Speciation and fractionation of Ca and the REE in fresh and marine waters

This study is concerned with speciation and fractionation of the rare earth elements (REE) and calcium (Ca) in aqueous solutions. The aim is to investigate the chemical states and physical sizes in which these elements can be present. The REE (including neodymium) and Ca have contrasting geochemical behavior in aqueous solutions. Ca is a major dissolved element, while the REE are trace components and highly reactive with aquatic particles. The major interests of the five papers included in this thesis are the following: · Papers I and V deal with the behavior of neodymium (Nd) and its isotopes in the Kalix River and some marine waters. · The diffusive gradients in thin-films (DGT) method is developed for measuring Ca and Mg in Paper II. · Paper III presents a speciation and fractionation study of Ca in the Kalix and Amazonian rivers. · The rare earth elements and their carrier phases are investigated in the Kalix river in Paper IV. For most elements a detailed study of speciation and fractionation can not be performed using only one method. This is due to the overall heterogeneity of the material, considering both size and chemical composition, which is present in aquatic solutions. During this project the aquatic geochemistry of the REE and Ca has been studied using mainly three methods; cross-flow filtration (CFF), field-flow fractionation (FFF) and diffusive gradients in thin-films (DGT). Field work has to a large part been conducted in the Kalix River, in northern Sweden, which is one of the last pristine river systems in Europe. Some field work has also been conducted in the Baltic Sea and the Arctic Ocean. Results from Amazonian rivers are also presented. These are the main conclusions from this work: The DGT technique works equally well for measuring Ca and Mg in natural waters as previously reported for trace metal. A significant colloidal phase for Ca could be detected in the Kalix River and in different Amazonian rivers. This was concluded independently using both CFF and FFF. Variations in REE signatures in the Kalix River suggests two different pathways for the REE during weathering and release form soil profiles and transport in the river. No significant variation in Nd-isotopic composition could be detected in the Kalix River although concentrations varied by a factor of ~10. This suggests that there is one major source for Nd in the river although different pathways for the REE may exist. A study of Nd in the Kalix River, the Baltic Sea and the Arctic Ocean showed that the isotopic compositions in the diffusible fractions were similar to water samples. However, the relative amount of diffusible Nd increased with salinity, probably reflecting the lower concentration of colloidal and particulate material in marine waters.

Preparation and characterisation of refractory whiskers and selected alumina composites

A whisker is a common name of single crystalline inorganic fibre of small dimensions, typically 0.5-1 μm in diameter and 20-50 μm in length. Whiskers are mainly used as reinforcement of ceramics. This work describes the synthesis and characterisation of new whisker types. Ti0.33Ta0.33Nb0.33CxN1-x, TiB2, B4C, and LaxCe1-xB6 have been prepared by carbothermal vapour–liquid–solid (CTR-VLS) growth mechanisms in the temperature range 900-1800°C, in argon or nitrogen. Generally, carbon and different suitable oxides were used as whisker precursors. The oxides reacted via a carbothermal reduction process. A halogenide salt was added to form gaseous metal halogenides or oxohalogenides and small amount of a transition metal was added to catalyse the whisker growth. In this mechanism, the whisker constituents are dissolved into the catalyst, in liquid phase, which becomes supersaturated. Then a whisker could nucleate and grow out under continuous feed of constituents. The syntheses of TiC, TiB2, and B4C were followed at ordinary synthesis conditions by means of mass spectrometry (MS), thermogravimetry (TG), differential thermal analysis (DTA) and quenching. The main reaction starting temperatures and reaction time for the different mixtures was revealed, and it was found that the temperature inside the crucible during the reactions was up to 100°C below the furnace set-point, due to endothermic nature of the reactions. Quench experiments showed that whiskers were formed already when reaching the temperature plateau, but the yield increased fast with the holding time and reached a maximum after about 20-30 minutes. Growth models for whisker formation have been proposed. Alumina based composites reinforced by (2-5 vol.%) TiCnano and TiNnano and 25 vol.% of carbide, and boride phases (whiskers and particulates of TiC, TiN, TaC, NbC, (Ti,Ta)C, (Ti,Ta,Nb)C, SiC, TiB2 and B4C) have been prepared by a developed aqueous colloidal processing route followed by hot pressing for 90 min at 1700°C, 28 MPa or SPS sintering for 5 minutes at 1200-1600°C and 75 MPa. Vickers indentation measurements showed that the lowest possible sintering temperature is to prefer from mechanical properties point of view. In the TiNnano composites the fracture mode was typically intergranular, while it was transgranular in the SiCnano composites. The whisker and particulate composites have been compared in terms of e.g. microstructure and mechanical properties. Generally, additions of whiskers yielded higher fracture toughness compared to particulates. Composites of commercially available SiC whiskers showed best mechanical properties with a low spread but all the other whisker phases, especially TiB2, exhibited a great potential as reinforcement materials.

Crystallization on the Mesoscale : Self-Assembly of Iron Oxide Nanocubes into Mesocrystals

Self-assembly of nanoparticles is a promising route to form complex, nanostructured materials with functional properties. Nanoparticle assemblies characterized by a crystallographic alignment of the nanoparticles on the atomic scale, i.e. mesocrystals, are commonly found in nature with outstanding functional and mechanical properties. This thesis aims to investigate and understand the formation mechanisms of mesocrystals formed by self-assembling iron oxide nanocubes. We have used the thermal decomposition method to synthesize monodisperse, oleate-capped iron oxide nanocubes with average edge lengths between 7 nm and 12 nm and studied the evaporation-induced self-assembly in dilute toluene-based nanocube dispersions. The influence of packing constraints on the alignment of the nanocubes in nanofluidic containers has been investigated with small and wide angle X-ray scattering (SAXS and WAXS, respectively). We found that the nanocubes preferentially orient one of their {100} faces with the confining channel wall and display mesocrystalline alignment irrespective of the channel widths.  We manipulated the solvent evaporation rate of drop-cast dispersions on fluorosilane-functionalized silica substrates in a custom-designed cell. The growth stages of the assembly process were investigated using light microscopy and quartz crystal microbalance with dissipation monitoring (QCM-D). We found that particle transport phenomena, e.g. the coffee ring effect and Marangoni flow, result in complex-shaped arrays near the three-phase contact line of a drying colloidal drop when the nitrogen flow rate is high. Diffusion-driven nanoparticle assembly into large mesocrystals with a well-defined morphology dominates at much lower nitrogen flow rates. Analysis of the time-resolved video microscopy data was used to quantify the mesocrystal growth and establish a particle diffusion-based, three-dimensional growth model. The dissipation obtained from the QCM-D signal reached its maximum value when the microscopy-observed lateral growth of the mesocrystals ceased, which we address to the fluid-like behavior of the mesocrystals and their weak binding to the substrate. Analysis of electron microscopy images and diffraction patterns showed that the formed arrays display significant nanoparticle ordering, regardless of the distinctive formation process.  We followed the two-stage formation mechanism of mesocrystals in levitating colloidal drops with real-time SAXS. Modelling of the SAXS data with the square-well potential together with calculations of van der Waals interactions suggests that the nanocubes initially form disordered clusters, which quickly transform into an ordered phase.