resistance to corrosion. The clinical significance of the degradation of metal implants has been the purpose of the second method; the interaction between human body and metal components is critical to understand how and why they arrive to corrosion. The percentage of damage in the joints of the prosthetic components has been calculated via high resolution photos and the software ImageJ. The 40% and 50% of the area appeared to have scratches or multiple lines due to mechanical artifacts. The third method of analysis has been made through the use of electron microscopy to quantify the wear surface in polyethylene components. Different joint movements correspond to different mechanisms of damage, which were imprinted in the parts of polyethylene examined. The most affected area was located mainly in the side edges. The results could help the manufacturers to modify the design of the prostheses and thus reduce the number of explants. It could also help surgeons in choosing the model of the prosthesis to be implanted in the patient.