Studies of Inorganic Layer and Framework Structures Using Time-, Temperature- and Pressure-Resolved Powder Diffraction Techniques

This thesis is concerned with in-situ time-, temperature- and pressure-resolved synchrotron X-ray powder diffraction investigations of a variety of inorganic compounds with twodimensional layer structures and three-dimensional framework structures. In particular, phase stability, reaction kinetics, thermal expansion and compressibility at non-ambient conditions has been studied for 1) Phosphates with composition MIV(HPO4)2·nH2O (MIV = Ti, Zr); 2) Pyrophosphates and pyrovanadates with composition MIVX2O7 (MIV = Ti, Zr and X = P, V); 3) Molybdates with composition ZrMo2O8. The results are compiled in seven published papers and two manuscripts. Reaction kinetics for the hydrothermal synthesis of α-Ti(HPO4)2·H2O and intercalation of alkane diamines in α-Zr(HPO4)2·H2O was studied using time-resolved experiments. In the high-temperature transformation of γ-Ti(PO4)(H2PO4)·2H2O to TiP2O7 three intermediate phases, γ'-Ti(PO4)(H2PO4)·(2-x)H2O, β-Ti(PO4)(H2PO4) and Ti(PO4)(H2P2O7)0.5 were found to crystallise at 323, 373 and 748 K, respectively. A new tetragonal three-dimensional phosphate phase called τ-Zr(HPO4)2 was prepared, and subsequently its structure was determined and refined using the Rietveld method. In the high-temperature transformation from τ-Zr(HPO4)2 to cubic α-ZrP2O7 two new orthorhombic intermediate phases were found. The first intermediate phase, ρ-Zr(HPO4)2, forms at 598 K, and the second phase, β-ZrP2O7, at 688 K. Their respective structures were solved using direct methods and refined using the Rietveld method. In-situ high-pressure studies of τ-Zr(HPO4)2 revealed two new phases, tetragonal ν-Zr(HPO4)2 and orthorhombic ω-Zr(HPO4)2 that crystallise at 1.1 and 8.2 GPa. The structure of ν-Zr(HPO4)2 was solved and refined using the Rietveld method. The high-pressure properties of the pyrophosphates ZrP2O7 and TiP2O7, and the pyrovanadate ZrV2O7 were studied up to 40 GPa. Both pyrophosphates display smooth compression up to the highest pressures, while ZrV2O7 has a phase transformation at 1.38 GPa from cubic to pseudo-tetragonal β-ZrV2O7 and becomes X-ray amorphous at pressures above 4 GPa. In-situ high-pressure studies of trigonal α-ZrMo2O8 revealed the existence of two new phases, monoclinic δ-ZrMo2O8 and triclinic ε-ZrMo2O8 that crystallises at 1.1 and 2.5 GPa, respectively. The structure of δ-ZrMo2O8 was solved by direct methods and refined using the Rietveld method.

Structural investigation of Nb-based layer sulfides

In this work we have investigated the intercalation of electron-donors between NbS2 slabs in Nb-based layer sulfides. Two series of Sr substituted Nb-based misfit sulfides belonging to the 1.5Q/1H and 1Q/1H series of misfit layer compounds have been synthesised. For large lanthanides (Ln=La, Ce), only the 1Q/1H compounds formed whereas for smaller lanthanides and yttrium, both types of phases can be obtained. The crystal structure of misfit sulfide (Pr0.55Sr0.45S)1.15NbS2 has been refined using the composite approach. In the Q-slab, Pr-atoms are partly replaced by Sr with a random distribution over one cation position. The crystal structure of misfit sulfide [(Sm1/3Sr2/3S)1.5]1.15NbS2 belonging to the 1.5Q/1H series have also been determined. The obtained results suggest a preferred occupancy of the cation positions in the slab where Sr atoms mainly occupy positions on the exterior of the slab while Sm atoms are in the center of the slab. The (La1-xSrxS)1.15NbS2 solid solution (0.1<x<0.9) has also been studied. It was found that the maximum value of Sr substitution is 40-50% and therefore, the minimal value of charge transfer to stabilize this structure type is about 0.6ē per Nb atom. An attempt to synthesize SrxNbS2 (0.1≤x≤0.5) intercalates was made but single phases were not obtained and increasing the temperature from 1000оС to 1100оС leads to the decomposition of these intercalates. Single crystals of Sr0.22Nb1.05S2 and Sr0.23NbS2 were found and their structures were determined. The structures belong to two different types of packings with statistical distribution of Sr between layers. A new superconducting sulfide, "EuNb2S5", was investigated by ED and HREM and its structure model consisting of Nb7S14 and (Eu3S4)2 slabs alternating along the c-axis is suggested. An attempt to suggest a model for the structure of "SrNb2S5" by means of X-ray single crystal diffraction was made. The proposed structure consists of two types of slabs: a Nb7S14 and a [Sr6(NbS4)2S] slab with niobium in tetrahedral coordination. It is shown that "SrNb2S5" and "EuNb2S5" are have similar structures. For the first time, single crystals of the complex sulfide BaNb0.9S3 have also been studied by means of X-ray single crystal diffraction. The single crystal refinement and EDX analysis showed the existence of cation vacancies at the niobium position. BaNb0.9S3 has also been studied by ED and no superstructure was found which implies that and the vacancies are statistically distributed. No improvement of the magnetic properties of the studied compounds was observed in comparison to NbS2.