Nanocarbon-Supported Electrocatalysts for the Alkaline Water Splitting and Fuel Cells

Electrocatalysts play a significant role in the processes of electrochemical energy conversion. This thesis focuses on the preparation of carbon-supported nanomaterials and their application as electrocatalysts for alkaline water electrocatalysis and fuel cell. A general synthetic route was developed, i.e., species intercalate into carbon layers of graphite forming graphite intercalation compound, followed by dispersion producing graphenide solution, which then as reduction agent reacts with different metal sources generating the final materials. The first metal precursor used was non-noble metal iron salt, which generated iron (oxide) nanoparticles finely dispersed on carbon layers in the final composite materials. Meanwhile, graphite starting materials differing in carbon layer size were utilized, which would diversify corresponding graphenide solutions, and further produce various nanomaterials. The characterization results showed that iron (oxide) nanoparticles varying in size were obtained, and the size was determined by the starting graphite material. It was found that they were electrocatalytically active for oxygen reactions. In particular, the one with small iron (oxide) nanoparticles showed excellent electrocatalytic activity for both oxygen reduction reaction (ORR) and oxygen evolution reaction (OER). Afterwards, the metal precursor was tuned from non-noble metal salt to noble metal salt. It was confirmed that carbon-supported Rh, Pt, and RhPt (oxide) nanoparticle composite materials were also successfully obtained from the reaction between graphenide solution and corresponding noble metal precursor. The electrochemical measurements showed that the prepared noble metal-based nanomaterials were quite effective for hydrogen evolution reaction (HER) electrocatalysis, and the Rh sample could also display excellent electrocatalytic property towards OER. Moreover, by this synthetic approach carbon-supported noble metal Pt and non-noble metal nickel (Ni) composite material was also prepared. Therefore, the utilization efficiency of noble metal could be improved. The prepared NiPt sample displayed a property close to benchmark HER electrocatalyst.

Newly developed electrosynthesis of Layered Double Hydroxides: application to sensing, energy storage and conversion

Layered Double hydroxides (LDHs) have been widely studied for their plethora of fascinating features and applications. The potentiostatic electrodeposition of LDHs has been extensively applied in the literature as a fast and direct method to substitute classical chemical routes. However, it does not usually allow for a fine control of the M(II)/M(III) ratio in the synthesized material and it is not suitable for large anions intercalation. Therefore, in this work a novel protocol has been proposed with the aim to overcome all these constraints using a method based on potentiodynamic synthesis. LDHs of controlled composition were prepared using different molar ratios of the trivalent to bivalent cations in the electrolytic solution ranging from 1:1 to 1:4. Moreover, we were able to produce electrochemically LDHs intercalated with carbon nanomaterials for the first time. A one-step procedure which contemporaneously allows for the Ni/Al-LDH synthesis, the reduction of graphene oxide (GO) and its intercalation inside the structure has been developed. The synthesised materials have been applied in several fields of interest. First of all, LDHs with a ratio 3:1 were exploited, and displayed good performances as catalysts for 5-(hydroxymethyl)furfural electro-oxidation, thus suggesting to carry out further investigation for applications in the field of industrial catalysis. The same materials, but with different metals ratios, were tested as catalysts for Oxygen Evolution Reaction, obtaining results comparable to LDHs synthesised by the classical co-precipitation method and also a better activity with respect to LDHs obtained by the potentiostatic approach. The composite material based on LDH and reduced graphene oxide was employed to fabricate a cathode of a hybrid supercapacitor coupled with an activated carbon anode. We can thus conclude that, to date, the potentiodynamic method has the greatest potential for the rapid synthesis of reproducible films of Co and Ni-based LDHs with controlled composition.

Polyaniline-based materials and nanocomposites: from energy storage to sensing applications

The research work described in this thesis concerns materials for both energy storage and sensoristics applications. Firstly, the synthesis and characterization of magnetite (Fe3O4) functionalyzed with [3-(2-propynylcarbamate)propyl]triethoxysilane (PPTEOS) capable to reduce the gold precursor chloroauric acid (HAuCl4) without the need of additional reducing or stabilising agents is described. These nanoparticles were tested to improve performances of symmetric capacitors based on polyaniline and graphite foil. Energy storage applications were investigated also during six months stay at EPFL University of Lausanne where an investigation about different tailored catalysts for Oxygen Evolution Reaction in a particular Redox Flow Battery was carried out. For what concerns sensing applications, new materials based on cellulose modified with polyaniline and poly(2-acrylamido-2-methyl-1-propanesulfonic acid) (PAAMPSA) were synthesized, characterized and applied to monitor pressure, humidity, heart rate and lastly, bread fermentation in collaboration with the University of Fribourg and Zurich. The characterizations of all the materials investigated compriseed numerous techniques such as infrared attenuated total reflectance spectroscopy (IR-ATR), thermogravimetric analysis (TGA), scanning and transmission electron microscopy (SEM and TEM), alongside linear and cyclic voltammetry (LSV and CV), electrochemical impedance spectroscopy (EIS) and chronoamperometric analyses.