Sistemi adesivi con applicazioni in campo biomedicale

Polymeric adhesives have been used for many applications like suture and embolization, instead of classic surgical methods or as for dental uses. In this work both subjects have been investigated and the results separated in two parts. In the first, new dentinal adhesives with different polymerizable groups (methacrylic or vinyl-ethereal) were synthesized. A low sensitivity to hydrolysis and equal or enhanced properties, compared to existing commercial products, were considered essentials. Moreover, these monomers need to polymerize by radical photopolymerization and functional groups of different characteristics were tested. All these products were characterized by microtensile bond strength test to determine the bonding strength between the adhesive and tooth. Concerning embolization, cyanoacrylates are nowadays the most-used adhesives in surgery. Thus, they must respond to several requirements. For instance, polymerization time and adhesive strength need to be low, to avoid diffusion of the products in the body and adhesion to the catheter. In order to overcome these problems we developed new cyanoacrylates, which practically instantly polymerize upon contact with blood but do not demonstrate strong adhesion to the catheter, thank to the presence of fluorine atoms, linked to the ester chain. The synthesis of these products was carried out in several steps, such as the depolymerization of the corresponding oligomers at high temperature in acid conditions. Two types of adhesion strengths were determined. Bonding strength between human veins and a microcatheter was determined in vitro by using organic materials as the most realistic model. Another test, on two layers of skin, was conducted to verify the possible use of these new cyanoacrylates as a glue for sutures. As a conclusion, we were able to demonstrate that some of the prepared monomers posses adhesive strength and polymerization time lower than the commercial product Glubran2.

Zirconia in dentistry

The above factors emphasize the scope of this thesis for further investigations on zirconia, the improvement of all-ceramic zirconia restorations, and especially the interaction of zirconia and veneering and its influence on the performance of the whole restoration. The introduction, chapter 1, gave a literature overview on zirconia ceramics. In chapter 2, the objective of the study was to evaluate the effect of abrading before and after sintering using alumina-based abrasives on the surface of yttria-tetragonal zirconia polycrystals. Particular attention was paid to the amount of surface stress–assisted phase transformation (tetragonal→monoclinic) and the presence of microcracks. Chapter 3 is based on the idea that the conventional sintering techniques for zirconia based materials, which are commonly used in dental reconstruction, may not provide a uniform heating, with consequent generation of microstructural flaws in the final component. As a consequence of the sintering system, using microwave heating, may represent a viable alternative. The purpose of the study was to compare the dimensional variations and physical and microstructural characteristics of commercial zirconia (Y-TZP), used as a dental restoration material, sintered in conventional and microwave furnaces. Chapter 4 described the effect of sandblasting before and after sintering on the surface roughness of zirconia and the microtensile bond strength of a pressable veneering ceramic to zirconia.

Studio degli effetti della mordenzatura con acido fluoridrico sul disilicato di litio utilizzato in odontoiatria

Scopo dello studio: valutare i cambiamenti indotti da diversi trattamenti di mordenzatura sulla morfologia superficiale e sulla microstruttura di due vetro-ceramiche a base disilicato di litio (IPS e.max® Press e IPS e.max® CAD) ed esaminarne gli effetti sia sull’adesione con un cemento resinoso che sulla resistenza alla flessione. Materiali e metodi: Settanta dischetti (12 mm di diametro, 2 mm di spessore) di ogni ceramica sono stati preparati e divisi in 5 gruppi: nessun trattamento (G1), HF 5% 20s (G2), HF 5% 60s (G3), HF 9.6% 20s (G4), HF 9.6% 60s (G5). Un campione per ogni gruppo è stato analizzato mediante profilometro ottico e osservato al SEM. Per gli altri campioni è stato determinato lo shear bond strength (SBS) con un cemento resinoso. Dopo l’SBS test, i campioni sono stati caricati fino a frattura utilizzando il piston-on-three-ball test per determinarne la resistenza biassiale alla flessione. Risultati: L’analisi morfologica e microstrutturale dei campioni ha rivelato come diversi trattamenti di mordenzatura producano delle modifiche nella rugosità superficiale che non sono direttamente collegate ad un aumento dei valori di adesione e dei cambiamenti microstrutturali che sono più rilevanti con l’aumento del tempo di mordenzatura e di concentrazione dell’acido. I valori medi di adesione (MPa) per IPS e.max® CAD sono significativamente più alti in G2 e G3 (21,28 +/- 4,9 e 19,55 +/- 5,41 rispettivamente); per IPS e.max® Press, i valori più elevati sono in G3 (16,80 +/- 3,96). La resistenza biassiale alla flessione media (MPa) è più alta in IPS e.max® CAD (695 +/- 161) che in IPS e.max® Press (588 +/- 117), ma non è non influenzata dalla mordenzatura con HF. Conclusioni: il disilicato di litio va mordenzato preferibilmente con HF al 5%. La mordenzatura produce alcuni cambiamenti superficiali e microstrutturali nel materiale, ma tali cambiamenti non ne influenzano la resistenza in flessione.