Synthesis and thermal study of 8-hydroxy-quinoline derivatives of the alkaline Earth metals: I. Strontium complexes

Strontium complexes of 5,7-dibromo-, 5,7-dichloro-, 7-iodo- and 5-chloro-7-iodo-8-hydroxyquinoline were precipitated from an aqueous ammonia and acetone medium. The complexes obtained were Sr[(C9H4ONBr2)2]·2.5H 2O; Sr[(C9H4ONCl2)(OH)]·1.5H2O; Sr[(C9H5ONI)2]·5H2O and Sr[(C9H4ONICl)(OH)]·1.25H2O. The residues of their thermal decomposition were SrBr2; a mixture of SrCl2, SrCO3 and SrO3 SrCO3, and SrCO3, respectively. All were characterized by means of thermogravimetry, differential thermal analysis, complexometry with EDTA, atomic absorption spectroscopy, IR spectroscopy and X-ray diffraction. © 1999 Akadémiai Kiadó.

Structural and electrical properties of strontium barium niobate thin films crystallized by conventional furnace and rapid-thermal annealing process

Strontium barium niobate (SBN) thin films were crystallized by conventional electric furnace annealing and by rapid-thermal annealing (RTA) at different temperatures. The average grain size of films was 70 nm and thickness around 500 nm. Using x-ray diffraction, we identified the presence of polycrystalline SBN phase for films annealed from 500 to 700 °C in both cases. Phases such as SrNb2O6 and BaNb2O6 were predominantly crystallized in films annealed at 500 °C, disappearing at higher temperatures. Dielectric and ferroelectric parameters obtained from films crystallized by conventional furnace and RTA presented essentially the same values.

Dielectric relaxation and relaxor behavior in bilayered perovskites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microstructure and phase evolution of SrTiO3 thin films on Si prepared by the use of polymeric precursors

The use of polymeric precursors was employed in preparing SrTiO3 thin films by dip coating using Si (111) as substrate. Crack free films were obtained after sintering at temperatures ranging from 550 to 1000°C. The microstructure, characterized by SEM, shows the development of dense polycrystalline films with smooth surface and mean grain size of 52 nm, for films sintered at 1000°C. Grazing incident angle XRD characterization of these films shows that the SrTiO3 phase crystallizes from an inorganic amorphous matrix. No intermediate crystalline phase was identified.

Preparation and characterization of SrBi2Nb2O9 thin films made by polymeric precursors

A polymeric precursor solution was employed in preparing SrBi2Nb2O9 (SBN) powder and thin films dip coated onto Si(100) substrate. XRD results show that the SBN perovskite phase forms at temperatures as low as 600°C through an intermediate fluorite phase. This fluorite phase is observed for samples heat-treated at temperatures of 400 and 500°C. After heat treatment at temperatures ranging from 300 to 800°C, thin films were shown to be crack free. Grazing incident angle XRD characterization shows the occurrence of the fluorite intermediate phase for films also. The thickness of films, measured by MEV, was in the order of 80-100 nm.

The influence of crystallization route on the SrBi2Nb2O9 thin films

Polycrystalline SrBi2Nb2O9-layered ferroelectric thin films were synthesized on Pt/Ti/SiO2/Si substrate using the polymeric precursors solution. The dip-coated films were specular and crack-free and crystallized during firing at 700 °C. Single-, double-, and triple-layered films were obtained by several dips in the deposition solution, and the influence of crystallization between each dip was studied. Microstructure and morphological evaluation were followed by grazing incident x-ray diffraction (GIXRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Multilayered films obtained using the intermediate-crystallized layer route present a dense microstructure with spherical grains, with a preferential orientation in the 〈215〉 direction; films obtained using the intermediate-amorphous layer route are polycrystalline and present elongated grains around 250 nm in size.

Crystallographic, dielectric and optical properties of SrBi 2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (Pt/Ti/SiO 2 /Si), n -type (100)-oriented and p -type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P r values of 6.24 μC/cm 2 and 31.5 kV/cm for the film annealed at 800 C. The film deposited onto fused silica and treated at 700 C presented around 80% of transmittance. © 2002 Taylor & Francis.

Room-temperature photoluminescence in amorphous SrTiO3-The influence of acceptor-type dopants

Room-temperature photoluminescence (PL) was observed in undoped and 2 mol% Cr-, Al- and Y-doped amorphous SrTiO3 thin films. Doping increased the PL, and in the case of Cr significantly reduced the associated PL wavelength. The optical bandgaps, calculated by means of UV-vis absorption spectra, increased with crystallinity and decreased with the doping level. It was considered that yttrium and aluminum substituted Sr2+, whereas chromium replaced Ti4+. It is believed that luminescence centers are oxygen-deficient BO6 complexes, or the same centers with some other defects, such as oxygen or strontium vacancies, or BO6 complexes with some other defects placed in their neighborhood. The character of excitation and the competition for negatively charged non-bridging oxygen (NBO) among numerous types of BO6 defect complexes in doped SrTiO3 results in various broadband luminescence peak positions. The results herein reported are an indicative that amorphous titanates are sensitive to doping, which is important for the control of the electro-optic properties of these materials. The probable incorporation of Cr into the Ti site suggests that the existence of a double network former can lead to materials displaying a more intense photoluminescence.

Heterogeneous catalysis afford biodiesel of babassu, castor oil and blends

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Rietveld refinement, morphology and optical properties of (Ba 1-xSrx)MoO4 crystals

In this article, the structural refinement, morphology and optical properties of barium strontium molybdate [(Ba1-x Sr x )MoO4 with x = 0, 0.25, 0.50, 0.75 and 1] crystals, synthesized by the co-precipitation (drop-by-drop) method, are reported. The crystals obtained were structurally characterized by X-ray diffraction (XRD), Rietveld refinement, and Fourier transform-Raman (FT-Raman) and Fourier transform-infrared (FT-IR) spectroscopies. The shapes of the crystals were observed by means of field-emission scanning electron microscopy (FE-SEM). The optical properties were investigated using ultraviolet-visible (UV-Vis) absorption spectroscopy and photoluminescence (PL) measurements. XRD patterns, Rietveld refinement, and FT-Raman and FT-IR spectra showed that all of the crystals are monophasic with a scheelite-type tetragonal structure. The refined lattice parameters and atomic positions were employed to model the [BaO8], [SrO8] and [MoO4] clusters in the tetragonal lattices. The FE-SEM images indicate that increased x content produces a decrease in the crystal size and modifications in the crystal shape. UV-Vis spectra indicated a decrease in the optical band gap with an increase in x in the (Ba1-x Sr x )MoO4 crystals. Finally, a decrease in the intensity of PL emission is apparent with an increase in x up to 0.75 in the (Ba1-x Sr x )MoO4 crystal lattice when excited by a wavelength of 350nm, probably associated with the degree of structural order-disorder. © 2013 International Union of Crystallography Printed in Singapore - all rights reserved.

Synthesis, characterization and thermal studies of alkaline earth glycolate, except beryllium and radium

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal and crystalographic studies of mixture La2O3-SrO prepared via reaction in the solid state

The compound obtained via state solid reaction of the La2O3 and SrO oxides and expose the room atmosphere shows the crystallographic data of the compound reported as La2SrOx. However, thermogravimetric, differential thermal analysis and XRD with controlled temperature indicated that the stoichiometry of the compound is 2La(OH)(3)-SrCO3, which structural parameters were determined by using the Rietveld method. It was verified that when the compound exposed at room atmosphere, the mixture oxide absorbs H2O and CO2 producing hydroxide and carbonate of lanthanum and strontium, respectively, which thermal decomposition occurs by the same steps, producing the La2O3-SrO.

Microwave-hydrothermal synthesis of barium strontium titanate nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of barium and strontium addition on the ratio c/a of PZT obtained by the polymeric precursor method

Lead zirconate titanate powder, with Zr/Ti ratio of 50/50 was prepared by Pechini method after adding up to 10,0 mol% of Ba +2 and Sr +2 ions. Tetragonal phase is favored by the increase of barium and strontium concentration in the LiNbO 3 crystal lattice. The ratio c/a for tetragonal phase increases with the content of Ba +2 and Sr +2.

Structural phase evolution of strontium-doped lead titanate thin films prepared by the soft chemical technique

Strontium-modified lead titanate thin films with composition Pb1-xSrxTiO3 were grown on Pt/Ti/SiO2/Si substrates using the polymeric precursor method. The structural phase evolution as a function of the Sr contents was studied using micro-Raman scattering, specular reflectance infrared Fourier transform spectroscopy, and x-ray diffraction. The results showed a gradual change from tetragonal to cubic structure, the transition occurring at about x = 0.58. The infrared reflectance spectra showed that the frequency of several peaks decreases as the strontium concentration increases. These features are correlated with a decrease in the tetragonal distortion of the TiO6 octahedra as the strontium concentration increases.