Describing fatigue crack growth and load ratio effects in Al 2524 T3 alloy with an enhanced exponential model

The fatigue crack behavior in metals and alloys under constant amplitude test conditions is usually described by relationships between the crack growth rate da/dN and the stress intensity factor range Delta K. In the present work, an enhanced two-parameter exponential equation of fatigue crack growth was introduced in order to describe sub-critical crack propagation behavior of Al 2524-T3 alloy, commonly used in aircraft engineering applications. It was demonstrated that besides adequately correlating the load ratio effects, the exponential model also accounts for the slight deviations from linearity shown by the experimental curves. A comparison with Elber, Kujawski and "Unified Approach" models allowed for verifying the better performance, when confronted to the other tested models, presented by the exponential model. (C) 2012 Elsevier Ltd. All rights reserved.

Fatigue crack growth of Al 7475 T761 under constant and variable amplitude loading

Experimental programs in constant and variable amplitude loading were performed to obtain a x N curves and to study retardation in fatigue crack growth due to overloads. The main aim of this research program was to analyse the effect of overload ratio and number of overload peaks. The effect of underloads, before and after the overload blocks was also studied. The generalised equation of Paris-Erdogan type was used for modelling of obtained data on crack propagation under constant amplitude load.

Mechanical strength and subcritical crack growth under wet cyclic loading of glass-infiltrated dental ceramics

Objectives. Evaluate the flexural strength (sigma) and subcritical crack growth (SCG) under cyclic loading of glass-infiltrated alumina-based (IA, In-Ceram Alumina) and zirconia-reinforced (IZ, In-Ceram Zirconia) ceramics, testing the hypothesis that wet environment influences the SCG of both ceramics when submitted to cyclic loading.Methods. Bar-shaped specimens of IA (n = 45) and IZ ( n = 45) were fabricated and loaded in three-point bending (3P) in 37 degrees C artificial saliva (IA(3P) and IZ(3P)) and cyclic fatigued (F) in dry (D) and wet (W) conditions (IA(FD), IA(FW), IZ(FD), IZ(FW)). The initial sigma and the number of cycles to fracture were obtained from 3P and F tests, respectively. Data was examined using Weibull statistics. The SCG behavior was described in terms of crack velocity as a function of maximum stress intensity factor (K(Imax)).Results. The Weibull moduli (m = 8) were similar for both ceramics. The characteristic strength (sigma(0)) of IA and IZ was and 466 MPa 550 MPa, respectively. The wet environment significantly increased the SCG of IZ, whereas a less evident effect was observed for IA. In general, both ceramics were prone to SCG, with crack propagation occurring at K(I) as low as 43-48% of their critical K(I). The highest sigma of IZ should lead to longer lifetimes for similar loading conditions.Significance. Water combined with cyclic loading causes pronounced SCG in IZ and IA materials. The lifetime of dental restorations based on these ceramics is expected to increase by reducing their direct exposure to wet conditions and/or by using high content zirconia ceramics with higher strength. (C) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Modelling of fatigue crack growth following overloads

In variable-amplitude loading there are interaction effects between the loading history and the crack propagation rate. The most important of these effects is the retardation in the crack propagation, which may raise the life of the cracked structureconsiderably. The main objective of this research is to analyse and quantify the retardation of crack propagation in a thin plate of the high-resistance aluminium alloy 2024-T3, comparing the results obtained from the mathematical models proposed to account for the retardation effect. The specimens were tested under high-low loading sequences, for different crack sizes and overload ratios. A simplified model was developed, based on crack closure theory, that could represent the crack behaviour during retardation very well. © 1991.

Microstructural effects on fatigue crack growth behavior of a microalloyed steel

Thermal transformations on microalloyed steels can produce multiphase microstructures with different amounts of ferrite, martensite, bainite and retained austenite. These different phases, with distinct morphologies, are determinant of the mechanical behavior of the steel and can, for instance, affect the crack path or promote crack shielding, thus resulting in changes on its propagation rate under cyclic loading. The aim of the present work is to evaluate the effects of microstructure on the tensile strength and fatigue crack growth (FCG) behaviour of a 0.08%C-1,5%Mn (wt. pct.) microalloyed steel, recently developed by a Brazilian steel maker under the designation of RD480. This steel is being considered as a promising alternative to replace low carbon steel in wheel components for the automotive industry. Various microstructural conditions were obtained by means of heat treatments followed by water quench, in which the material samples were kept at the temperatures of 800, 950 and 1200 °C. In order to describe the FCG behavior, two models were tested: the conventional Paris equation and a new exponential equation developed for materials showing non-linear FCG behavior. The results allowed correlating the tensile properties and crack growth resistance to the microstructural features. It is also shown that the Region II FCG curves of the dual and multiphase microstructural conditions present crack growth transitions that are better modeled by dividing them in two parts. The fracture surfaces of the fatigued samples were observed via scanning electron microscopy in order to reveal the fracture mechanisms presented by the various material conditions. © 2010 Published by Elsevier Ltd.

Fatigue crack growth rate in mode I of a carbon fiber 5HS weave composite laminate processed via RTM

Delamination or crack propagation between plies is a critical issue for structural composites. In viewing this issue and the large application of woven fabrics in structural applications, especially the ones that requires high drapeability to be preformed in a RTM mold cavity such as the asymmetric ones, e.g HS series, this research aimed in dynamically testing the carbon fiber 5HS/RTM6 epoxy composites under opening mode using DCB set up in order to investigate the crack growth rate behavior in an irregular surface produced by the fabric waviness. The evaluation of the energy involved in each crack increment was based on the Irwin-Kies equation using compliance beam theory. The tests were conducted at constant stress ratio of R=0.1 with displacement control, frequency of 10 Hz, in accordance to ASTM E647-00 for measurement of crack growth rate. The results showed large scatter when compared to unidirectional carbon fiber composites due to damage accumulation at the fill tows.

Muscle growth in Nile tilapia (Oreochromis niloticus): histochemical, ultrastructural and morphometric study

Muscle growth in Nile tilapia (Oreochromis niloticus) was studied focusing on histochemical, ultrastructural, and morphometric characteristics of muscle fibers. Based on body length (cm), we studied four groups: G1 = 1.36+/-0.09, G2 = 3.38+/-0.44, G3 = 8.90+/-1.47, and G4 = 28.30+/-3.29 (mean+/-S.D.). All groups showed intense reaction to NADH-TR in subdermal fibers and weak or no reaction in deep layer fibers. In G3 and G4, an intermediate layer was also observed with fibers presenting weak reaction; in G4, groups of fibers with intense reaction were observed in the subdermal region. The myosin ATPase (m-ATPase) activities were acid-stable and alkali-labile in subdermal fibers; most deep layer fibers were alkali-stable and acid-labile. Intermediate fibers were acid-labile and alkali-stable. Two fiber populations were observed near deep muscle layer: one large presenting weak acid- and alkali-stable and the other small alkali-stable.During growth, muscle fiber hypertrophy was more evident in intermediate and white fibers for G3 and G4. However, in these groups, the presence of fiber diameters less than or equal to21 mum suggested that there is still substantial fiber recruitment, confirmed by ultrastructural study, but hypertrophy is the main mechanism contributing to increase in muscular mass. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

Modeling the growth of LT and TL-oriented fatigue cracks in longitudinally and transversely pre-strained Al 2524-T3 alloy

The aluminum alloy 2524 (Al-Cu-Mg) was developed during the 90s mainly to be employed in aircraft fuselage panels, replacing the standard Al 2024. In the present analysis the fatigue crack growth (FCG) behavior of 2524-T3 was investigated, regarding the influence of three parameters: load ratio, pre strain and crack plane orientation of the material. The pre strain of aluminum alloys is usually performed in order to obtain a more homogeneous precipitates distribution, accompanied by an increase in the yield strength. In this work, it was evaluated the resistance of Al 2524-T3 sheet samples to the fatigue crack growth, having L-T and T-L crack orientations. FCG tests were performed under constant amplitude loading at three distinct positive load ratios. The three material conditions were tested: as received(AR), pre strained longitudinally (SL) and transversally (ST) in relation to rolling direction. In order to describe FCG behavior, two-parameter kinetic equations were compared: a Paris-type potential model and a new exponential equation introduced in a previous work conducted by our research group. It was observed that the exponential model, which takes into account the deviations from linearity presented by da/dN versus AK data, describes more adequately the FCG behavior of Al 224-T3 in relation to load ratio, pre strain effects and crack plane orientation. © 2011 Published by Elsevier Ltd.

Fadiga em compósitos 5HS carbono/epóxi processados via RTM: relação entre cargas axiais no plano e modos de delaminação

Pós-graduação em Engenharia Mecânica - FEG

Influência de defeitos e diferentes processos de fabricação nas propriedades mecânicas finais de cerâmicas

Os materiais cerâmicos são atualmente cada vez utilizados como opção na engenharia mundial. Por se tratar de materiais com alta resistência mecânica, possuem muitas aplicações em diversas áreas, como por exemplo a de mancais, a automotiva (sensores, isoladores, catalisadores, pistões, válvulas, revestimentos), a de implantes biocompatíveis (dentário, substituição óssea, válvulas cardíacas), a de produtos sujeitos ao desgaste (guias), a de refratários (revestimento de equipamento bélico, componentes de fornos), a eletrônica, e outras. Nos processos de fabricação da cerâmica há uma gama de fatores que contribuem para as características do produto final. Devido a isso, muitos pesquisadores têm trabalhado no estudo da influência de determinados defeitos e técnicas de produção de cerâmicas nas características do produto final. Este trabalho tem como objetivo fazer uma revisão bibliográfica de recentes artigos que analisam a influência de fatores como velocidade de queima, surgimento de trincas, porosidade, fases cristalinas, e tamanho de partículas, nas propriedades mecânicas finais das cerâmicas. Pode-se concluir que é possível aperfeiçoar o processo de fabricação da cerâmica a fim de promover as melhores propriedades mecânicas possíveis, conhecendo-se fatores prejudiciais e métodos adequados para se obter o melhor produto final.

Considerations about the welding repair effects on the structural integrity of an airframe critical to the flight-safety

Structures critical to the flight-safety are commonly submitted to several maintenance repairs at the welded joints in order to prolong the in-service life of aircrafts. The aim of this study is to analyze the effects of Tungsten Inert Gas (TIG) welding repair on the structural integrity of the AISI 4130 aeronautical steel by means of experimental fatigue crack growth tests in base-material, heat-affected zone (HAZ) and weld metal. The tests were performed on hot-rolled steel plate specimens, 0.89 mm thick, with load ratio R = 0.1, constant amplitude, at 10 Hz frequency and room temperature. Increase of the fracture resistance was observed in the weld metal but decreasing in the HAZ after repair. The results were associated to microhardness and microstructural changes with the welding sequence. (C) 2010 Published by Elsevier Ltd.

Evaluation of the fretting fatigue behaviour of commercially pure titanium

Fretting fatigue occurs when the contact surfaces of two components undergo small oscillatory movement while they are subjected to a clamping force. A cyclic external load gives rise to the early initiation of fatigue cracks, thus reducing their service life. In this paper, the fretting fatigue behaviour of commercially pure titanium flat samples (1.5 mm thick) is evaluated. A fretting device composed of a frame, load cell, and two screw-mounted cylindrical fretting pads with convex extremities was built and set to a servo-hydraulic testing machine. The fatigue tests were conducted under load control at a frequency of 10 Hz and stress ratio R = 0.1, with various contact load values applied to the fretting pads. Additional tests under inert environment allowed assessing the role of oxidation on the wear debris formation. The fracture surfaces and fretting scars were analysed via scanning electron microscopy in order to evaluate the surface damage evolution and its effect on the fatigue crack features. The effect of the fretting condition on the S-N curve of the material in the range of 10(4)-10(6) cycles is described. Fatigue crack growth calculations allowed estimating the crack initiation and propagation lives under fretting conditions. The effect of the fretting condition in fatigue life is stronger for the lower values of cyclic stress and does not seem to depend on the contact loading value.

Study of the dimensions of double-torsion test specimens

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characteristics of the double-torsion test to determine the R-curve of ceramic materials

Double-torsion tests were carried out on a commercial ceramic floor tile to verify whether this test is suitable for determining the R-curve of ceramics. The instantaneous crack length was obtained by means of compliance calibration, and it was found that the experimental compliance underestimates the real crack length. The load vs. displacement curves were also found to drop after maximum loading, causing the stress intensity factor to decline. The R-curves were calculated by two methods: linear elastic fracture mechanics and the energetic method. It was obtained that the average values of crack resistance, R, and the double of the work of fracture, 2 · γwof, did not depend on notch length, a0, which is a highly relevant finding, indicating that these parameters were less dependent on the test specimen's geometry. The proposal was to use small notches, which produce long stable crack propagation paths that in turn are particularly important in the case of coarse microstructures.

Determinação da taxa de propagação de trinca por fadiga dos aços SAE-1050 e SAE-4130 empregados na fabricação de eixos ferroviários

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)