Improvement of the chemical resistance of zirconium fluoride glasses coated with a Tiron (R) modified tin oxide layer prepared by the sol-gel process

In order to improve the chemical resistance of zirconium fluoride glass a protective transparent SnO2 layer was deposited by the solgel dip-coating process in the presence of Tiron (R) as particle surface modifier agent. After water immersion for different periods of time, both coated and non-coated fluoride glasses were analyzed by scanning electron microscopy, mass loss evaluation, infrared spectroscopy and X-ray photoelectron spectroscopy. In contrast to the effects occurring for non-coated glass, where the surface undergoes a rapid selective dissolution of the most soluble species, the results for the SnO2-coated glass showed that the filling of the film nanopores by dissolved glass material results in a hermetic barrier protecting the glass surface. The selective glass dissolution was confirmed by liquid chromatography measurements of the etching solution after each exposure time. (c) 2006 Elsevier B.V. All rights reserved.

Electrical percolation during gelation of lithium doped siloxane-poly(oxyethylene) hybrids

Gelation mechanisms of lithium-doped Siloxane-Poly(oxyethylene) (PEO) hybrids containing polymer of two different molecular weight (500 and 1900 g/mol) were investigated through the evolution of the electrical properties during the solgel transition. The results of electrical measurements, performed by in-situ complex impedance spectroscopy, were correlated with the coordination and the dynamical properties of the lithium ions during the process as shown by Li-7 NMR measurements. For both hybrids sols, a decrease of the conductivity is observed at the initial gelation stage, due to the existence of an inverted percolation process consisting of the progressive separation of solvent molecules containing conducting species in isolated islands during the solid network formation. An increase of conductivity occurs at more advanced stages of gelation and aging, attributed to the increasing connectivity between PEO chains promoted by the formation of crosslinks of siloxane particles at their extremities, favoring hopping motions of lithium ions along the chains.

Erbium-activated HfO2-based waveguides for photonics

70SiO2 - 30HfO2 planar waveguides, activated by Er3+ concentration ranging from 0.3 to 1 mol%, were prepared by solgel route, using dip-coating deposition on silica glass substrates. The waveguides showed high densification degree, effective intermingling of the two components of the film, and uniform surface morphology. Propagation losses of about 1 dB/cm were measured at 632.8 nm. When pumped with 987 nm or 514.5 nm continuous-wave laser light, the waveguides showed the 4I 13/2→4I15/2 emission band with a bandwidth of 48 nm. The spectral features were found independent both on erbium content and excitation wavelength. The 4I13/2 level decay curves presented a single exponential profile, with a lifetime between 2.9-5.0 ms, depending on the erbium concentration.

Utilização de sistemas poliméricos híbridos orgânicos-inorgânicos no desenvolvimento de sistemas formadores de filme

Pós-graduação em Ciências Farmacêuticas - FCFAR

Espumas cerâmicas produzidas pela conjugação dos processos sol-gel, aeração e emulsificação

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Avaliação de processos de degradação de corantes dispersos por técnicas eletroquímica e fotoeletroquímica usando eletrodos de Pt, filmes finos e nanotubos de 'TI'/'TIO IND. 2' e bicomponentes 'W'/'WO IND. 3'/'TIO IND. 2'

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Electrical properties of highly conducting Sno2:Sb nanocrystals synthesized using a nonaqueous sol gel method

This work describes the synthesis of highly conducting antimony-doped tin oxide (ATO) nanocrystals prepared via a nonaqueous sol–gel route in the size range of 4–6 nm and provides insights into its electrical properties. The antimony composition was varied from 1 to 18 mol% and the lowest resistivity (4.0 × 10−4Ω·cm) was observed at room temperature in the SnO2:8.8 mol% Sb composition. The samples were evaluated by X-ray diffraction, high-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, and scanning electron microscope, and resistivity measurements were taken in the four-probe mode in the temperature range of 13–300 K. The results show highly crystalline nanoparticles in a monodisperse colloidal system, dependence on the shape of ATO nanoparticles as a function of Sb distribution, low resistivity, and semiconductor–metal transition.

Analysis of fluoxetine and norfluoxetine in human plasma by HPLC-UV using a high purity C18 silica-based SPE sorbent

This paper reports on the development and validation of a simple and sensitive method that uses solid phase extraction (SPE) and liquid chromatography with ultraviolet detection to analyze fluoxetine (FLX) and norfluoxetine (NFLX) in human plasma samples. A lab-made C18 SPE phase was synthesized by using a sol–gel process employing a low-cost silica precursor. This sorbent was fully characterized by nuclear magnetic resonance (NMR), Fourier-transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM) to check the particles' shape, size and C18 functionalization. The lab-made C18 silica was used in the sample preparation step of human plasma by the SPE-HPLC-UV method. The method was validated in the 15 to 500 ng mL 1 range for both FLX and NFLX using a matrix matched curve. Detection limits of 4.3 and 4.2 ng mL 1 were obtained for FLX and NFLX, respectively. The repeatability and intermediary precision achieved varied from 7.6 to 15.0% and the accuracy ranged from 14.9 to 9.1%. The synthesized C18 sorbent was compared to commercial C18 sorbents. The average recoveries were similar (85–105%), however the lab-made C18 silica showed fewer interfering peaks in the chromatogram. After development and validation, the method using the lab-made C18 SPE was applied to plasma samples of patients under FLX treatment (n ¼ 6). The concentrations of FLX and NFLX found in the samples varied from 46.8–215.5 and 48.0–189.9 ng mL 1 , respectively.

The kinetic of mullite crystallization: Effect of water content

The kinetic of mullite crystallization from sol–gel method, with different water content, was investigated under non-isothermal conditions using DTA. The sols were obtained from Al(NO3)3.9H2O (ANN) and Si(OC2H5)4 (TEOS) mixtures by varying the water–alcohol content of the system. The crystalline phase changes were verified by X-ray diffraction (XRD). For a sample prepared using ethanol-based alkoxide solution (M0), only Al-poor mullite (p-mullite) crystallizes at 1000 °C; for the one synthesized with low water concentration (M6) Al-rich mullite (r-mullite) and spinel crystallize together; and for a sample prepared using a water-based alkoxide solution only spinel is formed. Thus, the variation of water contents during the synthesis caused great variations in the course of mullitization process. The average value of the apparent activation energy determined for p-mullite, r-mullite and spinel phase crystallization were found to be E = (899 ± 61) kJ mol−1, E = (1015 ± 272) kJ mol−1 and E = (980 ± 196) kJ mol−1, respectively. These results showed that sample M(0) was a monophasic gel, where aluminum and silicon atoms are mixed at a molecular level while sample M(100) was a diphasic gel, where silicon and aluminum atoms are distributed in a nanometric level. The fast reaction between TEOS and water molecules is responsible for this great difference in the sample's homogeneity. The kinetic model of the crystallization process was determined using Malek's procedure. It was established that the crystallization of p-mullite, r-mullite and spinel phase can be described by Šesták–Berggren autocatalytic model.

Optical filters and resonant cavities based on di-ureasil organic–inorganic hybrids

Sol–gel derived poly(oxyethylene)/siloxane organic–inorganic di-ureasil hybrids containing different amounts (20–60% mol) of methacrylic acid (McOH) modified zirconium oxo-clusters (Zr-OMc) were processed as thin films and transparent and shape controlled monoliths. Laser direct writing was used to create channel waveguides, Bragg gratings, Fabry–Perot cavities and optical filters. The resulting Fabry–Perot optical cavity displays a free spectral range of 16.55 GHz and a fringe intensity contrast of 5.35 dB. Optical rejection values between 6.7 and 10.4 dB were obtained by varying the amount of the Zr-OMc oxo-clusters.