Application of bauxite waste from amazon region in the heavy clay industry

In this work, a method was developed for the application of red mud, an alkaline leaching waste, from a bauxite processing plant located in northern Brazil (Amazon region) as starting material for heavy clay products. Samples were prepared by pressing blends of red mud and clay, which were then fired at temperatures from 900 ºC to 1190 ºC. Characterization was carried out by chemical analysis, differential thermal analysis (DTA) and X-ray diffraction (XRD), and the following ceramic properties were evaluated: water absorption, linear shrinkage and flexural strength. In order to evaluate the Na⁺ stability in the dense ceramic, leaching tests were also carried out on the specimens after sintering process. Results indicated that samples with 50 and 70 wt% of red mud are proper for being used in the production of ceramic bodies, due to its excellent properties, mainly high mechanical resistance and low water absorption, showing thus, an option to minimizing the environmental impacts caused by the aluminum industry.

Estudo do comportamento térmico e propriedades físico-mecânicas da lama vermelha

Neste trabalho, estudou-se o comportamento térmico, a evolução das fases cristalinas com a temperatura e as propriedades físico-mecânicas da Lama Vermelha (LV) procedente da indústria de alumínio do Estado do Maranhão. O estudo foi realizado por Análise Termogravimétrica (TG) e Calorimetria Exploratória Diferencial (DSC), Dilatometria Ótica até 1350 ºC; enquanto a evolução das fases cristalinas com a temperatura foi realizada no intervalo entre 750 a 1150 ºC por Difração de Raios-X (DRX). As propriedades físico-mecânicas como Superfície Específica, Granulometria, Limite Plástico (LP), Limite de Liquidez (LL), Índice de Plasticidade (IP), Tensão de Ruptura a Flexão (TRF), Absorção de Água (AA), Retração Linear Após Queima (R_L) e Porosidade Aparente (PA) foram determinadas nas mesmas temperaturas. As seguintes fases cristalinas foram detectadas: hematita, sodalita e anatásio entre 750-850 ºC; e hematita, nefelina e sodalita entre 950-1150 ºC. Os ensaios tecnológicos demonstraram que a LV pode ser aplicada para o processamento de materiais cerâmicos estruturais, pois apresenta pouca reatividade entre 870-950 ºC, com elevada AA, e baixas R_L e TRF. Entre 950 e 1350 ºC, a LV sofreu uma retração que variou entre 5-50 %, com fusão total a 1350 ºC, devido à presença de fases minerais do tipo feldespatoides em sua composição.

Ceramic raw materials from the State of Maranhão, Brazil. Part 1: chemical and mineralogical characterization and technological properties of clays from São Luis, Rosário, Pinheiro and Mirinzal

Nesse trabalho, foram caracterizadas algumas argilas coletadas nos municípios de São Luís, Rosário, Pinheiro e Mirinzal. A caracterização foi realizada através dos ensaios de difração de raios X, massa específica real, capacidade de troca de cátions (CTC), área superficial, distribuição granulométrica, análise química, análise térmica (TG-DTA) e limites de Atterberg. Ensaios tecnológicos de retração linear, antes e após a queima, absorção de água e tensão de ruptura a flexão, em três pontos, foram realizados em corpos de prova prensados uniaxialmente a 20 MPa e tratados termicamente em 850, 950, 1050, 1150 e 1250ºC. Os resultados obtidos permitiram identificar duas argilas de queima branca, constituídas de quartzo, caolim, feldspato e anatásio, com excelentes propriedades para uso em cerâmica branca. As restantes são queima vermelha e possuem composição mineralógica de quartzo, caolim, feldspato, montmorilonita, hematita e goetita. Estas últimas apresentaram valores moderados de plasticidade e são adequadas para aplicações em cerâmica vermelha.