Síntese hidrotermal de sodalita básica a partir de um rejeito de caulim termicamente ativado

Basic sodalite was successfully synthesized by hydrothermal method using kaolin waste as source of Aluminum and Silicon. This waste is mainly composed by kaolinite and is produced in large amount by kaolin processing industries for paper coating from the Amazon region. Initially, the waste has been calcined at 700 ºC for 2 h and then reacted with the following solutions: Na₂CO₃ and mixture of Na₂CO₃ + NaOH to 150 ºC with autogenous pressure for 24 h. The raw materials and transformed materials were characterized by XRD, FTIR and SEM. In both studied media, well-crystallized, basic sodalite was the only phase synthesized, while in the literature usually a mixture of zeolites is obtained.

Synthesis and characterization of zeolite NaP using kaolin waste as a source of silicon and aluminum

The synthesis of zeolite NaP using kaolin waste, from the Amazon region, as a predominant source of silicon and aluminum has been studied. The zeolitisation process occurred in hydrothermal conditions using static autoclaving and the effects of time, temperature, and the Si/Al ratio were investigated. The starting material and the phases formed as reaction products were characterized by XRD, SEM and FTIR. The results showed that pure zeolite NaP is hydrothermally synthesized, at 100 °C for 20 hours, using metakaolin waste material in alkaline medium in presence of additional silica. The XRD and SEM analyses indicate that the synthesized zeolite presents good crystallinity.

Estudo do crescimento de nanofitas de céria dopada com gadolínio por sistema de aquecimento por micro-ondas

O óxido de cério (céria) tem atraído atenção devido às suas importantes aplicações, como em células a combustível de óxido sólido, catalisadores de gases de exaustão de automóveis, catalisadores para a obtenção de hidrogênio, bloqueadores de raios ultravioleta, biomateriais, entre outros. Controlar os métodos de síntese da céria é de grande importância para explicar ou prever essas propriedades. Desta forma, o objetivo deste trabalho foi estudar o crescimento de nanofitas de óxido de cério em um sistema hidrotérmico assistido por micro-ondas, no qual 8 min foram obtidas nanofitas com comprimentos próximos a 330 nm, em 130 ºC e pressão de 3 atm. Os resultados colaboram para pesquisas em reformadores para obtenção de etanol e/ou anodos de células combustíveis de óxido sólido.