Resolution of a titanium implant fracture after a recurrent trauma

Post-traumatic complications occasionally lead to tooth loss as well as the need for future implants. However, rehabilitation with endosseous osseointegrated implants does not protect the patient from the risk of suffering a new trauma. Implant fracture and the damage of the hexagon are post-traumatic complications that guide the clinician to preparing a more intricate treatment plan. The authors present a clinical case of a recurrent trauma of maxillary implant fracture. The treatment plan was to remove the implants followed by autogenous bone grafting to correct the defect. Two titanium implants were replaced, followed by connective tissue graft after allowing complete the healing process of the bone graft to occur. In the postoperative period of 6 months, satisfactory results have been shown as regards soft and hard tissues wound healing.

Osseointegrated Implant Fracture: Causes and Treatment

Despite its high success rate, therapy with osseointegrated dental implants is not free of complications. Among the problems that may occur is fracture of implants, which, albeit a rare phenomenon, may lead to unpleasant clinical outcomes for the patient, as well as for the clinician. Thus, it is paramount to know the factors related to the biological processes involved in maintenance of osseointegration and biomechanics applied to dental implants to prevent such complications, as well as treatment options available to deal with the problem. Therefore, the objectives of this work were to investigate the literature to identify causative factors that may lead to fracture of dental implants and to discuss available procedures.

BMP implant associated with platelet-rich plasma in orbit fracture repair

Purpose: To evaluate a bone morphogenetic protein (BMP) implant with and without platelet-rich plasma (PRP), which is supposed to accelerate fracture consolidation in the orbit fracture treatment. Methods: Thirty-six white rabbits were subjected to orbital fracture and treated in three groups: BMP implant fracture repair (G1), BMP plus PRP implant fracture repair (G2), and fracture and spontaneous repair (G3). The animals were sacrificed at 7, 30, 90, and 180 days after surgery. A radiology evaluation was carried out on the 7th day after the fracture and at the sacrifice moments. After the animals' death, the orbital content material was removed and prepared for morphological and morphometric analysis. Results: Radiology suggested intramembranous and progressive cavitation and ossification without a reduction in implant size and with signs of calcium deposition; these events were confirmed by histological analysis, which showed a lymphomononuclear inflammatory reaction in G1 and G2, more intense 7 days after surgery and reducing after 30 days. Associating PRP with BMP did not accelerate bone induction. Conclusion: BMP implant promotes bone induction, integration at fracture site, scarce inflammatory reaction, and may be a good alternative in orbit fracture reconstruction. The addition of PRP to the BMP plate did not accelerate the resolution, and its use is not necessary. Copyright © Informa Healthcare USA, Inc.

Dental implant fractures: aetiology, treatment and case report

Purpose: This study aimed to investigate the etiology, clinical manifestations, and treatment options of dental implants fractures through a literature review and to relate a clinical report. Methods: A literature review was performed using the Medline database and this paper describes a case demonstrating the management of implant fracture. Twenty two articles were selected in the present literature review. Results: Nowadays the use of dental implants to rehabilitate completely and partially edentulous patients became the best treatment option; however, this treatment is suitable to failure. The fracture of implant body is a possible complication. The fracture of implant body is a late complication and is related to the failure in implant design or material, non-passive fitting of the prosthetic crown and overloading. Clinically, prosthesis instability and spontaneous bleeding are observed. Three options of treatment have been indicated: complete removal of implant fragment, maintenance of implant fragment, and surface preparation of the fragment with insertion of a new abutment. Conclusion: The literature indicates the complete removal of the fragment as the best treatment option.

Estudo comparativo do Titânio versus Polímero vegetal para fixação interna rígida de fraturas orbitárias de coelhos

Pós-graduação em Bases Gerais da Cirurgia - FMB

THE EFFECT of E-GLASS FIBERS and ACRYLIC RESIN THICKNESS on FRACTURE LOAD IN A SIMULATED IMPLANT-SUPPORTED OVERDENTURE PROSTHESIS

Statement of problem. Implant overdenture prostheses are prone to acrylic resin fracture because of space limitations around the implant overdenture components.Purpose. The purpose of this study was to evaluate the influence of E-glass fibers and acrylic resin thickness in resisting acrylic resin fracture around a simulated overdenture abutment.Material and methods. A model was developed to simulate the clinical situation of an implant overdenture abutment with varying acrylic resin thickness (1.5 or 3.0 mm) with or without E-glass fiber reinforcement. Forty-eight specimens with an underlying simulated abutment were divided into 4 groups (n=12): 1.5 mm acrylic resin without E-glass fibers identified as thin with no E-glass fiber mesh (TN-N); 1.5 mm acrylic resin with E-glass fibers identified as thin with E-glass fiber mesh (TN-F); 3.0 mm acrylic resin without E-glass fibers identified as thick without E-glass fiber mesh (TK-N); and 3.0 mm acrylic resin with E-glass fibers identified as thick with E-glass fiber mesh (TK-F). All specimens were submitted to a 3-point bending test and fracture loads (N) were analyzed with a 2-way ANOVA and Tukey's post hoc test (alpha=.05).Results. The results revealed significant differences in fracture load among the 4 groups, with significant effects from both thickness (P<.001) and inclusion of the mesh (P<.001). Results demonstrated no interaction between mesh and thickness (P=.690). The TN-N: 39 +/- 5 N; TN-F: 50 +/- 6.9 N; TK-N: 162 +/- 13 N; and TK-F: 193 +/- 21 N groups were all statistically different (P<.001).Conclusions. The fracture load of a processed, acrylic resin implant-supported overdenture can be significantly increased by the addition of E-glass fibers even when using thin acrylic resin sections. on a relative basis, the increase in fracture load was similar when adding E-glass fibers or increasing acrylic resin thickness. (J Prosthet Dent 2011;106:373-377)

Incomplete mandibular fracture after lateralization of the inferior alveolar nerve for implant placement

PURPOSE: The present case describes an inferior alveolar nerve lateralization for implant placement that caused mandible fracture a few days after surgery. CLINICAL REPORT: In this case, a 56-year-old female patient who had a severely atrophied jaw and showing bone height less than 7 mm from the bone crest and the mandibular canal was submitted to surgery lateralization of the inferior alveolar conducted with piezzo. Even with all postoperative care, the patient suffered an incomplete fracture of the mandible a few days after lateralization of the inferior alveolar nerve for implant placement. The patient was treated with soft diet and medications for pain and antibiotics, besides removing the implant associated with the fracture. CONCLUSION: It is suggested that this procedure may be conducted in 2 operative periods: firstly, the lateralization of the inferior alveolar; and secondly, after a period of 3 months, the implant placement in a situation of more bone stability. Copyright © 2013 by Mutaz B. Habal, MD.

Aesthetic rehabilitation of a complicated crown-root fracture of the maxillary incisor: combination of orthodontic and implant treatment

The aim of this paper is to present a complex rehabilitation, of fractured tooth, with implants in anterior region considering the orthodontics extrusion to clinical success. At 7 years old, the patient fractured the maxillary left central incisor and the dentist did a crown with the fragment. Twenty years later, the patient was referred to a dental clinic for orthodontic treatment, with the chief complaint related to an accentuated deep bite, and a professional started an orthodontic treatment. After sixteen months of orthodontic treatment, tooth 21 fractured. The treatment plan included an orthodontic extrusion of tooth 21 and implant placement. This case has been followed up and the clinical and radiographic examinations show excellence esthetic results and satisfaction of patient. The forced extrusion can be a viable treatment option in the management of crown root fracture of an anterior tooth to gain bone in a vertical direction. This case emphasizes that to achieve the esthetic result a multidisciplinary approach is necessary.

Effect of implant connection and restoration design (screwed vs. cemented) in reliability and failure modes of anterior crowns

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

THE SERVICE LIFE of IMPLANT-RETAINED OVERDENTURE ATTACHMENT SYSTEMS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In Vitro Study of Fracture Load and Fracture Pattern of Ceramic Crowns: A Finite Element and Fractography Analysis

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Mechanical Strength and Analysis of Fracture of Titanium Joining Submitted to Laser and Tig Welding

This study compared the tensile strength and fracture mechanism of tungsten inert gas (TIG) welds in cylindrical rods of commercially pure titanium (cp Ti) with those of laser welds and intact samples. Thirty dumbbell-shaped samples were developed by using brass rods as patterns. The samples were invested in casings, subjected to thermal cycles, and positioned in a plasma arc welding machine under argon atmosphere and vacuum, and titanium was injected under vacuum/pressure. The samples were X-rayed to detect possible welding flaws and randomly assigned to three groups to test the tensile strength and the fracture mechanism: intact, laser welding, and TIG welding. The tensile test results were investigated using ANOVA, which indicated that the samples were statistically similar. The fracture analysis showed that the cpTi samples subjected to laser welding exhibited brittle fracture and those subjected to TIG welding exhibited mixed brittle/ductile fracture with a predominance of ductile fracture with the presence of microcavities and cleavage areas. Intact samples presented the characteristic straightening in the fracture areas, indicating the ductility of the material.

Histomorphometric evaluation of a threaded, sandblasted, acid-etched implant retrieved from a human lower jaw: A case report

The purpose of this study was to histomorphometrically evaluate the bone-to-implant contact and bone area around a titanium implant retrieved from a human lower jaw. A screw-shaped titanium implant (sandblasted and acid-etched surface) was removed from a 68-year-old male after having been in function for 40 months because of a fracture of the abutment screw. Following the implant removal, an undecalcified section was obtained. The histomorphometric analysis showed a rate of 75.40% of bone-to-implant contact and 89.30% of bone area filling within the limits of the implant threads. The surrounding bone healed in a well-organized pattern and could not be differentiated from the anginal alveolus. The histologic evidence showed a high degree of osseointegration in a threaded, sandblasted, and acid-etched implant retrieved from a human lower jaw after functional loading for 40 months. Copyright © 2005 by Lippincott Williams & Wilkins.

Biomechanical effect of one session of low-level laser on the bone-titanium implant interface

Low-level laser (LLL) has been used on peri-implant tissues for accelerating bone formation. However, the effect of one session of LLL in the strength of bone-implant interface during early healing process remains unclear. The present study aims to evaluate the removal torque of titanium implants irradiated with LLL during surgical preparation of implant bed, in comparison to non-irradiation. Sixty-four Wistar rats were used. Half of the animals were included in LLL group, while the other half remained as control. All animals had the tibia prepared with a 2 mm drill, and a titanium implant (2.2 × 4 mm) was inserted. Animals from LLL group were irradiated with laser (gallium aluminum arsenide), with a wavelength of 808 nm, a measured power output of 50 mW, to emit radiation in collimated beams (0.4 cm2), for 1 min and 23 s, and an energy density of 11 J/cm2. Two applications (22 J/cm 2) were performed immediately after bed preparation for implant installation. Flaps were sutured, and animals from both groups were sacrificed 7, 15, 30, and 45 days after implant installation, when load necessary for removing implant from bone was evaluated by using a torquimeter. In both groups, torque values tended to increase overtime; and at 30 and 45 days periods, values were statistically higher for LLL group in comparison to control (ANOVA test, p < 0.0001). Thus, it could be suggested that a single session of irradiation with LLL was beneficial to improve bone-implant interface strength, contributing to the osseointegration process. © 2012 Springer-Verlag London Ltd.