Effect of citrate ions on the electrochemical behaviour of low-carbon steel in borate buffer solutions

The electrochemical behaviour of cold-rolled low carbon steel was studied on both active and passive potential regions in borate buffer solutions with and without the addition of sodium citrate (NaCit). In the active region anodic charges increased significantly and RCT values decreased with citrate, due to the formation of soluble complexes. In the passive potential region the film formed at +0.4 V in borate buffer solution with and without 0.010 M NaCit is probably enriched by Fe3O4 oxide, while films formed at +0.8 V are probably enriched by gamma-Fe2O3. The equivalent circuit [R-s(R(CT)Q)] fitted all experimental impedance data. (C) 2003 Elsevier Ltd. All rights reserved.

In vivo microbiological evaluation of the effect of biomechanical preparation of root canals using different irrigating solutions

The aim of this study was to evaluate the antimicrobial effect of biomechanical preparation using different irrigating solutions. Seventy-eight root canals from premolars of four dogs were used. After experimental induction of periapical lesions, the root canals were prepared using the following solutions for irrigation: Group 1) 2.5% sodium hypochlorite (NaOCl); Group 2) 2% chlorhexidine (CHX); Group 3) saline solution and Group 4) control group with no biomechanical preparation. The microbiological evaluation of the root canals was performed by counting the colony forming units (CFUs) using different culture mediums. Two absorbent paper cones were used in each root canal in order to collect the microbiological samples before, and thirty days after the biomechanical preparation. The culture plates were incubated in aerobic, anaerobic and microaerophilic environment. Statistical evaluation was carried out using analysis of variance, Tukey and Student tests. The results demonstrated that there was reduction in the number of microorganisms in the NaOCl and CHX groups (p<0.05). There was greater effectiveness in the chlorhexidine group. The group that used saline solution and the control group presented an increased number of microorganisms. It can be concluded that the use of antimicrobial irrigating solutions during biomechanical preparation promotes the reduction of endodontic microbiota. However, a considerable number of microorganisms were still observed.

In vitro evaluation of the action of irrigating solutions associated with intracanal medications on Escherichia coli and its endotoxin in root canals

Objective: The purpose of this study was to evaluate the efficacy of auxiliary chemical substances and intracanal medications on Escherichia coli and its endotoxin in root canals. Material and Methods: Teeth were contaminated with a suspension of E. coli for 14 days and divided into 3 groups according to the auxiliary chemical substance used: G1) 2.5% sodium hypochlorite (NaOCl); G2) 2% chlorhexidine gel (CLX); G3) pyrogen-free solution. After, these groups were subdivided according to the intracanal medication (ICM): A) Calcium hydroxide paste (Calen (R)), B) polymyxin B, and C) Calcium hydroxide paste+2% CLX gel. For the control group (G4), pyrogen-free saline solution was used without application of intracanal medication. Samples of the root canal content were collected immediately after biomechanical preparation (BMP), at 7 days after BMP, after 14 days of intracanal medication activity, and 7 days after removal of intracanal medication. The following aspects were evaluated for all collections: a) antimicrobial activity; b) quantification of endotoxin by the limulus Amebocyte lysate test (LAL). Results were analyzed by the kruskal-wallis and Dunn's tests at 5% significance level. Results: The 2.5% NaOCl and CLX were able to eliminate E. coli from root canal lumen and reduced the amount of endotoxin compared to saline. Conclusions: It was concluded that 2.5% NaOCl and CLX were effective in eliminating E. coli. Only the studied intracanal medications were to reduce the amount of endotoxin present in the root canals, regardless of the irrigant used.

Preparation of ceramic membranes from surface modified tin oxide nanoparticles

The preparation of crack-free SnO2 supported membranes requires the development of new strategies of synthesis capable to allow controlled changes of surface chemistry and to improve the processability of supported layers. In this way, the controlled modification of the SnO2 nanoparticle surface by adding capping molecules like Tiron(R) ((OH)(2)C6H2(SO3Na)(2)) during the sol-gel process was studied, aiming to obtain high performance membranes. Colloidal suspensions were prepared by hydrolyzing SnCl4.5H(2)O aqueous solution with NH4OH in presence of Tiron(R). The effect of the amount of Tiro(R) (from I to 20 wt.%) on the structural features of nanoparticles, powder redispersability and particle-solution interface properties was investigated by X-ray powder diffraction (XRPD), extended X-ray absorption fine structure (EXAFS), quasi-elastic light scattering and electrophoretic mobility measurements. XRPD and EXAFS results showed that the addition of Tiron(R) up to 20 wt.% to colloidal suspensions does not affect the crystallite size of SnO2 primary particles, determined around 2-3 nm. This value is comparable to the hydrodynamic size measured after redispersion of powder prepared with amount of Tiro(R) higher than 7.5 wt.%, indicating the absence of condensation reactions between primary particles after the initial precipitation step. As a consequence the powder with amount of Tiron(R) > 7.5 wt.%, can be fully redispersed in aqueous solution at pH greater than or equal to I I until a nanoparticle concentration of 6 vol.%. The electrophoresis measurements showed a decrease of the isoelectric point by increasing the amount of grafted Tiron(R) at the SnO2 nanoparticle surface, resulting in negatively charged particle-solution interface in all the studied pH range (2-11). These features govern the gelation process favoring the preparation of crack-free SnO2 supported membranes. The control exercised by Tiron(R) modifying agent in the aggregation process allows the fine-tuning of the porosity, from 0.124 to 0.065 cm(3) g(-1), and mean pore size, from 6.4 to 1.9 nm, as the amount of grafted molecules increases from 0 to 10 wt.%. In consequence, the membrane cut-off determined by filtration of polyethylene glycol standard solutions can be screened from 1500 to 3500 g mol(-1). (C) 2002 Elsevier B.V. B.V. All rights reserved.

Preparation of ZnO nanoparticles: Structural study of the molecular precursor

The structure of zinc acetate derived precursor currently used in the sol-gel synthesis of ZnO nanoparticles is described. The reaction products obtained before and after reflux of ethanolic zinc acetate solution have been studied by UV-Vis, photoluminescence, FTIR and EXAFS at the Zn K edge. EXAFS results evidence for both precursor solutions a change from the octahedral coordination sphere of oxygen atoms characteristic of the solid zinc acetate dihydrate compound into a four-fold environment. The EXAFS spectra of precursor solutions can be satisfactorily reproduced using the molecular structure reported for Zn4O(Ac)(6) (Ac = COOCH3). UV-Vis and FTIR measurements are also in agreement with the formation of this oligomeric precursor. The structural modification is more pronounced after reflux at 80degreesC, because the increase of the Zn4O(Ac)(6) amount and the formation of nearly 3.0 nm sized ZnO nanoparticle.

Preparation of 9/65/35 PLZT thin films deposited by a dip-coating process

Crack-free polycrystalline PLZT (Pb,a)(Zr,Ti)O-3 thin films with the perovskite structure were prepared by dir-coating using the Pechinis process. Lead acetate, hydrated lanthanum carbonate, zirconium n-propoxide and titanium isopropoxide were used as raw materials. The viscosity of the solution was adjusted in the range of 20 to 56 cP and the films were deposited by a dip-coating process on silicon (100) as substrate. Solutions with ionic concentration of 0.1 and 0.2 M were used. Thin film deposition was accomplished by dipping the substrates in the solution with control of withdrawal speed from 5 to 20 mm/min. The thin films were thermally treated in two steps: at 300 degreesC amid 650 degreesC. The influence of withdrawal speed. viscosity, heating rate and ionic concentration on the morphology of PLZT thin film was discussed. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Preparation of 9.5/65/35 PLZT powders by organic precursor method

In this study the preparation of 9.5/65/35 PLZT ceramic powders were investigated. The powders with the formula Pb0.905La0.095(Zr0.65 Ti0.35)0.976O3 + 3.5 w% PbO were prepared using Pechini process and partial oxalate method. The powder phase formation, powder morphology, and green density of PLZT were shown.

Smear layer removal capacity of disinfectant solutions used with and without EDTA for the irrigation of canals: a SEM study.

The purpose of this study was to carry out a scanning electron microscopic (SEM) analysis of the cleaning qualities and smear layer removal from root canal walls, instrumented and irrigated with 2.5% NaOCl, 2.0% chlorhexidine and saline solutions. Fifty extracted teeth were used in this study. All teeth were radiographed to determine the existence of a single canal. The crowns were cut at the cervical limit and the root canals were instrumented with K-type files up to size 45. During root canal preparation, irrigations were made with the different solutions being evaluated: Group 1: 2.5% NaOCl (10 roots); Group 2: 2.5% NaOCl and 17% EDTA for 2 minute (10 roots); Group 3: 2.0% chlorhexidine (10 roots); Group 4: 2.0% chlorhexidine and 17% EDTA for 2 minutes (10 roots); Group 5: saline solution (5 roots); Group 6: saline solution and 17% EDTA for 2 minutes (5 roots). After instrumentation, the canals were irrigated with each one of the solutions and the roots were cut in the buccolingual direction for SEM analysis, at the cervical, middle and apical thirds, to ascertain the presence or absence of smear layer and debris. SEM analysis was performed by three calibrated examiners and scores were submitted to Kruskal-Wallis test at the significance level of p = 5%. Results showed that the use of 17% EDTA decreased the smear layer significantly (p < 0.05) for all evaluated solutions in all thirds. When EDTA was not used, a significantly higher quantity of smear layer on the apical third was observed only in the NaOCl groups. The use of 17% EDTA was significant for debris removal except for the chlorhexidine groups. The following conclusion could be drawn: the use of 17% EDTA was necessary to enhance cleanness of the root canals.

Influence of brush type as a carrier of adhesive solutions and paper points as an adhesive-excess remover on the resin bond to root dentin

Purpose: To evaluate the influence of the brush type as a earner of priming adhesive solutions and the use of paper points as a remover of the excess of these solutions on the push-out bond strength of resin cement to bovine root dentin. The null hypotheses were that brush type and the use of paper points do not affect the bond strength. Materials and Methods: The canals of 80 single-root bovine roots (16 mm in length) were prepared at 12 mm using the preparation drill (FRC Postec Plus, Ivoclar). Half of each root was embedded in acrylic resin and the specimens were divided into 8 groups, considering the factors brush type (4 levels) and paper point (2 levels) (n = 10): Gr 1: small microbrush (Cavi-Tip, SDI); Gr 2: Microbrush (Dentsply); Gr 3: Endobrush (Bisco); Gr 4: conventional brush (Bisco); Gr 5: Cavi-Tip (SDI) + paper points; Gr 6: Microbrush (Dentsply) + paper points; Gr 7: Endobrush (Bisco) + paper points; Gr 8: conventional brush (Bisco) + paper points. The root dentin was treated with a multistep total-etch adhesive system (All Bond 2). The adhesive system was applied using each microbrush, with and without using paper points. One fiber post was molded with addition silicon and 80 posts were made of resin cement (Duolink), The resin posts were luted (Duolink resin cement), and the specimens were stored for 24 h in water at 37°C. Each specimen was cut into 4 disk-shaped samples (1.8 mm in thickness), which were submitted to the push-out test. Results: The brush type (p < 0.0001) (small microbrush > microbrush = endobrush = conventional brush) and the use of paper points (p = 0.0001) (with > without) influenced the bond strength significantly (two-way ANOVA). The null hypotheses were rejected. Conclusion: The smallest brush (Cavi-Tip) and the use of paper points significantly improved the resin bond to bovine root dentin.

Preparation of a clay-modified carbon paste electrode based on 2-thiazoline-2-thiol-hexadecylammonium sorption for the sensitive determination of mercury

A montmorillonite from Wyoming-USA was used to prepare an organo-clay complex, named 2-thiazoline-2-thiol-hexadecyltrimethylammonium-clay (TZT-HDTA-clay), for the purpose of the selective adsorption of the heavy metals ions and possible use as a chemically modified carbon paste electrode (CMCPE). Adsorption isotherms of Hg 2+, Pb 2+, Cd 2+, Cu 2+, and Zn 2+ from aqueous solutions as a function of the pH were studied at 298 K. Conditions for quantitative retention and elution were established for each metal by batch and column methods. The organo-clay complex was very selective to Hg(II) in aqueous solution in which other metals and ions were also present. The accumulation voltammetry of Hg(II) was studied at a carbon paste electrode chemically modified with this material. The mercury response was evaluated with respect to the pH, electrode composition, preconcentration time, mercury concentration, cleaning solution, possible interferences and other variables. A carbon paste electrode modified by TZT-HDTA-clay showed two peaks: one cathodic peak at about 0.0 V and an anodic peak at 0.25 V, scanning the potential from -0.2 to 0.8 V (0.05 M KNO 3 vs. Ag/AgCl). The anodic peak at 0.25 V presents excellent selectivity for Hg(II) ions in the presence of foreign ions. The detection limit was estimated as 0.1 μg L -1. The precision of determination was satisfactory for the respective concentration level. 2005 © The Japan Society for Analytical Chemistry.

Dependence of the electrical conductivity and elastomeric properties on sample preparation of blends of polyaniline and natural rubber

Blend films (free-standing) containing 20% in volume of polyaniline (PANI) in 80% of natural rubber (NR) were fabricated by casting in three different ways: (1) adding PANI-EB (emeraldine base) dissolved in N-methyl-2-pyrrolidone (NMP) to the latex (NRL), (2) adding PANI-EB dissolved in in-cresol to NR dissolved in xylol (NRD), (3) overlaying the surface of a pure NR cast film with a PANI layer grown by in situ polymerization (NRO). All the films were immersed into HCl solution to achieve the primary doping (protonation) of PANI before the characterization. The main goal here was to investigate the elastomeric and electrical conductivity properties for each blend, which may be applied as pressure and deformation sensors in the future. The characterization was carried out by optical microscopy, dc conductivity, vibrational spectroscopy (infrared absorption and Raman scattering), thermogravimetry analysis (TGA), differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMTA), and tensile stress-strain curves. The results suggest that the NRL blend is the most suitable in terms of mechanical and electrical properties required for applications in pressure and deformation sensors: a gain of conductivity without losing the elastomeric property of the rubber. (c) 2005 Wiley Periodicals, Inc.

Preparation of polymeric micelles for use as carriers of tuberculostatic drugs

Purpose: This paper focuses on the characterization of polymeric micelle-forming tuberculostatic prodrugs and the antimycobacterial activity of these prodrugs.Method: By the condensation of hydroxymethylpyrazinamide, isoniazid and rifampin with free carboxyl groups on the copolymer poly(ethyleneglycol)-poly(aspartic acid), micelle-forming carrier-drug conjugates were obtained. These micelles were characterized by dynamic light scattering, to measure the micelle diameter; by acid-base titration, to determine the percentage of carboxylic groups occupied by the tuberculostatic; by Sudan III solubility tests, to estimate the critical micelle concentration (CMC); and visual control and spectrophotometric measurement, to determine the stability of micelles. These micelles were tested in vitro against several Mycobacterium strains.Results: As expected, the size and distribution of the micelle-forming tuberculostatic prodrugs found to be small (78.2nm, 84.2nm and 98.9 nm) while the level of the drug conjugated was high (65.02-85.7%). Furthermore, the micelles were stable in vitro, exhibiting a low level of CMC and stronger antimycobacterial activity than the original drugs.Conclusion: the results demonstrate that polymeric micelles can be used as efficient carriers for drugs, which alone, exhibit undesired pharmacokinetics, poor solubility, and low stability. The synthesized micelle-forming tuberculostatic prodrugs opens a perspective of alternative prodrugs that prolong action and decrease the toxicity of the tuberculostatic drugs of choice.

Disclosing the generic behavior of topological solutions: An orbit-based approach

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Preparation of Ni-Ti-Mo and Ni-Ti-Mo-Zr Alloys by High-Energy Ball Milling and Subsequent Hot Pressing

This work discusses on the preparation of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr (at-%) alloys by high-energy ball milling and hot pressing, which are potentially attractive for dental and medical applications. The milling process was performed in stainless steel balls (19mm diameter) and vials (225 mL) using a rotary speed of 300rpm and a ball-to-powder weight ratio of 10:1. Hot pressing under vacuum was performed in a BN-coated graphite crucible at 900 degrees C for 1 h using a load of 20 MPa. The milled and hot-pressed materials were characterized by X-ray diffraction, electron scanning microscopy, and electron dispersive spectrometry. Peaks of B2-NiTi and Ni4Ti3 were identified in XRD patterns of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr powders milled for 1h. The NiTi compound dissolved small Mo amounts lower than 4 at%, which were measured by EDS analysis. Moreover, it was identified the existence of an unknown Mo-rich phase in microstructures of the hot-pressed Ni-Ti-Mo alloys.