Aquivion-based spray freeze-dried composite catalysts for the cascade conversion of furfural to γ-valerolactone

Furfural is one of the most promising biomass derived platform molecules. It is to this day produced in volumes above 300 ktons per year from the hydrolysis and dehydration of hemicellulose, one of the main components of lignocellulosic biomass. While the majority of the yearly production is destined to selective reduction to furfuryl alcohol for the production of furan resins, these molecules hold great potential for the production of more valuable chemicals, fuels, fuel additives and solvents. Among these products are alkyl levulinates and γ-valerolactone. To convert furfural to these target products, a cascade process involving Lewis acidity-catalysed reduction steps and Brønsted acidity-catalysed steps. In order to develop catalysts capable of promoting the one-pot domino reaction from furfural to γ-valerolactone, the two kinds of acidity must both be present. To this end, in this work, the spray freeze-drying technique is employed to combine the high activity and strong Brønsted acidity of Aquivion with the structural properties and Lewis acidity of different supporting metal oxide, forming composite catalysts. The flexibility of the spray freeze-drying technique and the modulable composition of the catalysts allowed a thorough study of the complex network of equilibria underlying the cascade reaction, while achieving high selectivities towards the final product.

Biodegradable systems for the development of functional materials

This PhD work was aimed to design, develop, and characterize gelatin-based scaffolds, for the repair of defects in the muscle-skeletal system. Gelatin is a biopolymer widely used for pharmaceutical and medical applications, thanks to its biodegradability and biocompatibility. It is obtained from collagen via thermal denaturation or chemical-physical degradation. Despite its high potential as biomaterial, gelatin exhibits poor mechanical properties and a low resistance in aqueous environment. Crosslinking treatment and enrichment with reinforcement materials are thus required for biomedical applications. In this work, gelatin based scaffolds were prepared following three different strategies: films were prepared through the solvent casting method, electrospinning technique was applied for the preparation of porous mats, and 3D porous scaffolds were prepared through freeze-drying. The results obtained on films put into evidence the influence of pH, crosslinking and reinforcement with montmorillonite (MMT), on the structure, stability and mechanical properties of gelatin and MMT/gelatin composites. The information acquired on the effect of crosslinking in different conditions was utilized to optimize the preparation procedure of electrospun and freeze-dried scaffolds. A successful method was developed to prepare gelatin nanofibrous scaffolds electrospun from acetic acid/water solution and stabilized with a non-toxic crosslinking agent, genipin, able to preserve their original morphology after exposure to water. Moreover, the co-electrospinning technique was used to prepare nanofibrous scaffolds at variable content of gelatin and polylactic acid. Preliminary in vitro tests indicated that the scaffolds are suitable for cartilage tissue engineering, and that their potential applications can be extended to cartilage-bone interface tissue engineering. Finally, 3D porous gelatin scaffolds, enriched with calcium phosphate, were prepared with the freeze-drying method. The results indicated that the crystallinity of the inorganic phase influences porosity, interconnectivity and mechanical properties. Preliminary in vitro tests show good osteoblast response in terms of proliferation and adhesion on all the scaffolds.