Synthesis and characterization of polymeric ionic liquid through free radical polymerization of acryloyl imidazolium-based ionic liquid monomer

This thesis investigates the synthesis of polymeric ionic liquid [(poly-acryloyloxy)6C6C1im][NTf2], by free radical polymerization of acryloyl imidazolium-base ionic liquid monomer [(acryloyloxy)6C6C1im][NTf2]. Moreover, the smartest synthetic route to obtain this monomer was investigated. Two different synthesis were compared. The first one started from the preparation of the monomer 6-chlorohexyl acrylate followed by substitution and metathesis to reach ionic liquid monomer. The second one started from synthesis of the ionic liquid [(HO)6C6C1im]Cl followed by metathesis and esterification in order to get ionic liquid monomer [(acryloyloxy)6C6C1im][NTf2].

Raft miniemulsion (co)polymerization of methyl methacrylate and n-butyl acrylate

This thesis work is part of a larger synthesis project about alkyd resins from natural sources, copolymerized with methyl acrylate and n-butyl acrylates, which wil be used for coatings purpose. The aim is to control the copolymerization of methyl acrylate and n-butyl acrylate in RAFT miniemulsion. The research was divided into three parts. First the homopolymerization of methyl methacrylate and n-butyl acrylate was studied by varying different parameters such as the amount of surfactant, the amount of initiator, pH, and especially the RAFT agent. Then two macro RAFT agents were synthesized, as suggested by the existing literature. Finally, the two monomers were copolymerized using both the RAFT used for the homopolymerization and those synthesized in the second stage. To verify the obtained control over the polymerization, the synthesized polymers were analyzed by gel permeation chromatography, GPC, thus finding their molecular weight and its polydispersity.

Synthesis, characterization and crystallization of bionanocomposites based on PLLA, PCL and nanocellulose

In recent years, environmental concerns and the expected shortage in the fossil reserves have increased further development of biomaterials. Among them, poly(lactide) PLA possess some potential properties such as good ability process, excellent tensile strength and stiffness equivalent to some commercial petroleum-based polymers (PP, PS, PET, etc.). This biobased polymer is also biodegradable and biocompatible However, one great disadvantage of commercial PLA is slow crystallization rate, which restricts its use in many fields. Using of nanofillers is viewed as an efficient strategy to overcome this problem. In this thesis, the effect of bionanofillers in neat PLA and in blends of poly (L-lactide)(PLA)/poly(ε-Caprolactone) (PCL) has been investigated. The used nanofillers are: poly(L-lactide-co-ε-caprolactone) and poly(L-lactide-b-ε-caprolactone) grafted on cellulose nanowhiskers and neat cellulose nanowhiskers (CNW). The grafting reaction of poly(L-lactide-co-caprolactone) and poly (L-lactide-b-caprolactone) on the nanocellulose has been performed by the grafting from technique. In this way the polymerization reaction it is directly initiated on the substrate surface. The condition of the reaction were chosen after a temperature and solvent screening. By non-isothermal an isothermal DSC analysis the effect of bionanofillers on PLA and 80/20 PLA/PCL was evaluated. Non-isothermal DSC scans show a nucleating effect of the bionanofillers on PLA. This effect is detectable during PLA crystallization from the glassy state. Cold crystallization temperature is reduced upon the addition of the poly(L-lactide-b-caprolactone) grafted on cellulose nanowhiskers that is most performing bionanofiller in acting as a nucleating agent. On the other hand, DSC isothermal analysis on the overall crystallization rate indicate that cellulose nanowhiskers are best nucleating agents during isothermal crystallization from the melt state. In conclusion, nanofillers have different behavior depending on the processing conditions. However, the efficiency of our nanofillers as nucleating agent was clearly demonstrated in both isothermal as in non-isothermal condition.