Pre-resonant Raman effect of CrO2- 4 in a metasilicate glass

Pre-resonant Raman effect of chromate ion, CrO2- 4, was observed in a metasilicate glass with molar composition 2Na2O · 1CaO · 3SiO2 containing 1.0 wt% of Cr2O3. Raman spectra were measured by the conventional 90° scattering geometry and by the microprobe Raman spectroscopic techniques. The presence of chromate ions in the glass is favoured by the glass composition and oxidizing conditions during the glass melting, and they are responsible for optical absorption bands at 370 and 250 nm. Raman spectrum of the undoped glass presents bands at 625, 860 and 980 cm-1, and the presence of chromate ions gives rise to additional bands at 365, 850 and a shoulder at 890 cm-1. An enhancement of the 850 cm-1 Raman band is observed with decreasing laser exciting wavelength. The exciting frequency dependence of the intensity of this band is discussed in terms of theoretical models given in the literature.

Optical filters and resonant cavities based on di-ureasil organic–inorganic hybrids

Sol–gel derived poly(oxyethylene)/siloxane organic–inorganic di-ureasil hybrids containing different amounts (20–60% mol) of methacrylic acid (McOH) modified zirconium oxo-clusters (Zr-OMc) were processed as thin films and transparent and shape controlled monoliths. Laser direct writing was used to create channel waveguides, Bragg gratings, Fabry–Perot cavities and optical filters. The resulting Fabry–Perot optical cavity displays a free spectral range of 16.55 GHz and a fringe intensity contrast of 5.35 dB. Optical rejection values between 6.7 and 10.4 dB were obtained by varying the amount of the Zr-OMc oxo-clusters.