On the characterization of the mechanical behaviour of bonded steel-CFRP adhesive joints

The use of adhesively bonded carbon fiber reinforced polymers (CFRP) is well established to repair metallic structural elements in the aerospace industry for more than three decades. Despite a few exceptions, this technology has yet not been exploited for the steel construction industry where there is a great need to rehabilitate old metallic bridges. For instance, in Europe more than 30% of the railway bridge stock operated for more than 100 years. These bridges are made of old mild steel or puddle iron that exhibits poor behaviour due to the quality of the material itself and degradation caused by the long-term loading or environmental effects. The modest results for Steel/CFRP joints obtained may be due to the type of adhesive used. In fact, most of the previous studies utilized brittle adhesives specially developed for concrete structures. Recent ductile adhesives that made for the automotive industry for metallic joints should be more appropriate. In this study, an experimental investigation on the behaviour of CFRP/steel adhesively bonded joints is presented. A comparison between brittle adhesives and ductile adhesives is conducted. The results show that the ductile adhesives achieve much higher performance than the brittle ones. The brittle adhesives provide more stiffness to the adhesive joint. In the specimens with the ductile adhesives, the failure pattern started by yielding the steel bars first then the adhesive joint which is promising since it can facilitate the design significantly if the steel yielding can be used as a design criterion. The main disadvantage of ductile adhesives is they are usually more expensive than brittle ones. In order to solve this issue, bi-adhesive joints, in which the joint is mainly made of (low cost) brittle adhesive and ductile adhesive in the stress concentration region, are proposed. The results revealed very high improvement up to the yielding strength of the steel bars and with a balanced stiffness.

Debonding and crack propagation in cracked steel beams strengthened with CFRP and subjected to cyclic loads.

The reinforcement methods used to restore or increase the bearing capacity of metal structures are based on the application of steel plates to be bolted or welded to the original structure, which can cause problems to the integrity of the original structure. These difficulties can be overcome with the introduction of fiber-reinforced composite materials. FRPs are characterized by high strength to weight ratio, and they are very resistant to corrosion. In this dissertation a cracked steel I-beam reinforced with Carbon Fiber-Reinforced Polymer will be studied by performing a numerical evaluation of the structure with the commercial Finite Element Method software ABAQUS. The crack propagation will be computed using XFEM, while the debonding of the reinforcement layer will be found by considering a cohesive contact interface between the beam and the CFRP plate. The results will show the efficiency of the strengthening method in increasing the load carrying capacity of the cracked beam, and in reducing the crack opening of the initial notch.

Inkjet-printed poly(N-isopropylacrylamide)/graphene electrodes for selective electroanalytical sensing

The main research topic of the present master thesis consisted in the modification and electrochemical testing of inkjet printed graphene electrodes with a thin polymeric hydrogel layer made of cross-linked poly(N-isopropylacrylamide) (PNIPAAM) acting as a functional layer to fabricate selective sensors. The first experimental activities dealt with the synthesis of the polymeric hydrogel and the modification of the active surface of graphene sensors through photopolymerization. Simultaneous inkjet printing and photopolymerization of the hydrogel precursor inks onto graphene demonstrated to be the most effective and reproducible technique for the modification of the electrode with PNIPAAM. The electrochemical performance of the modified electrodes was tested through cyclic voltammetry. Voltammograms with standard redox couples with either positive, neutral or negative charges, suggested an electrostatic filtering effect by the hydrogel blocking negatively charged redox species in near neutral pH electrolyte solutions from reaching the electrode surface. PNIPAAM is a known thermo-responsive polymer, but the variation of temperature did not influence the filtering properties of the hydrogels for the redox couples studied. However, a variation of the filter capacity of the material was observed at pH 2 in which the PNIPAAM hydrogel, most likely in protonated form, became impermeable to positively charged redox species and permeable to negatively charged species. Finally, the filtering capacity of the electrodes modified with PNIPAAM was evaluated for the electrochemical determination of analytes in presence of negatively charge potential interferents, such as antioxidants like ascorbic acid. The outcome of the final experiments suggested the possibility to use the inkjet-printed PNIPAAM thin layer for electroanalytical applications as an electrostatic filter against interferents of opposite charges, typically present in complex matrices, such as food and beverages.