Analisi morfologica e molecolare di cellule da colture primarie umane esposte a resine biocompatibili

The cytotoxicity of dental composites has been attributed to the release of residual monomers from polymerized adhesive systems due to degradation processes or the incomplete polymerization of materials. 2-Hydroxyethyl methacrylate (HEMA) is one of the major components released from dental adhesives. Cytotoxic effects due to high concentrations of HEMA have already been investigated, but the influence of minor toxic concentrations for long-term exposition on specific proteins such as type I collagen and tenascin has not been studied in depth. The objective of this project was to study the effect of minor toxic concentrations of HEMA on human gingival fibroblasts (HGFs) and human pulp fibroblasts (HPFs), investigating modification in cell morphology, cell viability, and the influence on type I collagen and tenascin proteins. Different concentrations of the resin monomer and different times of exposition were tested on both cell lines. The cell vitality was determined by MTT assay, and high-resolution scanning electron microscopy analysis was performed to evaluate differences in cell morphology before and after treatment. To evaluate the variability in the expression and synthesis of procollagen α1 type I and tenascin proteins on HGFs and HPFs treated with HEMA at different concentrations immunofluorescence, RT-PCR and western blot analysis, were carried out. The treatments on HGFs with 3mmol/L HEMA, showed a strong reduction of procollagen α1 type I protein at 72h and 96h, demonstrating that HEMA interferes both with the synthesis of the procollagen α1 type I protein and its mRNA expression. The results obtained on HPFs treated with different concentrations of HEMA ranging from 0,5mmol/L to 3mmol/L and for different exposition times showed a strong reduction in cell viability in specimens treated for 96h and 168h, while immunofluorescence and western blotting analysis demonstrated a reduction of procollagen α1 type I and an overexpression of tenascin protein. In conclusion, our results showed that the concentrations of HEMA we tested, effect the normal cell production and activity, such as the synthesis of some dental extracellular matrix proteins.

Sistemi adesivi con applicazioni in campo biomedicale

Polymeric adhesives have been used for many applications like suture and embolization, instead of classic surgical methods or as for dental uses. In this work both subjects have been investigated and the results separated in two parts. In the first, new dentinal adhesives with different polymerizable groups (methacrylic or vinyl-ethereal) were synthesized. A low sensitivity to hydrolysis and equal or enhanced properties, compared to existing commercial products, were considered essentials. Moreover, these monomers need to polymerize by radical photopolymerization and functional groups of different characteristics were tested. All these products were characterized by microtensile bond strength test to determine the bonding strength between the adhesive and tooth. Concerning embolization, cyanoacrylates are nowadays the most-used adhesives in surgery. Thus, they must respond to several requirements. For instance, polymerization time and adhesive strength need to be low, to avoid diffusion of the products in the body and adhesion to the catheter. In order to overcome these problems we developed new cyanoacrylates, which practically instantly polymerize upon contact with blood but do not demonstrate strong adhesion to the catheter, thank to the presence of fluorine atoms, linked to the ester chain. The synthesis of these products was carried out in several steps, such as the depolymerization of the corresponding oligomers at high temperature in acid conditions. Two types of adhesion strengths were determined. Bonding strength between human veins and a microcatheter was determined in vitro by using organic materials as the most realistic model. Another test, on two layers of skin, was conducted to verify the possible use of these new cyanoacrylates as a glue for sutures. As a conclusion, we were able to demonstrate that some of the prepared monomers posses adhesive strength and polymerization time lower than the commercial product Glubran2.

Effetti della viscoelasticità sulla misura dell’energia di adesione tra film di polietilene

Lo stretch film è una diffusa applicazione per imballaggio dei film in polietilene (PE), utilizzato per proteggere diversi prodotti di vari dimensioni e pesi. Una caratteristica fondamentale del film è la sua proprietà adesiva in virtù della quale il film può essere facilmente chiuso su se stesso. Tipicamente vengono scelti gradi lineari a bassa densità (LLDPE) con valori relativamente bassi di densità a causa delle loro buone prestazioni. Il mercato basa la scelta del materiale adesivo per tentativi piuttosto che in base alla conoscenza delle caratteristiche strutturali ottimali per l’applicazione. Come per i pressure sensitive adhesives, le proprietà adesive di film stretch in PE possono essere misurati mediante "peel testing". Esistono molti metodi standard internazionali ma i risultati di tali prove sono fortemente dipendenti dalla geometria di prova, sulla possibile deformazione plastica che si verificano nel peel arm(s), e la velocità e temperatura. Lo scopo del presente lavoro è quello di misurare l'energia di adesione Gc di film stretch di PE, su se stessi e su substrati diversi, sfruttando l'interpretazione della meccanica della frattura per tener conto dell'elevata flessibilità e deformabilità di tali film. Quindi, la dipendenza velocità/temperatura di Gc sarà studiata con riferimento diretto al comportamento viscoelastico lineare dei materiali utilizzati negli strati adesivi, per esplorare le relazioni struttura-proprietà che possono mettere in luce i meccanismi molecolari coinvolti nei processi di adesione e distacco. Nella presente caso, l’adesivo non è direttamente disponibile come materiale separato che può essere messo tra due superfici di prova e misurato per la determinazione delle sue proprietà. Il presupposto principale è che una parte, o fase, della complessa struttura semi-cristallina del PE possa funzionare come adesivo, e un importante risultato di questo studio può essere una migliore identificazione e caratterizzazione di questo "fase adesiva".