DNA Psi-condensation and reentrant decondensation: Effect of the PEG degree of polymerization

psi-Condensation of DNA fragments of about 4 kbp was induced by poly(ethylene glycol) (PEG), with degrees of polymerization ranging from 45 to 182, and univalent salt (NaCl). Using circular dichroism spectroscopy, we were able to accurately determine the critical amount of PEG needed to induce condensation, as a function of the NaCl concentration. A significant dependence on the PEG degree of polymerization was found. Phase boundaries determined for the multimolecular condensation were very similar to those observed previously for the monomolecular collapse, with two asymptotic regimes at low and high salt concentrations. We analyze our data using a theoretical model that properly takes into account both the polyelectrolyte nature of the DNA and the liquid crystallinity of the condensed phase. The model assumes that all PEG is excluded from the condensates and shows reentrant decondensation only at low salt. We also systematically study reentrant decondensation and find a very strong dependence on PEG molecular weight. At low PEG molecular weight, decondensation occurs at relatively low concentrations of PEG, and over a wide range of salt concentrations. This suggests that in the reentrant decondensation the flexible polymers used are not completely excluded from the condensed phase.

Exothermic Behavior, Degree of Conversion, and Viscoelastic Properties of Experimental and Commercially Available Hard Chairside Reline Resins

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis and characterization of microcrystalline cellulose produced from bacterial cellulose

In this study, microcrystalline cellulose (MCC) was prepared from the acid hydrolysis of bacterial cellulose (BC) produced in culture medium of static Acetobacter xylinum. The MCC-BC produced an average particle size between 70 and 90 mu m and a degree of polymerization (DP) of 250. The characterization of samples was performed by thermogravimetric analysis, X-ray diffraction, and scanning electron microscopy (SEM). The MCC shows a lower thermal stability than the pristine cellulose, which was expected due to the decrease in the DP during the hydrolysis process. In addition, from X-ray diffractograms, we observed a change in the crystalline structure. The images of SEM for the BC and MCC show clear differences with modifications of BC fiber structure and production of particles with characteristics similar to commercial MCC.

Structural characterization of a new dextran with a low degree of branching produced by Leuconostoc mesenteroides FT045B dextransucrase

This paper offers the physical and chemical characterization of a new dextran produced by Leuconostoc mesenteroides FT045B. The chemical structure was determined by Fourier Transform Infrared spectroscopy and 1H Nuclear Magnetic Resonance spectroscopy. The dextran was hydrolyzed by endodextranase; the products were analyzed using thin layer chromatography and compared with those of commercial B-512F dextran. The number-average molecular weight and degree of polymerization of the FT045B dextran were determined by the measurement of the reducing value using the copper bicinchoninate method and the measurement of total carbohydrate using the phenol-sulfuric acid method. The data revealed that the structure of the dextran synthesized by FT045B dextran sucrase is composed of d-glucose residues, containing 97.9% α-(1,6) linkages in the main chains and 2.1% α-(1,3) branch linkages compared with the commercial B-512F dextran, which has 95% α-(1,6) linkages in the main chains and 5% α-(1,3) branch linkages. © 2012 Elsevier Ltd. All rights reserved.

Production of β-(1,3)-glucanases by Trichoderma harzianum Rifai: Optimization and Application to Produce Gluco-oligosaccharides from Paramylon and Pustulan

β-(1→3)-Glucanases were produced by Trichoderma harzianum Rifai PAMB-86 cultivated on botryosphaeran in a bench-fermenter and optimised by the response surface method. Maximal enzyme titres occurred at 5 days, initial pH 5.5 and aeration of 1.5vvm. β-(1→3)-The β-glucanolytic enzyme complex produced by T. harzianum Rifai PAMB- 86 was fractionated by gel filtration into 2 fractions (F-I, F-II), and employed to produce gluco-oligosaccharides from algal paramylon ((1→3)-β-D-glucan) and lichen pustulan ((1→6)-β-D-glucan). Both enzymes attacked paramylon to the extent of ~15-20% in 30 min releasing glucose and laminaribiose as major end-products, and laminarioligosaccharides of degree of polymerization (DP) ≥3. Only F-I degraded pustulan resulting in ~2% degradation at 30 min, with glucose, gentiobiose and gentio-oligosaccharides of DP ≥4 as major products. The difference in the nature of the hydrolysis products can be explained by the substrate specificities of each enzyme fraction, and the structural differences of the β-D-glucans attacked.

Effect of water-bath post-polymerization on the mechanical properties, degree of conversion, and leaching of residual compounds of hard chairside reline resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of different light sources and photo-activation methods on degree of conversion and polymerization shrinkage of a nanocomposite resin

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Degree of conversion and molecular weight of one denture base and three reline resins submitted post-polymerization treatments

The effect of post-polymerization treatments (MW-microwave irradiatron and WB-water-bath) on the degree of conversion (DC) of three reline resins (Ufi Gel hard-U, Kooliner-K, and Tokuso Rebase Fast-T) and one denture base resin (Lucitone 550-L), submitted to two polymerization cycles (LS-short and LL-long), was evaluated by using FT-Raman spectroscopy (n = 5). The molecular weight (Mw) of the powder of all materials and of K polymerized specimens (control; MW; and WB; n = 3) was analyzed using GPC. DC data were analyzed using Kruskal-Wallis test (α = .05). For control specimens, there were no significant differences between U (68%) and LL (77%) and among LL, K (81%), and T (84%). LS (92%) had the highest DC (P<0.05). Only material K exhibited an increased DC after WB (P<0.05). All powders had Mw from 4.0 × 105 to 6.5 × 105 and narrow Mw distributions (2.1 to 3.6). Polymerization and post-polymerization produced K specimens with Mw similar to that of K powder.

The effect of polymerization mode on monomer conversion, free radical entrapment, and interaction with hydroxyapatite of commercial self-adhesive cements

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Conversion Degree of Indirect Resin Composites and Effect of Thermocycling on Their Physical Properties

Purpose: This study evaluated the degree of conversion (DC) of four indirect resin composites (IRCs) with various compositions processed in different polymerization units and investigated the effect of thermal aging on the flexural strength and Vicker's microhardness.Materials and Methods: Specimens were prepared from four IRC materials, namely Gr 1: Resilab (Wilcos); Gr2: Sinfony (3M ESPE); Gr3: VITA VMLC (VITA Zahnfabrik); Gr4: VITA Zeta (VITA Zahnfabrik) using special molds for flexural strength test (N = 80, n = 10 per group) (25 x 2 x 2 mm(3), ISO 4049), for Vicker's microhardness test (N = 80, n = 10 per group) (5 x 4 mm(2)) and for DC (N = 10) using FT-Raman Spectroscopy. For both flexural strength and microhardness tests, half of the specimens were randomly stored in distilled water at 37 degrees C for 24 hours (Groups 1 to 4), and the other half (Groups 5 to 8) were subjected to thermocycling (5000 cycles, 5 to 55 +/- 1 degrees C, dwell time: 30 seconds). Flexural strength was measured in a universal testing machine (crosshead speed: 0.8 mm/min). Microhardness test was performed at 50 g. The data were analyzed using one-way and two-way ANOVA and Tukey's test (alpha = 0.05). The correlation between flexural strength and microhardness was evaluated with Pearson's correlation test (alpha = 0.05).Results: A significant effect for the type of IRC and thermocycling was found (p = 0.001, p = 0.001) on the flexural strength results, but thermocycling did not significantly affect the microhardness results (p = 0.078). The interaction factors were significant for both flexural strength and microhardness parameters (p = 0.001 and 0.002, respectively). Thermocycling decreased the flexural strength of the three IRCs tested significantly (p < 0.05), except for VITA Zeta (106.3 +/- 9.1 to 97.2 +/- 14 MPa) (p > 0.05) when compared with nonthermocycled groups. Microhardness results of only Sinfony were significantly affected by thermocycling (25.1 +/- 2.1 to 31 +/- 3.3 Kg/mm(2)). DC values ranged between 63% and 81%, and were not significantly different between the IRCs (p > 0.05). While a positive correlation was found between flexural strength and microhardness without (r = 0.309) and with thermocycling (r = 0.100) for VITA VMLC, negative correlations were found for Resilab under the same conditions (r = -0.190 and -0.305, respectively) (Pearson's correlation coefficient).Conclusion: Although all four IRCs presented nonsignificant DC values, flexural strength and microhardness values varied between materials with and without thermocycling.

Maturity degree of composts from municipal solid wastes evaluated by differential scanning calorimetry

Differential scanning calorimetry (DSC) in association with chemical analysis was applied to assess the maturity reached by the organic fraction of Municipal Solid Wastes (MSW) subjected to composting processes with manual and fixed aeration and sampled at different composting times. Thermograms showed that the difference in the treatments, i.e., the manual aeration and the fixed aeration, had no relevant effect on the stabilization and maturation of OM in the substrates. Common thermal effects observed were: a low temperature endotherm assigned to dehydration and/or loss of peripheral polysaccharides chains; a medium temperature exotherm assigned to loss of peptidic structures, and a high temperature exotherm assigned to oxydation and polycondensation of aromatic nuclei of the molecule. Results obtained suggest that in the experimental conditions used, a shorter time of composting (about 30 d) appears adequate, in order to limit the extended mineralization of OM, whereas a prolonged composting time (up to 132 d) would produce a compost of poor quality with high ash content and low OM content.

Changes on degree of conversion of dual-cure luting light-cured with blue LED

The indirect adhesive procedures constitute recently a substantial portion of contemporary esthetic restorative treatments. The resin cements have been used to bond tooth substrate and restorative materials. Due to recently introduction of the self-bonding resin luting cement based on a new monomer, filler and initiation technology has become important to study the degree of conversion of these new materials. In the present work the polymerization reaction and the filler content of dual-cured dental resin cements were studied by means of infra-red spectroscopy (FT-IR) and thermogravimetry (TG). Twenty specimens were made in a metallic mold (8 mm diameter × 1 mm thick) from each of 2 cements, Panavia® F2.0 (Kuraray) and RelyX™ Unicem Applicap (3M/ESPE). Each specimen was cured with blue LED with power density of 500 mW/cm 2 for 30 s. Immediately after curing, 24 and 48 h, and 7 days DC was determined. For each time interval 5 specimens were pulverized, pressed with KBr and analyzed with FT-IR. The TG measurements were performed in Netzsch TG 209 under oxygen atmosphere and heating rate of 10°C/min from 25 to 700°C. A two-way ANOVA showed DC (%) mean values statistically significance differences between two cements (p < 0.05). The Tukey's test showed no significant difference only for the 24 and 48 h after light irradiation for both resin cements (p > 0.05). The Relx-Y™ Unicem mean values were significantly higher than Panavia® F 2.0. The degree of conversion means values increasing with the storage time and the filler content showed similar for both resin cements. © 2009 Pleiades Publishing, Ltd.

Degree of conversion of polymer-matrix composite assessed by FTIR analysis

Aims and objectives: The behavior of polymer-matrix composite is dependent on the degree of conversion. The aim of this study was to evaluate the degree of conversion of two resin cements following storage at 37°C immediately, 24 and 48 hours, and 7 days after light-curing by FTIR analysis. Materials and methods: The specimens were made in a metallic mold and cured with blue LED with power density of 500 mW/cm2 for 30 seconds. The specimens were pulverized, pressed with KBr and analyzed with FTIR following storage times. Statistical analysis used: ANOVA (two-way) and Tukey's post hoc. Results: To the polymer-matrix composites between 24 and 48 hours does not show a significant increase (p > 0.05), however, the highest values were found after 7 days. Conclusion: The polymer-matrix composites used in this study showed similarity on the degree of conversion and increased of according to the time of storage.

Effect of ceramic shade on the degree of conversion of a dual-cure resin cement analyzed by FTIR

Objectives: The aim of this research was to evaluate the degree of monomer conversion of different resin cement shades when photocured under different feldspathic ceramic shades. The photocuring time was also evaluated as well as the translucency of each ceramic shade. Methods: Three VITA VM7 ceramic shades (Base Dentin 0M1, Base Dentin 2M2 and Base Dentin 5M3) were used to determine the translucency percentage. A spectrophotometer MiniScan was used to measure the opacity percentage of each specimen (2-mm-thick) and then the translucency was calculated. To measure the degree of conversion (DC), the resin cement (Variolink II; A3 Yellow and transparent) specimens (thickness: 100 μm) were photocured under a ceramic block (2-mm-thick) for 20 or 40 s. Specimens photocured without the ceramic block were used as control. Sixteen groups (n = 3) were evaluated. Micro-ATR/FTIR spectrometry was used to evaluate the extent of polymerization of all specimens after 24 h. The %DC was calculated of experimentally polymerized versus maximally polymerized composite. Results: The translucency percentages of 0M1, 2M2 and 5M3 ceramics were 12.41 (1.02)%, 5.75 (1.91)% and 1.07 (0.03)%, respectively. The %DC of both resin cement shades cured under ceramic 5M3 was significantly lower than the other groups (p < 0.05). The %DC of 0M1 groups exhibited no significant difference from 2M2 groups (p > 0.05), with the exception of the transparent cement photocured for 40 s. Conclusion: Photocuring under 2 mm ceramic showed that the increase in chroma saturation significantly decreased Variolink II resin cement %DC (100-μm-thick). © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Evaluation of degree of conversion and hardness of dental composites photoactivated with different light guide tips

Objective: The aim of this study was to evaluate the degree of conversion and hardness of different composite resins, photo-activated for 40 s with two different light guide tips, fiber optic and polymer. Methods: Five specimens were made for each group evaluated. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm-1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm-1. The Vickers hardness measurements were performed in a universal testing machine. A 50 gf load was used and the indenter with a dwell time of 30 seconds. The degree of conversion and hardness mean values were analyzed separately by ANOVA and Tukey's test, with a significance level set at 5%. Results: The mean values of degree of conversion for the polymer and fiber optic light guide tip were statistically different (P<.001). The hardness mean values were statistically different among the light guide tips (P<.001), but also there was difference between top and bottom surfaces (P<.001). Conclusions: The results showed that the resins photo-activated with the fiber optic light guide tip promoted higher values for degree of conversion and hardness.