Dynamical Elastic Moduli of the Ti-13Nb-13Zr biomaterial alloy by mechanical spectroscopy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Corrosion resistance enhancement of SAE 1020 steel after Chromium implantation by nitrogen ion recoil

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of electroless nickel interlayer on the fatigue strength of chromium electroplated AISI 4340 steel

Deposition of wear-resistant hard chromium plating leads to a decrease in the fatigue strength of the base material. Despite the effective protection against wear and corrosion, fatigue life and environmental requirements result in pressure to identify alternatives or to improve conventional chromium electroplating mechanical characteristics. An interesting, environmentally safer and cleaner alternative for the replacement of hard chronic plating is tungsten carbide thermal spray coating, applied by high velocity oxyfuel (HVOF) process.To improve the fatigue strength of aeronautical steel chromium electroplated, shot peening is a successfully used method. Multiple lacer systems of coatings are considered to have larger resistance to crack propagation in comparison with simple layer.The aim of this study was to analyze the effect of nickel underplate on the fatigue strength of hard chromium plated AISI 4340 steel in two mechanical conditions: HRc 39 and HRc 52.Rotating bending fatigue tests results indicate that the clectroless nickel plating underlayer is responsible for the increase in fatigue strength of AISI 4340 steel chromium electroplated. This behavior may be attributed to the largest toughness/ductility and compressive residual stresses which, probably, arrested or delayed the inicrocrack propagation from the hard chromium external layer. The compressive residual stress field (CRSF) induced by the electroplating process was determined by X-ray diffraction method. The evolution of fatigue strength compressive residual stress field CRSF and crack sources are discussed and analyzed by SEM. (c) 2006 Elsevier Ltd. All rights reserved.

Quantitative fractography under light microscopy: A digital image processing approach

This work is an example of the improvement on quantitative fractography by means of digital image processing and light microscopy. Two techniques are presented to investigate the quantitative fracture behavior of Ti-4Al-4V heat-treated alloy specimens, under Charpy impact testing. The first technique is the Minkowski method for fractal dimension measurement from surface profiles, revealing the multifractal character of Ti-4Al-4V fracture. It was not observed a clear positive correlation of fractal values against Charpy energies for Ti-4Al-4V alloy specimens, due to their ductility, microstructural heterogeneities and the dynamic loading characteristics at region near the V-notch. The second technique provides an entire elevation map of fracture surface by extracting in-focus regions for each picture from a stack of images acquired at successive focus positions, then computing the surface roughness. Extended-focus reconstruction has been used to explain the behavior along fracture surface. Since these techniques are based on light microscopy, their inherent low cost is very interesting for failure investigations.

Caracterização mecânica e microestrutural de um aço baixo carbono microligado com estrutura multifásica

Neste trabalho foi realizada a caracterização mecânica e microestrutural de um aço microligado com estrutura multifásica. Foi aplicado tratamento térmico pré-determinado, objetivando a formação de uma microestrutura multifásica no material. Na caracterização microestrutural foram utilizados ataques químicos à base de metabissulfito de sódio e ácido pícrico, enquanto a caracterização mecânica foi realizada através de ensaios de tração. Os resultados demonstram o elevado potencial dos aços multifásicos em aplicações que necessitem de valores superiores de resistência e ductilidade, pois tanto para temperatura isotérmica de 400ºC quanto para 350ºC houve um ganho no limite de resistência à tração ficando em torno de 786MPa e 773MPa respectivamente, representando um aumento de 15,5% e 13,6% com relação ao material fornecido.

Mechanical Strength and Analysis of Fracture of Titanium Joining Submitted to Laser and Tig Welding

This study compared the tensile strength and fracture mechanism of tungsten inert gas (TIG) welds in cylindrical rods of commercially pure titanium (cp Ti) with those of laser welds and intact samples. Thirty dumbbell-shaped samples were developed by using brass rods as patterns. The samples were invested in casings, subjected to thermal cycles, and positioned in a plasma arc welding machine under argon atmosphere and vacuum, and titanium was injected under vacuum/pressure. The samples were X-rayed to detect possible welding flaws and randomly assigned to three groups to test the tensile strength and the fracture mechanism: intact, laser welding, and TIG welding. The tensile test results were investigated using ANOVA, which indicated that the samples were statistically similar. The fracture analysis showed that the cpTi samples subjected to laser welding exhibited brittle fracture and those subjected to TIG welding exhibited mixed brittle/ductile fracture with a predominance of ductile fracture with the presence of microcavities and cleavage areas. Intact samples presented the characteristic straightening in the fracture areas, indicating the ductility of the material.

Fadiga em dormentes de concreto reforçados com fibras de aço

A prestressed concrete monoblock railroad tie was designed to attend the characteristics of a Brazilian railroad track with 1,600 mm gauge and 320 kN axle load. Concrete ties specimens were manufactured without and with steel fibers in a volume fraction of 60 kg/m3 (0.76 % by volume), and three different initial prestress forces. Static and fatigue tests were carried out on the ties. Static tests showed that steel fibers increase the first crack and ultimate bending moments, increase significantly the slip force of the prestressing tendons, reduce crack width, add higher ductility to the ties and decrease the stress in the prestressing tendons. Under dynamic loading the steel fibers decreased the stress in the prestressing tendons by about 50%, which improved significantly the fatigue strength of the tie. A tie without fibers failed after only 150,000 cycles. However, a similar tie, with fibers, resisted 3,000,000 cycles without suffering fatigue failure.

Rectificacion de aceros fragiles y ductiles: Parametros de entrada para obtener los mejores resultados

In this work, the behavior of the steel surface grinding process with conventional grinding wheels was studied for various grinding conditions and a fixed dressing condition. The input parameters (wheel speed, workpiece speed, depth of cut), that set up the grinding conditions were determined as a function of the characteristics of the grinding machine. A test bench was established where the grinding power was measured in real time as a function of the volume of material removed. The results showed that in the grinding of fragile steels with a soft wheel and medium grit size, the average power of the cut shows a tendency to increase and become stabilized. The surface roughness of the piece decreased in all the tests and was proportional to the increase in the number of active grits. In tests on the grinding of ductile steels with a soft wheel and fine grit size, the wheel became dull until the moment that the abrasive grits were released from the cut surface.

Stacking faults in SiCf/SiC composite obtained by chemical vapor reaction process

SiC fiber-reinforced SiC matrix composite (SiCf/SiC) is one of the leading candidates in ceramic materials for engineering applications due to its unique combination of properties such as high thermal conductivity, high resistance to corrosion and working conditions. Fiber-reinforced composites are materials which exhibit a significant improvement in properties like ductility in comparison to the monolithic SiC ceramic. The SiCf/SiC composite was obtained from a C/C composite precursor using convertion reaction under high temperature and controlled atmosphere. In this work, SiC phase presented the stacking faults in the structure, being not possible to calculate the unit cell size, symmetry and bond lengths but it seem equal card number 29-1129 of JCPDS.

Dependência estrutural da capacidade de rotação plástic em vigas de concreto armado

Summary In this work the structural dependence of plastic rotation capacity in RC beams is evaluated using the Finite Element Method. The objective is to achieve a better understanding of the non-linear behavior of reinforced concrete members and perform extensive parameter studies, using a rational model developed by Bigaj [1] to analyze the phenomenon of plastic rotation capacity in reinforced concrete members. It is assumed that only bending failure is relevant due to sufficient member resistance against shear and torsion. The paper begins with the physical and theoretical background of the phenomenon of plastic hinge development in RC structures. Special emphasis is laid on the issue of structural dependence of deformation capacity of plastic hinges in RC members. Member size dependence and influence of properties of construction materials were emphasized as well. The essential components of the Bigajs model for calculating the plastic rotation capacity are discussed. The behaviour of the plastic hinge is analysed taking into account the strain localisation in the damage zones of the hinge region. The Fictitious Crack Model (FCM) and the Compressive Damage Zone Model (CDZ) are adopted in a Fracture Mechanics approach to model the behaviour of concrete in tension and compression, respectively. The approach is implemented in FEMOOP, a FEM in-house solver under development, and applied to evaluate ductility in 2D beams. The models were generated with GiD, a pre-processor and post-processor developed by CIMNE, and analyzed with the capabilities implemented in FEMOOP. © Universitat Politècnica de Catalunya, Barcelona, España 2010.

Design of biogas pipeline - Energy and sanitation

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Análise numérica da ductilidade de vigas de concreto armado convencional e de alto desempenho

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Caracterização microestrutural de um aço baixo carbono e baixos teores de elementos de ligas com estrutura contento ferrita acicular

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A influência da deformação plástica sobre a estabilidade mecânica da Austenita retida em aços 300M

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)