Atmospheric corrosion of quaternary bronzes (Cu-Sn-Zn-Pb): laboratory tests (accelerated ageing in wet & dry conditions)and field studies (the Bottego monument in Parma, Italy).

The interactions between outdoor bronzes and the environment, which lead to bronze corrosion, require a better understanding in order to design effective conservation strategies in the Cultural Heritage field. In the present work, investigations on real patinas of the outdoor monument to Vittorio Bottego (Parma, Italy) and laboratory studies on accelerated corrosion testing of inhibited (by silane-based films, with and without ceria nanoparticles) and non-inhibited quaternary bronzes are reported and discussed. In particular, a wet&dry ageing method was used both for testing the efficiency of the inhibitor and for patinating bronze coupons before applying the inhibitor. A wide range of spectroscopic techniques has been used, for characterizing the core metal (SEM+EDS, XRF, AAS), the corroded surfaces (SEM+EDS, portable XRF, micro-Raman, ATR-IR, Py-GC-MS) and the ageing solutions (AAS). The main conclusions were: 1. The investigations on the Bottego monument confirmed the differentiation of the corrosion products as a function of the exposure geometry, already observed in previous works, further highlighting the need to take into account the different surface features when selecting conservation procedures such as the application of inhibitors (i.e. the relative Sn enrichment in unsheltered areas requires inhibitors which effectively interact not only with Cu but also with Sn). 2. The ageing (pre-patination) cycle on coupons was able to reproduce the relative Sn enrichment that actually happens in real patinated surfaces, making the bronze specimens representative of the real support for bronze inhibitors. 3. The non-toxic silane-based inhibitors display a good protective efficiency towards pre-patinated surfaces, differently from other widely used inhibitors such as benzotriazole (BTA) and its derivatives. 4. The 3-mercapto-propyl-trimethoxy-silane (PropS-SH) additivated with CeO2 nanoparticles generally offered a better corrosion protection than PropS-SH.

Development of in vitro methods to test acetabular prosthetic reconstructions (messa a punto di metodi in vitro per la caratterizzazione biomeccanica di ricostruzioni acetabolari)

The revision hip arthroplasty is a surgical procedure, consisting in the reconstruction of the hip joint through the replacement of the damaged hip prosthesis. Several factors may give raise to the failure of the artificial device: aseptic loosening, infection and dislocation represent the principal causes of failure worldwide. The main effect is the raise of bone defects in the region closest to the prosthesis that weaken the bone structure for the biological fixation of the new artificial hip. For this reason bone reconstruction is necessary before the surgical revision operation. This work is born by the necessity to test the effects of bone reconstruction due to particular bone defects in the acetabulum, after the hip prosthesis revision. In order to perform biomechanical in vitro tests on hip prosthesis implanted in human pelvis or hemipelvis a practical definition of a reference frame for these kind of bone specimens is required. The aim of the current study is to create a repeatable protocol to align hemipelvic samples in the testing machine, that relies on a reference system based on anatomical landmarks on the human pelvis. In chapter 1 a general overview of the human pelvic bone is presented: anatomy, bone structure, loads and the principal devices for hip joint replacement. The purpose of chapters 2 is to identify the most common causes of the revision hip arthroplasty, analysing data from the most reliable orthopaedic registries in the world. Chapter 3 presents an overview of the most used classifications for acetabular bone defects and fractures and the most common techniques for acetabular and bone reconstruction. After a critical review of the scientific literature about reference frames for human pelvis, in chapter 4, the definition of a new reference frame is proposed. Based on this reference frame, the alignment protocol for the human hemipelvis is presented as well as the statistical analysis that confirm the good repeatability of the method.