Development and characterization of non-oxide ceramic composites for mechanical and tribological applications

The main reasons for the attention focused on ceramics as possible structural materials are their wear resistance and the ability to operate with limited oxidation and ablation at temperatures above 2000°C. Hence, this work is devoted to the study of two classes of materials which can satisfy these requirements: silicon carbide -based ceramics (SiC) for wear applications and borides and carbides of transition metals for ultra-high temperatures applications (UHTCs). SiC-based materials: Silicon carbide is a hard ceramic, which finds applications in many industrial sectors, from heat production, to automotive engineering and metals processing. In view of new fields of uses, SiC-based ceramics were produced with addition of 10-30 vol% of MoSi2, in order to obtain electro conductive ceramics. MoSi2, indeed, is an intermetallic compound which possesses high temperature oxidation resistance, high electrical conductivity (21·10-6 Ω·cm), relatively low density (6.31 g/cm3), high melting point (2030°C) and high stiffness (440 GPa). The SiC-based ceramics were hot pressed at 1900°C with addition of Al2O3-Y2O3 or Y2O3-AlN as sintering additives. The microstructure of the composites and of the reference materials, SiC and MoSi2, were studied by means of conventional analytical techniques, such as X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (SEM-EDS). The composites showed a homogeneous microstructure, with good dispersion of the secondary phases and low residual porosity. The following thermo-mechanical properties of the SiC-based materials were measured: Vickers hardness (HV), Young’s modulus (E), fracture toughness (KIc) and room to high temperature flexural strength (σ). The mechanical properties of the composites were compared to those of two monolithic SiC and MoSi2 materials and resulted in a higher stiffness, fracture toughness and slightly higher flexural resistance. Tribological tests were also performed in two configurations disco-on-pin and slideron cylinder, aiming at studying the wear behaviour of SiC-MoSi2 composites with Al2O3 as counterfacing materials. The tests pointed out that the addition of MoSi2 was detrimental owing to a lower hardness in comparison with the pure SiC matrix. On the contrary, electrical measurements revealed that the addition of 30 vol% of MoSi2, rendered the composite electroconductive, lowering the electrical resistance of three orders of magnitude. Ultra High Temperature Ceramics: Carbides, borides and nitrides of transition metals (Ti, Zr, Hf, Ta, Nb, Mo) possess very high melting points and interesting engineering properties, such as high hardness (20-25 GPa), high stiffness (400-500 GPa), flexural strengths which remain unaltered from room temperature to 1500°C and excellent corrosion resistance in aggressive environment. All these properties place the UHTCs as potential candidates for the development of manoeuvrable hypersonic flight vehicles with sharp leading edges. To this scope Zr- and Hf- carbide and boride materials were produced with addition of 5-20 vol% of MoSi2. This secondary phase enabled the achievement of full dense composites at temperature lower than 2000°C and without the application of pressure. Besides the conventional microstructure analyses XRD and SEM-EDS, transmission electron microscopy (TEM) was employed to explore the microstructure on a small length scale to disclose the effective densification mechanisms. A thorough literature analysis revealed that neither detailed TEM work nor reports on densification mechanisms are available for this class of materials, which however are essential to optimize the sintering aids utilized and the processing parameters applied. Microstructural analyses, along with thermodynamics and crystallographic considerations, led to disclose of the effective role of MoSi2 during sintering of Zrand Hf- carbides and borides. Among the investigated mechanical properties (HV, E, KIc, σ from room temperature to 1500°C), the high temperature flexural strength was improved due to the protective and sealing effect of a silica-based glassy phase, especially for the borides. Nanoindentation tests were also performed on HfC-MoSi2 composites in order to extract hardness and elastic modulus of the single phases. Finally, arc jet tests on HfC- and HfB2-based composites confirmed the excellent oxidation behaviour of these materials under temperature exceeding 2000°C; no cracking or spallation occurred and the modified layer was only 80-90 μm thick.

Studio del comportamento meccanico di smalti porcellanati per substrati metallici

Composite porcelain enamels are inorganic coatings for metallic components based on a special ceramic-vitreous matrix in which specific additives are randomly dispersed. The ceramic-vitreous matrix is made by a mixture of various raw materials and elements and in particular it is based on boron-silicate glass added with metal oxides(1) of titanium, zinc, tin, zirconia, alumina, ecc. These additions are often used to improve and enhance some important performances such as corrosion(2) and wear resistance, mechanical strength, fracture toughness and also aesthetic functions. The coating process, called enamelling, depends on the nature of the surface, but also on the kind of the used porcelain enamel. For metal sheets coatings two industrial processes are actually used: one based on a wet porcelain enamel and another based on a dry-silicone porcelain enamel. During the firing process, that is performed at about 870°C in the case of a steel substrate, the enamel raw material melts and interacts with the metal substrate so enabling the formation of a continuous varying structure. The interface domain between the substrate and the external layer is made of a complex material system where the ceramic vitreous and the metal constituents are mixed. In particular four main regions can be identified, (i) the pure metal region, (ii) the region where the metal constituents are dominant compared with the ceramic vitreous components, (iii) the region where the ceramic vitreous constituents are dominant compared with the metal ones, and the fourth region (iv) composed by the pure ceramic vitreous material. It has also to be noticed the presence of metallic dendrites that hinder the substrate and the external layer passing through the interphase region. Each region of the final composite structure plays a specific role: the metal substrate has mainly the structural function, the interphase region and the embedded dendrites guarantee the adhesion of the external vitreous layer to the substrate and the external vitreous layer is characterized by an high tribological, corrosion and thermal shock resistance. Such material, due to its internal composition, functionalization and architecture can be considered as a functionally graded composite material. The knowledge of the mechanical, tribological and chemical behavior of such composites is not well established and the research is still in progress. In particular the mechanical performances data about the composite coating are not jet established. In the present work the Residual Stresses, the Young modulus and the First Crack Failure of the composite porcelain enamel coating are studied. Due to the differences of the porcelain composite enamel and steel thermal properties the enamelled steel sheets have residual stresses: compressive residual stress acts on the coating and tensile residual stress acts on the steel sheet. The residual stresses estimation has been performed by measuring the curvature of rectangular one-side coated specimens. The Young modulus and the First Crack Failure (FCF) of the coating have been estimated by four point bending tests (3-7) monitored by means of the Acoustic Emission (AE) technique(5,6). In particular the AE information has been used to identify, during the bending tests, the displacement domain over which no coating failure occurs (Free Failure Zone, FFZ). In the FFZ domain, the Young modulus has been estimated according to ASTM D6272-02. The FCF has been calculated as the ratio between the displacement at the first crack of the coating and the coating thickness on the cracked side. The mechanical performances of the tested coated specimens have also been related and discussed to respective microstructure and surface characteristics by double entry charts.

Environmental weathering of natural and artificial stones used in historical architecture: influence of microstructure and new restoration methods

For some study cases (the Cathedral of Modena, Italy, XII-XIV century; the Ducal Palace in Mantua, Italy, XVI century; the church of San Francesco in Fano, Italy, XIV-XIX century), considered as representative of the use of natural and artificial stones in historical architecture, the complex interaction between environ-mental aggressiveness, materials’ microstructural characteristics and degradation was investigated. From the results of such analyses, it was found that materials microstructure plays a fundamental role in the actual extent to which weathering mechanisms affect natural and artificial stones. Consequently, the need of taking into account the important role of material microstructure, when evaluating the environmental aggressiveness to natural and artificial stones, was highlighted. Therefore, a possible quantification of the role of microstructure on the resistance to environmental attack was investigated. By exposing stone samples, with significantly different microstructural features, to slightly acidic aqueous solutions, simulating clean and acid rain, a good correlation between weight losses and the product of carbonate content and specific surface area (defined as the “vulnerable specific surface area”) was found. Alongside the evaluation of stone vulnerability, the development of a new consolidant for weathered carbonate stones was undertaken. The use of hydroxya-patite, formed by reacting the calcite of the stone with an aqueous solution of di-ammonium hydrogen phosphate, was found to be a promising consolidating tech-nique for carbonates stones. Indeed, significant increases in the mechanical prop-erties can be achieved after the treatment, which has the advantage of simply con-sisting in a non-hazardous aqueous solution, able to penetrate deeply into the stone (> 2 cm) and bring significant strengthening after just 2 days of reaction. Furthermore, the stone sorptivity is not eliminated after treatment, so that water and water vapor exchanges between the stone and the environment are not com-pletely blocked.

I materiali ceramici trasparenti: preparazione, caratterizzazione e correlazione microstruttura-proprietà

This thesis focuses on the ceramic process for the production of optical grade transparent materials to be used as laser hosts. In order to be transparent a ceramic material must exhibit a very low concentration of defects. Defects are mainly represented by secondary or grain boundary phases and by residual pores. The strict control of the stoichiometry is mandatory to avoid the formation of secondary phases, whereas residual pores need to be below 150 ppm. In order to fulfill these requirements specific experimental conditions must be combined together. In addition powders need to be nanometric or at least sub-micrometric and extremely pure. On the other hand, nanometric powders aggregate easily and this leads to a poor, not homogeneous packing during shaping by pressing and to the formation of residual pores during sintering. Very fine powders are also difficult to handle and tend to absorb water on the surface. Finally, the powder manipulation (weighting operations, solvent removal, spray drying, shaping, etc), easily introduces impurities. All these features must be fully controlled in order to avoid the formation of defects that work as scattering sources thus decreasing the transparency of the material. The important role played by the processing on the transparency of ceramic materials is often underestimated. In the literature a high level of transparency has been reported by many authors but the description of the experimental process, in particular of the powder treatment and shaping, is seldom extensively described and important information that are necessary to reproduce the described results are often missing. The main goal of the present study therefore is to give additional information on the way the experimental features affect the microstructural evolution of YAG-based ceramics and thus the final properties, in particular transparency. Commercial powders are used to prepare YAG materials doped with Nd or Yb by reactive sintering under high vacuum. These dopants have been selected as the more appropriate for high energy and high peak power lasers. As far as it concerns the powder treatment, the thesis focuses on the influence of the solvent removal technique (rotavapor versus spray drying of suspensions in ethanol), the ball milling duration and speed, suspension concentration, solvent ratio, type and amount of dispersant. The influence of the powder type and process on the powder packing as well as the pressure conditions during shaping by pressing are also described. Finally calcination, sintering under high vacuum and in clean atmosphere, and post sintering cycles are studied and related to the final microstructure analyzed by SEM-EDS and HR-TEM, and to the optical and laser properties.

Fiber-reinforced ceramics for thermostructural applications, produced by polymer impregnation pyrolysis

Several CFCC (Continuous Fiber Composite Ceramics) production processes were tested, concluding that PIP (Polymer Impregnation, or Infiltration, Pyrolysis) and CBC (Chemically Bonded Ceramics) based procedures have interesting potential applications in the construction and transportation fields, thanks to low costs to get potentially useful thermomechanical performances. Among the different processes considered during the Doctorate (from the synthesis of new preceramic polymers, to the PIP production of SiC / SiC composites) the more promising results came from the PIP process with poly-siloxanes on basalt fabrics preforms. Low processing time and costs, together with fairly good thermomechanical properties were demonstrated, even after only one or two PIP steps in nitrogen flow. In alternative, pyrolysis in vacuum was also tested, a procedure still not discussed in literature, but which could originate an interesting reduction of production costs, with only a moderate detrimental effect on the mechanical properties. The resulting CFCC is a basalt / SiCO composite that can be applied for continuous operation up to 600°C, also in oxidant environment, as TG and XRD demonstrated. The failure upon loading is generally pseudo-plastic, being interlaminar delamination the most probable rupture mechanism. . The strength depends on several different factors (microstructure, polymer curing and subsequent ceramic phase evolution, fiber pull-out, fiber strength, fiber percentage) and can only be optimized empirically. In order to be open minded in selecting the best technology, also CBC (Chemically Bonded Ceramics) matrixes were considered during this Doctorate, making some preliminary investigations on fire-resistant phosphate cements. Our results on a commercial product evidenced some interesting thermomechanical capabilities, even after thermal treatments. However the experiments showed also phase change and possible cracking and deformations even on slow drying (at 130°C) and easy rehydration upon exposure to environmental humidity.

Ab initio quantum mechanical investigation of structural and chemical-physical properties of selected minerals for minero-petrological, structural ceramic and biomaterial applications

The purpose of this thesis is the atomic-scale simulation of the crystal-chemical and physical (phonon, energetic) properties of some strategically important minerals for structural ceramics, biomedical and petrological applications. These properties affect the thermodynamic stability and rule the mineral-environment interface phenomena, with important economical, (bio)technological, petrological and environmental implications. The minerals of interest belong to the family of phyllosilicates (talc, pyrophyllite and muscovite) and apatite (OHAp), chosen for their importance in industrial and biomedical applications (structural ceramics) and petrophysics. In this thesis work we have applicated quantum mechanics methods, formulas and knowledge to the resolution of mineralogical problems ("Quantum Mineralogy”). The chosen theoretical approach is the Density Functional Theory (DFT), along with periodic boundary conditions to limit the portion of the mineral in analysis to the crystallographic cell and the hybrid functional B3LYP. The crystalline orbitals were simulated by linear combination of Gaussian functions (GTO). The dispersive forces, which are important for the structural determination of phyllosilicates and not properly con-sidered in pure DFT method, have been included by means of a semi-empirical correction. The phonon and the mechanical properties were also calculated. The equation of state, both in athermal conditions and in a wide temperature range, has been obtained by means of variations in the volume of the cell and quasi-harmonic approximation. Some thermo-chemical properties of the minerals (isochoric and isobaric thermal capacity) were calculated, because of their considerable applicative importance. For the first time three-dimensional charts related to these properties at different pressures and temperatures were provided. The hydroxylapatite has been studied from the standpoint of structural and phonon properties for its biotechnological role. In fact, biological apatite represents the inorganic phase of vertebrate hard tissues. Numerous carbonated (hydroxyl)apatite structures were modelled by QM to cover the broadest spectrum of possible biological structural variations to fulfil bioceramics applications.

Studio degli effetti della mordenzatura con acido fluoridrico sul disilicato di litio utilizzato in odontoiatria

Scopo dello studio: valutare i cambiamenti indotti da diversi trattamenti di mordenzatura sulla morfologia superficiale e sulla microstruttura di due vetro-ceramiche a base disilicato di litio (IPS e.max® Press e IPS e.max® CAD) ed esaminarne gli effetti sia sull’adesione con un cemento resinoso che sulla resistenza alla flessione. Materiali e metodi: Settanta dischetti (12 mm di diametro, 2 mm di spessore) di ogni ceramica sono stati preparati e divisi in 5 gruppi: nessun trattamento (G1), HF 5% 20s (G2), HF 5% 60s (G3), HF 9.6% 20s (G4), HF 9.6% 60s (G5). Un campione per ogni gruppo è stato analizzato mediante profilometro ottico e osservato al SEM. Per gli altri campioni è stato determinato lo shear bond strength (SBS) con un cemento resinoso. Dopo l’SBS test, i campioni sono stati caricati fino a frattura utilizzando il piston-on-three-ball test per determinarne la resistenza biassiale alla flessione. Risultati: L’analisi morfologica e microstrutturale dei campioni ha rivelato come diversi trattamenti di mordenzatura producano delle modifiche nella rugosità superficiale che non sono direttamente collegate ad un aumento dei valori di adesione e dei cambiamenti microstrutturali che sono più rilevanti con l’aumento del tempo di mordenzatura e di concentrazione dell’acido. I valori medi di adesione (MPa) per IPS e.max® CAD sono significativamente più alti in G2 e G3 (21,28 +/- 4,9 e 19,55 +/- 5,41 rispettivamente); per IPS e.max® Press, i valori più elevati sono in G3 (16,80 +/- 3,96). La resistenza biassiale alla flessione media (MPa) è più alta in IPS e.max® CAD (695 +/- 161) che in IPS e.max® Press (588 +/- 117), ma non è non influenzata dalla mordenzatura con HF. Conclusioni: il disilicato di litio va mordenzato preferibilmente con HF al 5%. La mordenzatura produce alcuni cambiamenti superficiali e microstrutturali nel materiale, ma tali cambiamenti non ne influenzano la resistenza in flessione.