Manufacturing and characterization of amorphous silicon alloys passivation layers for silicon hetero-junction solar cells

Nel presente lavoro di tesi magistrale sono stati depositati e caratterizzati film sottili (circa 10 nm) di silicio amorfo idrogenato (a-Si:H), studiando in particolare leghe a basso contenuto di ossigeno e carbonio. Tali layer andranno ad essere implementati come strati di passivazione per wafer di Si monocristallino in celle solari ad eterogiunzione HIT (heterojunctions with intrinsic thin layer), con le quali recentemente è stato raggiunto il record di efficienza pari a 24.7% . La deposizione è avvenuta mediante PECVD (plasma enhanced chemical vapour deposition). Tecniche di spettroscopia ottica, come FT-IR (Fourier transform infrared spectroscopy) e SE (spettroscopic ellipsometry) sono state utilizzate per analizzare le configurazioni di legami eteronucleari (Si-H, Si-O, Si-C) e le proprietà strutturali dei film sottili: un nuovo metodo è stato implementato per calcolare i contenuti atomici di H, O e C da misure ottiche. In tal modo è stato possibile osservare come una bassa incorporazione (< 10%) di ossigeno e carbonio sia sufficiente ad aumentare la porosità ed il grado di disordine a lungo raggio del materiale: relativamente a quest’ultimo aspetto, è stata sviluppata una nuova tecnica per determinare dagli spettri ellisometrici l’energia di Urbach, che esprime la coda esponenziale interna al gap in semiconduttori amorfi e fornisce una stima degli stati elettronici in presenza di disordine reticolare. Nella seconda parte della tesi sono stati sviluppati esperimenti di annealing isocrono, in modo da studiare i processi di cristallizzazione e di effusione dell’idrogeno, correlandoli con la degradazione delle proprietà optoelettroniche. L’analisi dei differenti risultati ottenuti studiando queste particolari leghe (a-SiOx e a-SiCy) ha permesso di concludere che solo con una bassa percentuale di ossigeno o carbonio, i.e. < 3.5 %, è possibile migliorare la risposta termica dello specifico layer, ritardando i fenomeni di degradazione di circa 50°C.

Electrical spectroscopy of rubrene bulk and thin film crystals

One of the most diffused electronic device is the field effect transistor (FET), contained in number of billions in each electronic device. Organic optoelectronics is an emerging field that exploits the unique properties of conjugated organic materials to develop new applications that require a combination of performance, low cost and processability. Organic single crystals are the material with best performances and purity among the variety of different form of organic semiconductors. This thesis is focused on electrical and optical characterization of Rubrene single crystal bulk and thin films. Rubrene bulk is well known but for the first time we studied thin films. The first Current-voltage characterization has been performed for the first time on three Rubrene thin films with three different thickness to extract the charge carriers mobility and to assess its crystalline structure. As results we see that mobility increase with thickness. Field effect transistor based on Rubrene thin films on $SiO_2$ have been characterize by current-voltage (I-V) analyses (at several temperatures) and reveals a hopping conduction. Hopping behavior probably is due to the lattice mismatch with the substrate or intrinsic defectivity of the thin films. To understand effects of contact resistance we tested thin films with the Transmission Line Method (TLM) method. The TLM method revealeds that contact resistance is negligible but evidenced a Schottky behavior in a limited but well determined range of T. To avoid this effect we carried out annealing treatment after the electrode evaporation iswe performed a compete I-V characterization as a function of in temperature to extract the electronic density of states (DOS) distribution through the Space Charge Limited Current (SCLC) method. The results show a DOS with an exponential trenddistribution, as expected. The measured mobility of thin films is about 0.1cm^2/Vs and it increases with the film thickness. Further studies are necessary to investigate the reason and improve performances. From photocurrent spectrum we calculated an Eg of about 2.2eV and both thin films and bulk have a good crystal order. Further measurement are necessary to solve some open problems