Application of carbon composite adsorbents prepared from coffee waste and clay for the removal of reactive dyes from aqueous solutions

A novel carbon composite was prepared from a mixture of coffee waste and clay with inorganic:organic ratio of 1.3 (CC-1.3). The mixture was pyrolysed at 700 °C. Considering the application of this adsorbent for removal of anionic dyes, the CC-1.3 was treated with a 6 mol L^-1 HCl for 24 h to obtain ACC-1.3. Fourier transform infrared (FTIR), N₂ adsorption/desorption curves, scanning electron microscope (SEM) and powder X-ray diffractometry (XRD) were used for characterisation of CC-1.3 and ACC-1.3 carbon adsorbents. The adsorbents were effectively utilised for removal of reactive blue 19 (RB-19) and reactive violet 5 (RV-5) textile dyes from aqueous solutions. The maximum amounts of RB-19 dye adsorbed at 25 °C are 63.59 (CC-1.3) and 110.6 mg g^-1 (ACC-1.3), and 54.34 (CC-1.3) and 94.32 mg g^-1 (ACC-1.3) for RV-5 dye. Four simulated dye-house effluents were used to test the application of the adsorbents for treatment of effluents.

Especiação e quimissorção de Pb(II) em rejeito de caulim

This study assesses the adsorption of Pb(II) on natural kaolin waste (KR_natural) and on that treated with 3 mol L^-1 H₂SO₄ and HCl. Equilibrium and thermodynamic parameters were determined. The results indicate that the values of CEC, specific area and SiO₂/Al₂O₃ ratio (4.6-6.0 cmol kg^-1, 14.0-16.0 m² g^-1 and 1.16-1.30, respectively) vary only slightly for the adsorbents; the concentration of Pb²⁺ is much higher than that of other species (PbOH⁺ and Pb(OH) ₂). The values of R_L, ΔGº, ΔHº and ΔSº are typical of feasible, spontaneous, exothermic and ordered adsorption. The chemisorption on KR _natural is more feasible and ordered.

Síntese e caracterização de materiais híbridos (PCHs e Organoargilas) com aplicabilidade na adsorção de fenol, benzeno e tolueno

Este estudo avalia o uso de argila do Estado do Acre de natureza esmectítica (argila original) como precursora na síntese de PCHs (Porous Clay Heterostructure) e na organofuncionalização com mercaptopropiltrimetoxisilano (MPTS-Arg) e aplicabilidade desses materiais como adsorventes de fenol, benzeno e tolueno em fase líquida. A síntese de PCHs envolve as seguintes etapas: preparação de organoargila com hexadeciltrimetilamônio (HDTMA-Argila); aumento do espaçamento basal (d₀₀₁) da organoargila usando o cosurfactante octilamina e adição concomitante de uma fonte de Si, como o tetraetilortosilicato (TEOS); lavagens com etanol em HCl, secagem a 60 o C (PCH-60 A e B); calcinação a 500 o C e 700 º C (PCH 500 A/B e PCH 700), com a remoção do surfatante/co-surfactante e consequente substituição destas substâncias orgânicas por prótons que permanecem nas paredes das galerias de pilares de SiO₂ até novo tratamento porventura realizado no PCH. O material MPTS-Arg foi obtido a partir da intercalação de mercaptopropiltrimetoxisilano na argila original sob agitação durante 1 h (Arg-MPTS 1) e na argila original previamente tratada com HCl 1 mol L^-1 e sob agitação durante 2 h (Arg-MPOS 2). Os materiais (argila original, HDTMA-Argila, PCH-60, PCH-500/700 e MPTS-Arg) foram caracterizados por difração de raios-X (DRX), microscopia eletrônica de varredura acoplado a espectroscopia de raios X por dispersão de energia (MEV/ EDS), espectroscopia de absorção molecular IV com transformada de Fourier (FTIR), técnicas de análises térmicas (DTA_TG) e análises texturais, como as medidas de área superficial específica (ASEBET, ASE_Langmuir), volume total de poros (VTP) e diâmetro médio de poros (DMP). Caracterização complementar por ressonância nuclear magnética no estado sólido acoplada a espectrometria de massa (RMN-M AS) foi realizada para o PCH-500 A. Nos experimentos de adsorção de fenol, benzeno e tolueno foram utilizadas suspensões aquosas dos adsorventes contendo separadamente os adsorvatos. As concentrações de equilíbrio de fenol, tolueno e benzeno foram medidas por espectroscopia de absorção molecular na região ultravioleta, conforme método aceito e aplicado em outros estudos de adsorção. Foram obtidos os seguintes resultados: identificação do argilomineral esmectita na argila natural com espaçamento basal de 1,25nm; intercalação do HDTMA e do MPTS com expansão do d(001) para 1,95nm (HDTMA-Arg 5) e 2,1nm (MPTS-Argila 1h). Após a modificação observou-se através da análise de EDS um decréscimo das concentrações dos elementos Na, Si e Al (%) nas posições interlamelares e aumento na concentração de C. O espectro ²⁹Si MAS NMR do PCH-500 A apresentou sinais químicos dos centro Q₃ Si(OSi)₃OH e Q₄ Si(OSi)₄ que indicam a formação de sílica em sua estrutura. Os PCHs (60 e 500 A) foram classificados como mesoporosos, apresentando ASE_BET entre 417 a 446 m² g^-1 e volume total de poros (cm³ g^-1) = 0,367 - 0,369. O aumento da temperatura de calcinação do PCH 500 para 700 o C (PCH 700) propiciou decréscimos em SBET (305 m² g^-1) e diâmetro médio de poros (0.976 nm). Foi verificado a partir da avaliação das medidas dos diâmetro de poros em PCH 700 que 46% das medidas correspondem a microporos. No estudo do equilíbrio de adsorção foram obtidos os valores de K_L (L mg^-1), K_F (L mg^-1) e q_Max (mg g^-1) nos seguintes processos: (i) adsorção de fenol (1.40; 2.26 e 3.80) e tolueno (145, 7.18 e 135) em PCH-500 A; (ii) adsorção de benzeno (0.33, 41.49 e 69.81) em PCH 500 B; (iii) na adsorção de tolueno em argila-MPOS 1 (1.06, 118.9 e 146) e argila-MPOS 2 (2.1, 92 e 97); (iv) na adsorção de fenol (0.07, 0.48 e 4.44) e benzeno (0.11, 4.95 e 35.8) em HDTA-Arg 5, respectivamente. Os dados obtidos sobre a caracterização dos materiais indicaram que a formação dos PCHs propiciou grande aumento nas concentrações de Si e decréscimo nas concentrações de Al, Fe e outros elementos, devido à delaminação- exfoliação da esmectita original. Foi verificado que os materiais são mais adequados para adsorção de tolueno e benzeno do que fenol.