Evaluation of the thermoplasticity of different gutta-percha cones and Resilon®

The goal of this study was to evaluate the thermoplasticity of conventional and thermoplastic gutta-percha and Resilon®, a polyester polymer-based material. Specimens with standardised dimensions were made from the following materials: conventional and thermoplastic gutta-percha (Dentsply), conventional and thermoplastic gutta-percha (Endopoints) and Resilon®. After 24 h, the specimens were placed in water at 70°C for 60 s, and thereafter positioned between two glass slabs. Each set was compressed by a 5-kg weight. Digital images of the specimens before and after compression were obtained and analysed. The thermoplasticity of each material was confirmed by the difference between final and initial areas of each sample. The data were analysed statistically by ANOVA and Tukey's test at a 5% significance level. Resilon® had the highest thermoplasticity means (P < 0.05). Among the gutta-percha cones, Endopoints TP (thermoplastic) presented the highest thermoplasticity means and differed significantly from the other commercial brands (P < 0.05). Resilon® had good thermoplasticity, endorsing its use as a thermoplastic root canal filling material. © 2007 The Authors. Journal compilation © 2007 Australian Society of Endodontology.

Solvent capacity of different substances on gutta-percha and resilon

The aim of this study was to evaluate the effectiveness of 3 solvents (eucalyptol, orange oil, and xylol) on 2 types of gutta-percha (conventional and thermoplastic) and Resilon. Specimens (10 mm diameter × 1 mm thick; n=7 per condition) were prepared and maintained at 37°C for 48 h. Each specimen was weighed on a precision scale every 24 h until its mass was stable, at which time the initial mass was determined. Specimens (n=7) were then immersed in the solvent solutions and, after 48 h at 37°C, they were reweighed at 24- h intervals, until stabilization (final mass). The difference between the final and the initial mass determined the solvent capacity of each solvent. Data were subjected to analysis of variance and Tukey's test at 5% significance level. The results demonstrated that xylol was the most effective, especially on conventional gutta-percha and Resilon (p<0.05). Eucalyptol and orange oil were more effective on thermoplastic gutta-percha than the other materials (p<0.05). It was concluded that all evaluated substances presented solvent action, but xylol was the most effective on both gutta-percha or Resilon.

Effectiveness of three solvents and two associations of solvents on gutta-percha and Resilon

This study evaluated the effectiveness of 3 solvents (Citrol orange oil, Eucalyptol and Tetrachloroethylene) and 2 associations of solvents (Citrol orange oil+Tetrachloroethylene and Eucalyptol+Tetrachloroethylene) on 3 types of gutta-percha (conventional, thermoplastic and EndoREZ) and Resilon. Ten discs (10 mm diameter x 1 mm thick) from each material were prepared using standard metallic molds. Each specimen was weighed to determinate its initial mass. The specimens were immersed in the solvents for 10 min, followed by immersion in distilled water for 20 min, and were then reweighed to obtain the final mass. The mean weight loss determined the solvent capacity. Data were analyzed by ANOVA and Tukey's test at 5% significance level. Tetrachloroethylene was the most effective on conventional gutta-percha (p<0.05). Tetrachloroethylene was also the most effective on thermoplastic gutta-percha, but it was not significantly different (p>0.05) from Eucalyptol+Tetrachloroethylene, Citrol+Tetrachloroethylene, and Citrol. All solvents and associations presented little effectiveness on Resilon. The association Eucalyptol+Tetrachloroethylene was the most effective on EndoREZ, but it did not differ significantly (p>0.05) from Citrol+Tetrachloroethylene and Tetrachloroethylene. All evaluated substances presented solvent action. Tetrachloroethylene improved the effectiveness of both Citrol and Eucalyptol.

Ability of Gutta-Percha and Resilon to Fill Simulated Lateral Canals by Using the Obtura II System

Introduction: The aim of this study was to evaluate the ability of Resilon (Resilon Research, LLC, North Branford, CT) and 2 types of gutta-percha to fill simulated lateral canals when using the Obtura II system (Model 823-700; Obtura Spartan, Fenton, MO). Methods: Forty-five human single-rooted teeth were selected and subjected to root canal preparation. After that, simulated lateral canals were made at 2, 5, and 8 mm from the working length (WL). The specimens were divided into 3 groups (n = 15) according to the filling material used: Obtura Flow 150 gutta-percha (Obtura flow), Odous Endo Flow gutta-percha (Odous; Odous de Deus Ind e Corn. Ltda Belo Horizonte, MG, Brazil), and Resilon pellets (Resilon). Root canals were filled using the Obtura II system with the tip inserted to 3 mm from the WL. No sealer was used for root canal obturation. Specimens were subjected to a tooth decalcification and clearing method, and filling of the lateral canals was analyzed by digital radiography and photographs. The measurement of lateral canal filling was done using Image Tool software (UTHSCSA Image Tool for Windows version 3.0, San Antonio, TX). Data were statistically analyzed with the Kruskal-Wallis test at 5% significance. Results: All materials showed an ability to penetrate into the simulated lateral canals, with a minimum percentage of 73% in all thirds of the root canal. Conclusions: It was concluded that gutta-percha and Resilon are solid core materials with a lateral canal filling ability when used with the Obtura II system. (J Endod 2012;38:676-679)

Análise da termoplasticidade e adesividade da guta-percha e resilon

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Filling of simulated lateral canals with gutta percha or resilon when using thermomechanical compaction

Aims: To evaluate the filling of simulated lateral canals with gutta-percha or Resilon when using thermomechanical compaction. Setting and Design: Forty-five human single-rooted teeth were subjected to tooth decalcification and clearing. Materials and Methods: After root canal preparation, artificial lateral canals were made at 2, 5, and 8 mm from the working length (WL), corresponding to the apical, middle, and cervical thirds, respectively. The specimens were divided (n = 15) according to the filling material: Dentsply gutta-percha (GD), Odous gutta-percha (GO), and Resilon cones (RE). Root canals were obturated by thermomechanical compaction using a #45 compactor and no sealer. Lateral canals were analyzed by digital radiography and digital images after tooth decalcification and clearing using the Image Tool software. Statistical Analysis Used: Data were subjected to the Kruskal-Wallis and Dunn tests at 5% significance. Results: In the coronal third, RE and GO presented more filling ability than GD (P < 0.05). In the middle and apical thirds, RE presented the best results. Conclusions: Resilon demonstrated filling ability as material for root canal obturation by using thermomechanical compaction.

Variability of physicochemical properties of an epoxy resin sealer taken from different parts of the same tube

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Tissue reaction to Endométhasone sealer in root canal fillings short of or beyond the apical foramen

Objective: This study evaluated the response of periapical tissues to the endodontic sealer Endomethasone in root canal fillings short of or beyond the apical foramen. Material and Methods: Twenty root canals of premolars and incisors of 2 mongrel dogs were used. After coronal access and pulp extirpation, the canals were instrumented up to a size 55 K-file and the apical cemental barrier was penetrated with a size 15 K-file to obtain a main apical foramen, which was widened to a size 25 K-file. The canals were irrigated with saline at each change of file. The root canals were obturated either short of or beyond the apical foramen by the lateral condensation of gutta-percha and Endomethasone, originating 2 experimental groups: G1: Endomethasone/short of the apical foramen; G2: Endomethasone/beyond the apical foramen. The animals were killed by anesthetic overdose 90 days after endodontic treatment. The individual roots were obtained and serial histological sections were prepared for histomorphological analysis (H&E and Brown & Brenn techniques) under light microscopy. The following parameters were examined: closure of the apical foramen of the main root canal and apical opening of accessory canals, apical cementum resorption, intensity of the inflammatory infiltrate, presence of giant cells and thickness and organization of the apical periodontal ligament. Each parameter was scored 1 to 4, 1 being the best result and 4 the worst. Data were analyzed statistically by the Wilcoxon nonparametric tests (p=0.05). Results: Comparing the 2 groups, the best result (p<0.05) was obtained with root canal filling with Endomethasone short of the apical foramen but a chronic inflammatory infiltrate was present in all specimens. Conclusions: Limiting the filling material to the root canal space apically is important to determine the best treatment outcome when Endomethasone is used as sealer.

Influence of apical foramen widening and sealer on the healing of chronic periapical lesions induced in dogs' teeth

Objective. The aim of this study was to evaluate the influence of apical foramen widening on the healing of chronic periapical lesions in dogs' teeth after root canal filling with Sealer 26 or Endomethasone.Study design. Forty root canals of dogs' teeth were used. After pulp extirpation, the canals were exposed to the oral cavity for 180 days for induction of periapical lesions, and then instrumented up to a size 55 K-file at the apical cemental barrier. In 20 roots, the cemental canal was penetrated and widened up to a size 25 K-file; in the other 20 roots, the cemental canal was preserved (no apical foramen widening). All canals received a calcium hydroxide intracanal dressing for 21 days and were filled with gutta-percha and 1 of the 2 sealers: group 1: Sealer 26/apical foramen widening; group 2: Sealer 26/no apical foramen widening; group 3: Endomethasone/apical foramen widening; group 4: Endomethasone/no apical foramen widening. The animals were killed after 180 days, and serial histologic sections from the roots were prepared for histomorphologic analysis. Scores were assigned according to preestablished histomorphologic parameters and analyzed statistically by Kruskal-Wallis and Mann-Whitney U tests.Results. Regarding new cementum formation, repair of cementum and bone resorption areas, presence of microorganisms, inflammatory cell infiltrate and periodontal ligament conditions, significantly better periapical healing was obtained when foramen widening was done and Sealer 26 was used.Conclusion. Apical foramen widening and calcium hydroxide-containing sealer were more favorable to the healing of chronic periapical lesions. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2010;109:932-940)

Reaction of rat connective tissue to a new calcium hydroxide-based sealer

The aim of this study was to histopathologically examine the reaction of the connective tissue of rats to 2 calcium hydroxide-based sealers, Acroseal and Sealapex. Dentin tubes containing the materials and empty control tubes were implanted into the dorsal connective tissue of 36 Wistar albino rats. The animals were killed after 7 or 30 days, and the specimens were prepared for histologic analysis with hematoxylin and eosin, Von Kossa technique, and polarized light. Results were statistically analyzed using Kruskal-Wallis test. Both materials caused mild or moderate inflammatory reactions on the 7th day, but these reactions decreased by the 30th day with no significant difference at any time (P > .05). Mineralization of the subcutaneous tissue of the rats was observed only with Sealapex.

A Mineral Trioxide Aggregate Sealer Stimulated Mineralization

The aim of this study was to evaluate the rat subcutaneous tissue response to implanted polyethylene tubes filled with Endo-CPM-Sealer (Portland Cement Modified Sealer) (EGEO S.R.L., Buenos Aires, Argentina) compared with Sealapex (SybronEndo, Glendora, CA) and Angelus MTA (Angelus, Londrina, Brazil). These materials were placed in polyethylene and dentin tubes and implanted into dorsal connective tissue of Wistar rats for 7, 15, 30, 60, and 90 days. The specimens were prepared to be stained with hematoxylin and eosin or Von Kossa or not stained for polarized light. Qualitative and quantitative evaluations of the reaction were performed. Both materials caused mild to moderate reactions at 7 days that decreased with time. The response was similar to the control on the 30th day with Endo-CPM-Sealer and Angelus MTA and on the 60th day with Sealapex. Mineralization and granulations birefringent to the polarized light were observed with all materials. it was possible to conclude that Endo-CPM-Sealer was biocompatible and stimulated mineralization. (J Endod 2009;35:256-260)

Mineral Trioxide Aggregate-based Endodontic Sealer Stimulates Hydroxyapatite Nucleation in Human Osteoblast-like Cell Culture

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Quantification of fibrosis and mast cells in the tissue response of endodontic sealer irradiated by low-level laser therapy

Low-level laser therapy (LLLT) accelerates tissue repair. Mast cells induce the proliferation of fibroblasts and the development of local fibrosis. The objective of this study was to quantify fibrosis rate and mast cells in connective tissue after endodontic sealer zinc oxide and eugenol (ZOE) was implanted and submitted to LLLT, immediately after implant and again 24 h later. Sixty mice were distributed into three groups: GI, GII, and GIII (n = 20). In GI, the tubes filled with Endofill were implanted in the animals and were not irradiated with LLLT. In GII, the tubes containing Endofill were implanted in the animals and then irradiated with red LLLT (InGaAIP) 685-nm wavelength, D=72 J/Cm(2), E = 2 J, T=58 s, P=35 mW, and in GIII, the tubes with Endofill were implanted and irradiated with infrared LLLT (AsGaAl) 830-nm wavelength, D=70 J/Cm(2), E = 2 J, T=40 s, P=50 mW. After 7 days and 30 days, the animals were killed. A series of 6-mu m-thick sections were obtained and stained with Toluidine Blue and Picrosirius and analyzed under a standard light microscope using a polarized light filter for the quantification of fibrosis. The statistics were qualitative and quantitative with a significance of 5%. The irradiation with LLLT did not offer improvement in the fibrosis rate, however, it provided a significant decrease in the concentration of independent mast cells for the period studied.

Effect of red and infrared low-level laser therapy in endodontic sealer on subcutaneous tissue

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

pH, Calcium Ion Release, and Setting Time of an Experimental Mineral Trioxide Aggregate-based Root Canal Sealer

Introduction: An experimental mineral trioxide aggregate sealer (MTAS) has been developed for use as a root canal sealer. The aim of this study was to evaluate the setting time, pH, and calcium ion release of MTAS compared with white Portland cement (CPB-40; Votorantin Cimentos, Camargo Correa SA, Pedro Leopoldo, MG, Brazil), white MTA Angelus (MTA; Angelus, Londrina, PR, Brazil), and AH Plus (Dentsply DeTrey, Konstanz, Germany). Methods: For the evaluation of setting time, each material was analyzed using Gilmore-type needles. Polyethylene tubes with the materials were immersed in distilled water for the measurement of pH (digital pH meter) and calcium release (atomic absorption spectrophotometry). The evaluations were performed at 3, 6, 12, 24, and 48 hours and 7, 14, and 28 days. Data were analyzed by analysis of variance and the Tukey test at 5% significance level. Results: MTAS showed higher calcium release at all experimental periods, a greater increase in pH up to 48 hours and the longest setting time. Conclusions: MTAS presented favorable properties for its indication as a root canal sealer. (J Endod 2011;37:844-846)