Biomimetic Materials for Biomedical Applications

Objects with complex shape and functions have always attracted attention and interest. The morphological diversity and complexity of naturally occurring forms and patterns have been a motivation for humans to copy and adopt ideas from Nature to achieve functional, aesthetic and social value. Biomimetics is addressed to the design and development of new synthetic materials using strategies adopted by living organisms to produce biological materials. In particular, biomineralized tissues are often sophisticate composite materials, in which the components and the interfaces between them have been defined and optimized, and that present unusual and optimal chemical-physical, morphological and mechanical properties. Moreover, biominerals are generally produced by easily traceable raw materials, in aqueous media and at room pressure and temperature, that is through cheap process and materials. Thus, it is not surprising that the idea to mimic those strategies proper of Nature has been employed in several areas of applied sciences, such as for the preparation of liquid crystals, ceramic thin films computer switches and many other advanced materials. On this basis, this PhD thesis is focused on the investigation of the interaction of biologically active ions and molecules with calcium phosphates with the aim to develop new materials for the substitution and repair of skeletal tissue, according to the following lines: I. Modified calcium phosphates. A relevant part of this PhD thesis has been addressed to study the interaction of Strontium with calcium phosphates. It was demonstrated that strontium ion can substitute for calcium into hydroxyapatite, causing appreciable structural and morphological modifications. The detailed structural analysis carried out on the nanocrystals at different strontium content provided new insight into its interaction with the structure of hydroxyapatite. At variance with the behaviour of Sr towards HA, it was found that this ion inhibits the synthesis of octacalcium phosphate. However, it can substitute for calcium in this structure up to 15 atom %, in agreement with the increase of the cell parameters observed on increasing ion concentration. A similar behaviour was found for Magnesium ion, whereas Manganese inhibits the synthesis of octacalcium phosphate and it promotes the precipitation of dicalcium phosphate dehydrate. It was also found that Strontium affects the kinetics of the reaction of hydrolysis of α-TCP. It inhibits the conversion from α-TCP to hydroxyapatite. However, the resulting apatitic phase contains significant amounts of Sr2+ suggesting that the addition of Sr2+ to the composition of α-TCP bone cements could be successfully exploited for its local delivery in bone defects. The hydrolysis of α-TCP has been investigated also in the presence of increasing amounts of gelatin: the results indicated that this biopolymer accelerates the hydrolysis reaction and promotes the conversion of α-TCP into OCP, suggesting that its addition in the composition of calcium phosphate cements can be employed to modulate the OCP/HA ratio, and as a consequence the solubility, of the set cement. II. Deposition of modified calcium phosphates on metallic substrates. Coating with a thin film of calcium phosphates is frequently applied on the surface of metallic implants in order to combine the high mechanical strength of the metal with the excellent bioactivity of the calcium phosphates surface layers. During this PhD thesis, thank to the collaboration with prof. I.N. Mihailescu, head of the Laser-Surface-Plasma Interactions Laboratory (National Institute for Lasers, Plasma and Radiation Physics – Laser Department, Bucharest) Pulsed Laser Deposition has been successfully applied to deposit thin films of Sr substituted HA on Titanium substrates. The synthesized coatings displayed a uniform Sr distribution, a granular surface and a good degree of crystallinity which slightly decreased on increasing Sr content. The results of in vitro tests carried out on osteoblast-like and osteoclast cells suggested that the presence of Sr in HA thin films can enhance the positive effect of HA coatings on osteointegration and bone regeneration, and prevent undesirable bone resorption. The possibility to introduce an active molecule in the implant site was explored using Matrix Assisted Pulsed Laser Evaporation to deposit hydroxyapatite nanocrystals at different content of alendronate, a bisphosphonate widely employed in the treatments of pathological diseases associated to bone loss. The coatings displayed a good degree of crystallinity, and the results of in vitro tests indicated that alendronate promotes proliferation and differentiation of osteoblasts even when incorporated into hydroxyapatite. III. Synthesis of drug carriers with a delayed release modulated by a calcium phosphate coating. A core-shell system for modulated drug delivery and release has been developed through optimization of the experimental conditions to cover gelatin microspheres with a uniform layer of calcium phosphate. The kinetics of the release from uncoated and coated microspheres was investigated using aspirin as a model drug. It was shown that the presence of the calcium phosphate shell delays the release of aspirin and allows to modulate its action.

Development of newly conceived biomimetic nano-structured biomaterials as scaffolds for bone and osteochondral regeneration

The present research thesis was focused on the development of new biomaterials and devices for application in regenerative medicine, particularly in the repair/regeneration of bone and osteochondral regions affected by degenerative diseases such as Osteoarthritis and Osteoporosis or serious traumas. More specifically, the work was focused on the synthesis and physico-chemical-morphological characterization of: i) a new superparamagnetic apatite phase; ii) new biomimetic superparamagnetic bone and osteochondral scaffolds; iii) new bioactive bone cements for regenerative vertebroplasty. The new bio-devices were designed to exhibit high biomimicry with hard human tissues and with functionality promoting faster tissue repair and improved texturing. In particular, recent trends in tissue regeneration indicate magnetism as a new tool to stimulate cells towards tissue formation and organization; in this perspective a new superparamagnetic apatite was synthesized by doping apatite lattice with di-and trivalent iron ions during synthesis. This finding was the pin to synthesize newly conceived superparamagnetic bone and osteochondral scaffolds by reproducing in laboratory the biological processes yielding the formation of new bone, i.e. the self-assembly/organization of collagen fibrils and heterogeneous nucleation of nanosized, ionically substituted apatite mimicking the mineral part of bone. The new scaffolds can be magnetically switched on/off and function as workstations guiding fast tissue regeneration by minimally invasive and more efficient approaches. Moreover, in the view of specific treatments for patients affected by osteoporosis or traumas involving vertebrae weakening or fracture, the present work was also dedicated to the development of new self-setting injectable pastes based on strontium-substituted calcium phosphates, able to harden in vivo and transform into strontium-substituted hydroxyapatite. The addition of strontium may provide an anti-osteoporotic effect, aiding to restore the physiologic bone turnover. The ceramic-based paste was also added with bio-polymers, able to be progressively resorbed thus creating additional porosity in the cement body that favour cell colonization and osseointegration.

Electrospun Polymeric Scaffolds with Enhanced Biomimetic Properties for Tissue Engineering Applications

This PhD Thesis is focused on the development of fibrous polymeric scaffolds for tissue engineering applications and on the improvement of scaffold biomimetic properties. Scaffolds were fabricated by electrospinning, which allows to obtain scaffolds made of polymeric micro or nanofibers. Biomimetism was enhanced by following two approaches: (1) the use of natural biopolymers, and (2) the modification of the fibers surface chemistry. Gelatin was chosen for its bioactive properties and cellular affinity, however it lacks in mechanical properties. This problem was overcome by adding poly(lactic acid) to the scaffold through co-electrospinning and mechanical properties of the composite constructs were assessed. Gelatin effectively improves cell growth and viability and worth noting, composite scaffolds of gelatin and poly(lactic acid) were more effective than a plain gelatin scaffold. Scaffolds made of pure collagen fibers were fabricated. Modification of collagen triple helix structure in electrospun collagen fibers was studied. Mechanical properties were evaluated before and after crosslinking. The crosslinking procedure was developed and optimized by using - for the first time on electrospun collagen fibers - the crosslinking reactant 1,4-butanediol diglycidyl ether, with good results in terms of fibers stabilization. Cell culture experiments showed good results in term of cell adhesion and morphology. The fiber surface chemistry of electrospun poly(lactic acid) scaffold was modified by plasma treatment. Plasma did not affect thermal and mechanical properties of the scaffold, while it greatly increased its hydrophilicity by the introduction of carboxyl groups at the fiber surface. This fiber functionalization enhanced the fibroblast cell viability and spreading. Surface modifications by chemical reactions were conducted on electrospun scaffolds made of a polysophorolipid. The aim was to introduce a biomolecule at the fiber surface. By developing a series of chemical reactions, one oligopeptide every three repeating units of polysophorolipid was grafted at the surface of electrospun fibers.

Biomimetic Scaffolds for the Controlled Release of Bioactive Molecules for Tissue Engineering Applications

The temporospatial controlled delivery of growth factors is crucial to trigger the desired healing mechanisms in target tissues. The uncontrolled release of growth factors has been demonstrated to cause severe side effects in its surrounding tissues. Thus, the first working hypothesis was to tune and optimize a newly developed multiscale delivery platform based on a nanostructured silicon particle core (pSi) and a poly (dl-lactide-co-glycolide) acid (PLGA) outer shell. In a murine subcutaneous model, the platform was demonstrated to be fully tunable for the temporal and spatial control release of the payload. Secondly, a multiscale approach was followed in a multicompartment collagen scaffold, to selectively integrate different sets of PLGA-pSi loaded with different reporter proteins. The spatial confinement of the microspheres allowed the release of the reporter proteins in each of the layers of the scaffold. Finally, the staged and zero-order release kinetics enabled the temporal biochemical patterning of the scaffold. The last step of this PhD project was to test if by fully embedding PLGA microspheres in a highly structured and fibrous collagen-based scaffold (camouflaging), it was possible to prevent their early detection and clearance by macrophages. It was further studied whether such a camouflaging strategy was efficient in reducing the production of key inflammatory molecules, while preserving the release kinetics of the payload of the PLGA microspheres. Results demonstrated that the camouflaging allowed for a 10-fold decrease in the number of PLGA microspheres internalized by macrophages, suggesting that the 3D scaffold operated by cloaking the PLGA microspheres. When the production of key inflammatory cytokines induced by the scaffold was assessed, macrophages' response to the PLGA microspheres-integrated scaffolds resulted in a response similar to that observed in the control (not functionalized scaffold) and the release kinetic of a reporter protein was preserved.

To Evaluate the Synergistic Effect of Different Crosslinking Strategies on Collagen Derivatives to Develop Funcional Biomimetic Scaffolds

The preliminary objective of this work was to study how the effect of different crosslinking methodologies can functionally modify various characteristics of biological macromolecules relevant for scaffold development in bone tissue engineering. The research study was classified and studied in three different phases: (i) different crosslinking strategies in gelatin functionalization, (ii) ribose mediated crosslinking in collagen-hydroxyapatite scaffold (iii) different crosslinking mechanisms in functional modification of bone-like scaffold. The obtained results were highly positive in all the three investigated studies. Though the core aim of this research was to explore the available crosslinking strategies in different biological macromolecules, the present study generated significant findings, largely contributing to provide optimum solutions in understanding how the crosslinking density can fine-tune the overall performance of a scaffold, relevant for its functioning in vivo. In particular, this study demonstrated that different crosslinkers at different conditions (pH and temperature) can modify the functional properties of the scaffolds differently, therefore this optimization strategies on these crosslinkers as obtained from this study results will help material scientists in the design and development of bioactive hybrid biomaterials for hard tissue regeneration.

Biomimetic surfaces for greener coastal infrastructures: an analysis of factors that contribute to make artificial structures more “natural”

The growing ecological awareness of Ocean Sprawl impacts is promoting the adoption of eco-engineering strategies to enhance the ecological performance of coastal infrastructures. Biomimicry, as an eco-engineering tool, aims to design infrastructure more suitable for wildlife by manipulating structural factors to mimic natural habitats. However, little is known about the extent to which natural and artificial substrates differ in their structure and to what extent such differences affect the biota. To fill these knowledge gaps and consequently design biomimetic surfaces, I initially explored how much physical structure diverges between various types of natural and artificial substrates and tested to what extent differences in physical structure and material composition affect the epibenthic communities. By mean of an in-field mensurative experiment and a systematic review coupled with a meta-analysis, I found that, although communities tended to differ between natural and artificial coastal habitats, both physical structure and material composition reported an overall mild effect on epibenthic communities. However, an informed choice of building material and an appropriate combination of multiple structural manipulations can promote ecological benefits at multiple levels, from increasing the ecological performance in situ to reducing the impacts during the production process. Thus, I combined my findings in a final experiment, still in progress, where I am testing the combined role of shape, brightness and inclination of biomimetic surfaces I have designed in producing benefits at multiple levels. Overall, I suggest that biomimicry has the potential to increase the ecological value of artificial habitats especially when a wide range of aspects is simultaneously considered. Indeed, none of the structural factors, individually, can fully mimic the “natural conditions” to effectively improve the ecological performance of the artificial substrates. This emphasizes the need to include in future works a multi-level perspective to fully achieve the great potential of biomimicry.

A 3D biomimetic in vitro model: a novel strategy to investigate glioma biology

Gliomas are one of the most frequent primary malignant brain tumors. Acquisition of stem-like features likely contributes to the malignant nature of high-grade gliomas and may be responsible for the initiation, growth, and recurrence of these tumors. In this regard, although the traditional 2D cell culture system has been widely used in cancer research, it shows limitations in maintaining the stemness properties of cancer and in mimicking the in vivo microenvironment. In order to overcome these limitations, different three-dimensional (3D) culture systems have been developed to mimic better the tumor microenvironment. Cancer cells cultured in 3D structures may represent a more reliable in vitro model due to increased cell-cell and cell-extracellular matrix (ECM) interaction. Several attempts to recreate brain cancer tissue in vitro are described in literature. However, to date, it is still unclear which main characteristics the ideal model should reproduce. The overall goal of this project was the development of a 3D in vitro model able to reproduce the brain ECM microenvironment and to recapitulate pathological condition for the study of tumor stroma interactions, tumor invasion ability, and molecular phenotype of glioma cells. We performed an in silico bioinformatic analysis using GEPIA2 Software to compare the expression level of seven matrix protein in the LGG tumors with healthy tissues. Then, we carried out a FFPE retrospective study in order to evaluate the percentage of expression of selected proteins. Thus, we developed a 3D scaffold composed by Hyaluronic Acid and Collagen IV in a ratio of 50:50. We used two astrocytoma cell lines, HTB-12 and HTB-13. In conclusion, we developed an in vitro 3D model able to reproduce the composition of brain tumor ECM, demonstrating that it is a feasible platform to investigate the interaction between tumor cells and the matrix.

Studio di biomateriali usati come scaffold per Tissue Engineering e loro caratterizzazione con tecniche spettroscopiche vibrazionali e di analisi termica

This research investigated someone of the main problems connected to the application of Tissue Engineering in the prosthetic field, in particular about the characterization of the scaffolding materials and biomimetic strategies adopted in order to promote the implant integration. The spectroscopic and thermal analysis techniques were usefully applied to characterize the chemico-physical properties of the materials such as – crystallinity; – relative composition in case of composite materials; – Structure and conformation of polymeric and peptidic chains; – mechanism and degradation rate; – Intramolecular and intermolecular interactions (hydrogen bonds, aliphatic interactions). This kind of information are of great importance in the comprehension of the interactions that scaffold undergoes when it is in contact with biological tissues; this information are fundamental to predict biodegradation mechanisms and to understand how chemico-physical properties change during the degradation process. In order to fully characterize biomaterials, this findings must be integrated by information relative to mechanical aspects and in vitro and in vivo behavior thanks to collaborations with biomedical engineers and biologists. This study was focussed on three different systems that correspond to three different strategies adopted in Tissue Engineering: biomimetic replica of fibrous 3-D structure of extracellular matrix (PCL-PLLA), incorporation of an apatitic phase similar to bone inorganic phase to promote biomineralization (PCL-HA), surface modification with synthetic oligopeptides that elicit the interaction with osteoblasts. The characterization of the PCL-PLLA composite underlined that the degradation started along PLLA fibres, which are more hydrophylic, and they serve as a guide for tissue regeneration. Moreover it was found that some cellular lines are more active in the colonization of the scaffold. In the PCL-HA composite, the weight ratio between the polymeric and the inorganic phase plays an essential role both in the degradation process and in the biomineralization of the material. The study of self-assembling peptides allowed to clarify the influence of primary structure on intermolecular and intermolecular interactions, that lead to the formation of the secondary structure and it was possible to find a new class of oligopeptides useful to functionalize materials surface. Among the analytical techniques used in this study, Raman vibrational spectroscopy played a major role, being non-destructive and non-invasive, two properties that make it suitable to degradation studies and to morphological characterization. Also micro-IR spectroscopy was useful in the comprehension of peptide structure on oxidized titanium: up to date this study was one of the first to employ this relatively new technique in the biomedical field.

Biomimetica per l'ingegneria tissutale dell'osso

Reconstruction of bone is needed for high bone loss due to congenital deformities, trauma or neoplastic diseases. Commonly, orthopaedic surgical treatments are autologus or allogenic bone implant or prosthetic implant. A choice to the traditional approaches could be represented by tissue engineering that use cells (and/or their products) and innovative biomaterials to perform bone substitutes biologically active as an alternative to artificial devices. In the last years, there was a wide improvement in biology on stem cells potential research and in biomedical engineering through development of new biomaterials designed to resemble the physiological tissues. Tissue engineering strategies and smart materials aim together to stimulate in vivo bone regeneration. This approaches drive at restore not only structure integrity and/or function of the original tissue, but also to induce new tissue deposition in situ. An intelligent bone substitute is now designed like not only a scaffold but also as carrier of regeneration biomolecular signals. Biomimetics has helped to project new tissue engineered devices to simulate the physiological substrates architecture, such extracellular matrix (ECM), and molecular signals that drive the integration at the interface between pre-existing tissue and scaffold. Biomimetic strategies want to increase the material surface biological activity with physical modifications (topography) o chemical ones (adhesive peptides), to improve cell adhesion to material surface and possibly scaffold colonization. This study evaluated the effects of biomimetic modifications of surgical materials surface, as poly-caprolattone (PCL) and titanium on bone stem cells behaviour in a marrow experimental model in vitro. Two biomimetic strategies were analyzed; ione beam irradiation, that changes the surface roughness at the nanoscale, and surface functionalization with specific adhesive peptides or Self Assembled Monolayers (SAMs). These new concept could be a mean to improve the early (cell adhesion, spreading..) and late phases (osteoblast differentiation) of cell/substrate interactions.

Analysis of ion channel stochastic signals for biosensing

In biological world, life of cells is guaranteed by their ability to sense and to respond to a large variety of internal and external stimuli. In particular, excitable cells, like muscle or nerve cells, produce quick depolarizations in response to electrical, mechanical or chemical stimuli: this means that they can change their internal potential through a quick exchange of ions between cytoplasm and the external environment. This can be done thanks to the presence of ion channels, proteins that span the lipid bilayer and act like switches, allowing ionic current to flow opening and shutting in a stochastic way. For a particular class of ion channels, ligand-gated ion channels, the gating processes is strongly influenced by binding between receptive sites located on the channel surface and specific target molecules. These channels, inserted in biomimetic membranes and in presence of a proper electronic system for acquiring and elaborating the electrical signal, could give us the possibility of detecting and quantifying concentrations of specific molecules in complex mixtures from ionic currents across the membrane; in this thesis work, this possibility is investigated. In particular, it reports a description of experiments focused on the creation and the characterization of artificial lipid membranes, the reconstitution of ion channels and the analysis of their electrical and statistical properties. Moreover, after a chapter about the basis of the modelling of the kinetic behaviour of ligand gated ion channels, a possible approach for the estimation of the target molecule concentration, based on a statistical analysis of the ion channel open probability, is proposed. The fifth chapter contains a description of the kinetic characterisation of a ligand gated ion channel: the homomeric α2 isoform of the glycine receptor. It involved both experimental acquisitions and signal analysis. The last chapter represents the conclusions of this thesis, with some remark on the effective performance that may be achieved using ligand gated ion channels as sensing elements.

Utilizzo di dispositivi magnetici nel trattamento della patologia artrosica del ginocchio

The use of scaffolds for Tissue Engineering (TE) is increasing due to their efficacy in helping the body rebuild damaged or diseased tissue. Hydroxyapatite (HA) is the most suitable bioactive ceramic to be used in orthopaedic reconstruction since it replicates the mineral component of the hard tissues, and it has therefore excellent biocompatibility properties. The temporal and spatial control of the tissue regeneration process is the limit to be overcome in order to treat large bone and osteochondral defects. In this thesis we describe the realization of a magnetic scaffolds able to attract and take up growth factors or other bio-agents in vivo via a driving magnetic force. This concept involves the use of magnetic nanoparticles (MNP) functionalized with selected growth factors or stem cells. These functionalized MNP act as shuttles transporting the bio-agents towards and inside the scaffold under the effect of the magnetic field, enhancing the control of tissue regeneration processes. This scaffold can be imagined as a fixed “station” that provides a unique possibility to adjust the scaffold activity to the specific needs of the healing tissue. Synthetic bone graft substitutes, made of collagen or biomineralized collagen (i.e. biomimetic Hydroxyapatite/collagen composites) were used as starting materials for the fabrication of magnetic scaffolds. These materials are routinely used clinically to replace damaged or diseased cartilaginous or bone tissue. Our magnetization technique is based on a dip-coating process consisting in the infilling of biologically inspired porous scaffolds with aqueous biocompatible ferrofluids’ suspensions. In this technique, the specific interconnected porosity of the scaffolds allows the ferrofluids to be drawn inside the structure by capillarity. A subsequent freeze-drying process allows the solvent elimination while keeping very nearly the original shape and porosity of the scaffolds. The remaining magnetic nanoparticles, which are trapped in the structure, lead to the magnetization of the HA/Collagen scaffold. We demonstrate here the possibility to magnetize commercially available scaffolds up to magnetization values that are used in drug delivery processes. The preliminary biocompatibility test showed that the investigated scaffolds provide a suitable micro-environment for cells. The biocompatibility of scaffold facilitates the growth and proliferation of osteogenic cells.

Synthesis and Physical-Chemical characterization of Metallic Nanoparticles

The stabilization of nanoparticles against their irreversible particle aggregation and oxidation reactions. is a requirement for further advancement in nanoparticle science and technology. For this reason the research aim on this topic focuses on the synthesis of various metal nanoparticles protected with monolayers containing different reactive head groups and functional tail groups. In this work cuprous bromide nanocrystals haave been synthetized with a diameter of about 20 nanometers according to a new sybthetic method adding dropwise ascorbic acid to a water solution of lithium bromide and cupric chloride under continuous stirring and nitrogen flux. Butane thiolate Cu protected nanoparticles have been synthetized according to three different syntesys methods. Their morphologies appear related to the physicochemical conditions during the synthesis and to the dispersing medium used to prepare the sample. Synthesis method II allows to obtain stable nanoparticles of 1-2 nm in size both isolated and forming clusters. Nanoparticle cluster formation was enhanced as water was used as dispersing medium probably due to the idrophobic nature of the butanethiolate layers coating the nanoparticle surface. Synthesis methods I and III lead to large unstable spherical nanoparticles with size ranging between 20 to 50 nm. These nanoparticles appeared in the TEM micrograph with the same morphology independently on the dispersing medium used in the sample preparation. The stability and dimensions of the copper nanoparticles appear inversely related. Using the same methods above described for the butanethiolate protected copper nanoparticles 4-methylbenzenethiol protected copper nanoparticles have been prepared. Diffractometric and spectroscopic data reveal that decomposition processes didn’t occur in both the 4-methylbenzenethiol copper protected nanoparticles precipitates from formic acid and from water in a period of time six month long. Se anticarcinogenic effects by multiple mechanisms have been extensively investigated and documented and Se is defined a genuine nutritional cancer-protecting element and a significant protective effect of Se against major forms of cancer. Furthermore phloroglucinol was found to possess cytoprotective effects against oxidative stress, thanks to reactive oxygen species (ROS) which are associated with cells and tissue damages and are the contributing factors for inflammation, aging, cancer, arteriosclerosis, hypertension and diabetes. The goal of our work has been to set up a new method to synthesize in mild conditions amorphous Se nanopaticles surface capped with phloroglucinol, which is used during synthesis as reducing agent to obtain stable Se nanoparticles in ethanol, performing the synergies offered by the specific anticarcinogenic properties of Se and the antioxiding ones of phloroalucinol. We have synthesized selenium nanoparticles protected by phenolic molecules chemically bonded to their surface. The phenol molecules coating the nanoparticles surfaces form low ordered arrays as can be seen from the wider shape of the absorptions in the FT-IR spectrum with respect to those appearing in that of crystalline phenol. On the other hand, metallic nanoparticles with unique optical properties, facile surface chemistry and appropriate size scale are generating much enthusiasm in nanomedicine. In fact Au nanoparticles has immense potential for both cancer diagnosis and therapy. Especially Au nanoparticles efficiently convert the strongly adsorbed light into localized heat, which can be exploited for the selective laser photothermal therapy of cancer. According to the about, metal nanoparticles-HA nanocrystals composites should have tremendous potential in novel methods for therapy of cancer. 11 mercaptoundecanoic surface protected Au4Ag1 nanoparticles adsorbed on nanometric apathyte crystals we have successfully prepared like an anticancer nanoparticles deliver system utilizing biomimetic hydroxyapatyte nanocrystals as deliver agents. Furthermore natural chrysotile, formed by densely packed bundles of multiwalled hollow nanotubes, is a mineral very suitable for nanowires preparation when their inner nanometer-sized cavity is filled with a proper material. Bundles of chrysotile nanotubes can then behave as host systems, where their large interchannel separation is actually expected to prevent the interaction between individual guest metallic nanoparticles and act as a confining barrier. Chrysotile nanotubes have been filled with molten metals such as Hg, Pb, Sn, semimetals, Bi, Te, Se, and with semiconductor materials such as InSb, CdSe, GaAs, and InP using both high-pressure techniques and metal-organic chemical vapor deposition. Under hydrothermal conditions chrysotile nanocrystals have been synthesized as a single phase and can be utilized as a very suitable for nanowires preparation filling their inner nanometer-sized cavity with metallic nanoparticles. In this research work we have synthesized and characterized Stoichiometric synthetic chrysotile nanotubes have been partially filled with bi and monometallic highly monodispersed nanoparticles with diameters ranging from 1,7 to 5,5 nm depending on the core composition (Au, Au4Ag1, Au1Ag4, Ag). In the case of 4 methylbenzenethiol protected silver nanoparticles, the filling was carried out by convection and capillarity effect at room temperature and pressure using a suitable organic solvent. We have obtained new interesting nanowires constituted of metallic nanoparticles filled in inorganic nanotubes with a inner cavity of 7 nm and an isolating wall with a thick ranging from 7 to 21 nm.

Sviluppo dei materiali innovativi e studio della loro interazione con sistemi biologici e biomimetici

Nell’ambito della Chimica Sostenibile e dell’applicazione dei suoi principi per la salvaguardia dell’ambiente, il progetto di dottorato ha riguardato lo sviluppo di materiali innovativi e lo studio della loro interazione con sistemi biologici e biomimetici. In particolare l’attività si è focalizzata sulla sintesi di liquidi ionici ed indagini delle interazioni con membrane cellulari e sull’utilizzo ed isolamento di molecole da fonti rinnovabili. I liquidi ionici sono sali organici liquidi a temperature inferiori ai 100 °C; sono considerati promettenti solventi a ridotta tossicità, ma vanno chiarite a pieno le modalità di interazione con i sistemi biologici ed i meccanismi di tossicità. A questo scopo è stata impiegata una batteria di test bio-chimici, con saggi di fluorescenza e colorimetrici, che hanno permesso di discriminare le diverse tipologie di interazioni con varie strutture di membrana. Le informazioni raccolte sono servite per progettare sostanze meno dannose per le strutture cellulari, al fine di scegliere le funzionalità molecolari che consentano ai liquidi ionici di mantenere la loro attività ma di essere meno dannosi per l’ambiente. Per quanto riguarda l’utilizzo ed isolamento di molecole da fonte rinnovabili, si è utilizzata la tecnica della pirolisi per l’ottenimento di starting materials ed il loro impiego nella sintesi di chemicals in alternativa a composti derivanti da fonti fossili. La pirolisi tradizionale della cellulosa fornisce una molecola interessante, per semplicità denominata LAC, in quantità insufficienti ad un uso applicativo. Nell’ambito delle ricerche svolte è stato scoperto che la pirolisi condotta in presenza di catalizzatori meso-strutturati (MCM-41) drogati con metalli di transizione, fornisce buone quantità di LAC. LAC si è dimostrato promettente sia per la produzione di nuove molecole con possibili applicazioni nella chimica fine e farmaceutica, che come monomero per nuovi polimeri (copolimero ed omopolimero).

Nuovo scaffold biomimetico per il trattamento delle lesioni osteocondrali: studio clinico pilota

Nel corso degli anni diverse sono le tecniche proposte per il trattamento delle lesioni osteocondrali, da quelle mini-invasive con stimolazione midollare fino a quelle più aggressive basate sul trapianto di tessuti autologhi o eterologhi. Tutti questi metodi hanno comunque dei difetti ed è questo il motivo per cui il trattamento delle lesioni osteocondrali rappresenta tuttora una sfida per il chirurgo ortopedico, in considerazione dell’alta specializzazione e del basso potere di guarigione del tessuto cartilagineo. Buoni risultati sono stati ottenuti con innesti bioingegnerizzati o matrici polimeriche impiantati nei siti danneggiati. La quantità di scaffolds in uso per la riparazione condrale ed osteocondrale è molto ampia; essi differiscono non solo per il tipo di materiali usati per la loro realizzazione, ma anche per la presenza di promotori di una o più linee cellulari , su base condrogenica o osteogenica. Quando ci si approccia ad una lesione condrale di grandi dimensioni, l’osso sub-condrale è anch’esso coinvolto e necessita di trattamento per ottenere il corretto ripristino degli strati articolari più superficiali. La scelta più giusta sembra essere un innesto osteocondrale bioingegnerizzato, pronto per l’uso ed immediatamente disponibile, che consenta di effettuare il trattamento in un unico tempo chirurgico. Sulla base di questo razionale, dopo uno studio preclinico animale e previa autorizzazione del comitato etico locale, abbiamo condotto uno studio clinico clinico pilota utilizzando un nuovo innesto biomimetico nanostrutturato per il trattamento di lesioni condrali ed osteocondrali del ginocchio; la sua sicurezza e maneggevolezza, così come la facile riproducibilità della tecnica chirurgica ed i risultati clinici ottenuti sono stati valutati nel tempo a 6, 12, 24, 36 e 48 mesi dall’impianto in modo da testare il suo potenziale intrinseco senza l’aggiunta di alcuna linea cellulare.