Catalysts for H2 production

The research of new catalysts for the hydrogen production described in this thesis was inserted within a collaboration of Department of Industrial Chemistry and Materials of University of Bologna and Air Liquide (Centre de Recherche Claude-Delorme, Paris). The aim of the work was focused on the study of new materials, active and stable in the hydrogen production from methane, using either a new process, the catalytic partial oxidation (CPO), or a enhanced well-established process, the steam methane reforming (SMR). Two types of catalytic materials were examined: 1) Bulk catalysts, i.e. non-supported materials, in which the active metals (Ni and/or Rh) are stabilized inside oxidic matrix, obtained from perovskite type compounds (PVK) and from hydrotalcite type precursors (HT); 2) Structured catalysts, i.e. catalysts supported on materials having high thermal conductivity (SiC and metallic foams). As regards the catalytic partial oxidation, the effect of the metal (Ni and/or Rh), the role of the metal/matrix ratio and the matrix formulation of innovative catalysts obtained from hydrotalcite type precursors and from perovskites were examined. In addition, about steam reforming process, the study was carried out first on commercial type catalysts, examining the deactivation in industrial conditions, the role of the operating conditions and the activity of different type of catalysts. Then, innovative materials bulk (PVK and HT) and structured catalysts (SiC and metallic foam) were studied and a new preparation method was developed.

Deidrogenazione catalitica di idrocarburi per la produzione di H2 "on-board"

Lo studio della deidrogenazione catalitica di idrocarburi affronta uno dei problemi principali per l'applicazione delle fuel cells in aeromobili. La conversione di miscele di idrocarburi in H2 può essere eseguita in loco, evitando le difficoltà di stoccaggio dell'idrogeno: l'H2 prodotto è privo di CO e CO2 e può essere alimentato direttamente alle celle a combustibile per dare energia ai sistemi ausiliari, mentre i prodotti deidrogenati, mantenendo le loro originali caratteristiche possono essere riutilizzati come carburante. In questo un lavoro è stato effettuato uno studio approfondito sulla deidrogenazione parziale (PDH) di diverse miscele di idrocarburi e carburante avio JetA1 desolforato utilizzando Pt-Sn/Al2O3, con l'obiettivo di mettere in luce i principali parametri (condizioni di reazione e composizione di catalizzatore) coinvolti nel processo di deidrogenazione. Inoltre, la PDH di miscele idrocarburiche e di Jet-A1 ha evidenziato che il problema principale in questa reazione è la disattivazione del catalizzatore, a causa della formazione di residui carboniosi e dell’avvelenamento da zolfo. Il meccanismo di disattivazione da residui carboniosi è stato studiato a fondo, essendo uno dei principali fattori che influenzano la vita del catalizzatore e di conseguenza l'applicabilità processo. Alimentando molecole modello separatamente, è stato possibile discriminare le classi di composti che sono coinvolti principalmente nella produzione di H2 o nell’avvelenamento del catalizzatore. Una riduzione parziale della velocità di disattivazione è stata ottenuta modulando l'acidità del catalizzatore al fine di ottimizzare le condizioni di reazione. I catalizzatori Pt-Sn modificati hanno mostrato ottimi risultati in termini di attività, ma soffrono di una disattivazione rapida in presenza di zolfo. Così, la sfida finale di questa ricerca era sviluppare un sistema catalitico in grado di lavorare in condizioni reali con carburante ad alto tenore di zolfo, in questo campo sono stati studiati due nuove classi di materiali: Ni e Co fosfuri supportati su SiO2 e catalizzatori Pd-Pt/Al2O3.

Catalysts and processes for next-generation H2 production

The present study is focused on the development of new VIII group metal on CeO2 – ZrO2 (CZO) catalyst to be used in reforming reaction for syngas production. The catalyst are tested in the oxyreforming process, extensively studied by Barbera [44] in a new multistep process configuration, with intermediate H2 membrane separation, that can be carried out at lower temperature (750°C) with respect the reforming processes (900 – 1000°C). In spite of the milder temperatures, the oxy-reforming conditions (S/C = 0.7; O2/C = 0.21) remain critical regarding the deactivation problems mainly deriving from thermal sintering and carbon formation phenomena. The combination of the high thermal stability characterizing the ZrO2, with the CeO2 redox properties, allows the formation of stable mixed oxide system with high oxygen mobility. This feature can be exploited in order to contrast the carbon deposition on the active metal surface through the oxidation of the carbon by means of the mobile oxygen atoms available at the surface of the CZO support. Ce0.5Zr0.5O2 is the phase claimed to have the highest oxygen mobility but its formation is difficult through classical synthesis (co-precipitation), hence a water-in-oil microemulsion method is, widely studied and characterized. Two methods (IWI and bulk) for the insertion of the active metal (Rh, Ru, Ni) are followed and their effects, mainly related to the metal stability and dispersion on the support, are discussed, correlating the characterization with the catalytic activity. Different parameters (calcination and reduction temperatures) are tuned to obtain the best catalytic system both in terms of activity and stability. Interesting results are obtained with impregnated and bulk catalysts, the latter representing a new class of catalysts. The best catalysts are also tested in a low temperature (350 – 500°C) steam reforming process and preliminary tests with H2 membrane separation have been also carried out.

Study and development of BaCe0.65Zr0.20Y0.1503-Δ (BCZY) – Gd0.2Ce0.8O2-Δ (GDC) dense ceramic membranes sysyem for high temperature H2 purification

The first main conclusion drawn from this dissertation concerns the amount of Pt deposited on the asymmetric layer of membrane produced by tape casting porosity shaping method. Three different amounts were investigated (0.15, 1.5 and 4.5 mg cm-2 ). The most optimal performance, based on H2 permeation performances, was attained when 1.5 mg cm-2 of Pt was deposited on the porous layer, resulting in a 0.642 mL min-1 cm-2 permeated H2 when 80% H2 in He was employed as the feed. Pt deposition method is influenced by the concentration of the Pt precursor, which results in different morphology of the catalyst. The second development focused on further optimization on tape casting membranes concerning the solvent employed for the Pt catalyst deposition. The same concentration of Pt was employed, depositing 1.5 mg cm-2 on the porous side of the membrane, but a mixture of acetone and water was employed as solvent. This mixture allowed the suppression of effects leading to poorly dispersed particles. As a result, it was possible to achieve 0.74 mL min-1 cm-2 at 750°C with 50% H2 in He. Lastly, first-ever permeation performance measurements into an innovative ceramic membrane type for hydrogen separation was investigated. In-depth research was done on a group of hierarchically-structured BaCe0.65Zr0.20Y0.15O3-δ(BCZY) - Gd0.2Ce0.8O2-δ(GDC) membranes produced by freeze casting porosity shaping method. Membranes were investigated observing the effect of deposition solvent and the effect of porous layer thickness. Employing a mixture of Acetone and water resulted in better hydrogen permeation at temperatures (T > 650°C), reaching 0.26 mL min-1 cm-2 at 750°C with 50% H2 in He. The reduction of porous layer thickness led to a hydrogen flow of 0.33 mL min-1 cm-2 , at 750°C with 50% H2 in He.