A chemical-loop approach for the generation of hydrogen by means of ethanol reforming

The work investigates the feasibility of a new process aimed at the production of hydrogen with inherent separation of carbon oxides. The process consists in a cycle in which, in the first step, a mixed metal oxide is reduced by ethanol (obtained from biomasses). The reduced metal is then contacted with steam in order to split the water and sequestrating the oxygen into the looping material’s structure. The oxides used to run this thermochemical cycle, also called “steam-iron process” are mixed ferrites in the spinel structure MeFe2O4 (Me = Fe, Co, Ni or Cu). To understand the reactions involved in the anaerobic reforming of ethanol, diffuse reflectance spectroscopy (DRIFTS) was used, coupled with the mass analysis of the effluent, to study the surface composition of the ferrites during the adsorption of ethanol and its transformations during the temperature program. This study was paired with the tests on a laboratory scale plant and the characterization through various techniques such as XRD, Mössbauer spectroscopy, elemental analysis... on the materials as synthesized and at different reduction degrees In the first step it was found that besides the generation of the expected CO, CO2 and H2O, the products of ethanol anaerobic oxidation, also a large amount of H2 and coke were produced. The latter is highly undesired, since it affects the second step, during which water is fed over the pre-reduced spinel at high temperature. The behavior of the different spinels was affected by the nature of the divalent metal cation; magnetite was the oxide showing the slower rate of reduction by ethanol, but on the other hand it was that one which could perform the entire cycle of the process more efficiently. Still the problem of coke formation remains the greater challenge to solve.

Newly developed electrosynthesis of Layered Double Hydroxides: application to sensing, energy storage and conversion

Layered Double hydroxides (LDHs) have been widely studied for their plethora of fascinating features and applications. The potentiostatic electrodeposition of LDHs has been extensively applied in the literature as a fast and direct method to substitute classical chemical routes. However, it does not usually allow for a fine control of the M(II)/M(III) ratio in the synthesized material and it is not suitable for large anions intercalation. Therefore, in this work a novel protocol has been proposed with the aim to overcome all these constraints using a method based on potentiodynamic synthesis. LDHs of controlled composition were prepared using different molar ratios of the trivalent to bivalent cations in the electrolytic solution ranging from 1:1 to 1:4. Moreover, we were able to produce electrochemically LDHs intercalated with carbon nanomaterials for the first time. A one-step procedure which contemporaneously allows for the Ni/Al-LDH synthesis, the reduction of graphene oxide (GO) and its intercalation inside the structure has been developed. The synthesised materials have been applied in several fields of interest. First of all, LDHs with a ratio 3:1 were exploited, and displayed good performances as catalysts for 5-(hydroxymethyl)furfural electro-oxidation, thus suggesting to carry out further investigation for applications in the field of industrial catalysis. The same materials, but with different metals ratios, were tested as catalysts for Oxygen Evolution Reaction, obtaining results comparable to LDHs synthesised by the classical co-precipitation method and also a better activity with respect to LDHs obtained by the potentiostatic approach. The composite material based on LDH and reduced graphene oxide was employed to fabricate a cathode of a hybrid supercapacitor coupled with an activated carbon anode. We can thus conclude that, to date, the potentiodynamic method has the greatest potential for the rapid synthesis of reproducible films of Co and Ni-based LDHs with controlled composition.