Physical and mechanical properties of thermally modified wood from E. grandis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of different drying methods on tbe rheological properties of raisins

The rheological parameters of raisins were obtained after three different drying methods: convective, osmo-convective and solar drying. Compression tests were applied to rehydrated samples by using a Texture Analyzer TAXT2i. A mathematical trick was used to determine the stress and area was calculated along the deformation. A power law model could adequately fit stress-true strain curves and parameters; K (measure of stiffness) and n (solid behavior index) were obtained as a function of water activity between 0.755 to 0.432. Results showed that these parameters were strongly dependent on water activity for all drying methods. The constant K, which indicates the resistance against deformation, increased with decreasing water activity. on the other hand, increasing water activity resulted in higher solid behavior indexes, showing a large deviation from the Hookean behavior.

Compressive fatigue in titanium dental implants submitted to fluoride ions action

The aim of this study was to assess the influence of a fluoridated medium on the mechanical properties of an internal hexagon implant-abutment set, by means of compression, mechanical cycling and metallographic characterization by scanning electronic microscopy. Five years of regular use of oral hygiene with a sodium fluoride solution content of 1500 ppm were simulated, immersing the samples in this medium for 184 hours, with the solutions being changed every 12 hours. Data were analyzed at a 95% confidence level with Fisher's exact test. After the action of fluoride ions, a negative influence occurred in the mechanical cycling test performed in a servohydraulic machine (Material Test System-810) set to a frequency of 15 Hz with 100,000 cycles and programmed to 60% of the maximum resistance of static compression test. The sets tended to fracture by compression on the screw, characterized by mixed ruptures with predominance of fragile fracture, as observed by microscopy. An evidence of corrosion by pitting on sample surfaces was found after the fluoride ions action. It may be concluded that prolonged contact with fluoride ions is harmful to the mechanical properties of commercially pure titanium structures.

Hindlimb unloading producing effects on bone biomechanical properties in mature male rats

Aging is associated with decline in muscle mass and strength and reduced bone density. Age-related bone loss is a primary factor in osteoporosis and all individuals are potential candidates for osteoporosis because bone loss with aging occurs in men and women, but less studied in men. To examine the appropriateness of hindlimb elevation, by tail suspension as a model for diminished mechanical loading, and to determine the influence of age on bone responsiveness to skeletal unloading, we use dual X ray absorptiometry (DXA) and digital radiographic images to analyze the response of the femur from mature rats to biomechanical loads. Femurs from male Wistar rats (9-mo-old) were scanned using DXA and DIGORA and measures obtained in ephipyseal and diaphyseal regions of interest. The mechanical testing was divided into compression load to fracture the head and a three-point bending load to fracture the femur middiaphysis. In femoral epiphysis from hindlimb unload (HU), animals presented significant differences between mineral bone content and density assessed by DXA. Detailed regions of femoral epiphysis (head, throcanteric fossa, throcanter and metaphysis) presented significant lower values from radiographic density. Only compressive load necessary to fracture the femoral head neck was also significantly diminished in HU animals. Disuse induced, as in elderly patients, deterioration of the trabecular bone architecture with critical effect on bone fragility. Rats with 21 days of hindlimb unloading can simulate disuse, suggesting that certain sub-regions of their aging bones are more susceptible to fracture, while other, i.e. diaphyses, are not.

Evolution of the mechanical properties of a tropical soil stabilized with lime and ash of rice rind

The ash of rice rind is a pozzolanic material that reacts with the calcium hydroxide (Ca (OH)2) forming bonding composites, when finely worn out and in water presence. Considering this behavior, the objective of the present work was to evaluate the potential use of this residue in the enrichment of the content of pozzolanic materials of a tropical soil stabilized with a commercial hydrated lime. The laboratory testing program incorporated unconfined compression strength tests performed on the soil and on its mixtures with contents of 8% of lime enriched with 5 and 10% of ash of rice rind in relation to the soil dry mass. The results of the testing program supported that the use of the residue was effective in increasing the degree of reactivity of the soil that was also directly related with the increase in the ash content and the period of cure of the mixtures.

Physicochemical and mechanical properties of zirconium oxide and niobium oxide modified Portland cement-based experimental endodontic sealers

Aim: To evaluate the physicochemical and mechanical properties of Portland cement-based experimental sealers (ES) with different radiopacifying agents (zirconium oxide and niobium oxide micro- and nanoparticles) in comparison with the following conventional sealers: AH Plus, MTA Fillapex and Sealapex. Methodology: The materials were tested for setting time, compressive strength, flow, film thickness, radiopacity, solubility, dimensional stability and formaldehyde release. Data were subjected to anova and Tukey tests (P < 0.05). Results: MTA Fillapex had the shortest setting time and lowest compressive strength values (P < 0.05) compared with the other materials. The ES had flow values similar to the conventional materials, but higher film thickness (P < 0.05) and lower radiopacity (P < 0.05). Similarly to AH Plus, the ES were associated with dimensional expansion (P > 0.05) and lower solubility when compared with MTA Fillapex and Sealapex (P < 0.05). None of the endodontic sealers evaluated released formaldehyde after mixing. Conclusion: With the exception of radiopacity, the Portland cement-based experimental endodontic sealers presented physicochemical properties according to the specifications no 57 ANSI/ADA (ADA Professional Product Review, 2008) and ISO 6876 (Dentistry - Root Canal Sealing Materials, 2012, British Standards Institution, London, UK). The sealers had setting times and flow ability that was adequate for clinical use, satisfactory compressive strength and low solubility. Additional studies should be carried out with the purpose of decreasing the film thickness and to determine the ideal ratio of radiopacifying agents in Portland cement-based root canal sealers. © 2013 International Endodontic Journal.

Properties of Mortar Using Cubes, Prism Halves, and Cylinder Specimens

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microparticulated and nanoparticulated zirconium oxide added to calcium silicate cement: Evaluation of physicochemical and biological properties

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural and optical properties of Cu2O crystalline electrodeposited films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of zirconium oxide and zinc oxide nanoparticles on physicochemical properties and antibiofilm activity of a calcium silicate-based material

The aim of the present study was to evaluate the antibiofilm activity against Enterococcus faecalis, compressive strength. and radiopacity of Portland cement (PC) added to zirconium oxide (ZrO2), as radiopacifier, with or without nanoparticulated zinc oxide (ZnO).The following experimental materials were evaluated: PC, PC + ZrO2, PC + ZrO2 + ZnO (5%), and PC + ZrO2 + ZnO (10%). Antibiofilm activity was analyzed by using direct contact test (DCT) on Enterococcus faecalis biofilm, for 5 h or 15 h. The analysis was conducted by using the number of colony-forming units (CFU/mL). The compressive strength was performed in a mechanical testing machine. For the radiopacity tests, the specimens were radiographed together with an aluminium stepwedge. The results were submitted to ANOVA and Tukey tests, with level of significance at 5%. The results showed that all materials presented similar antibiofilm activity (

Properties of one modified composite resin by TiO2 nanoparticles

The purpose of this study was to evaluate the compressive strength and color changes of one composite resin modified by TiO2 nanoparticles and their distribution by SEM.

Influence of addition of calcium oxide on physicochemical properties of Portland cement with zirconium or niobium oxide

Context: Calcium oxide (CaO) may be added to mineral trioxide aggregate (MTA) or Portland cement (PC) to improve physicochemical and biological properties. Aims: To evaluate the physicochemical properties of PC associated with radiopacifiers and CaO. Materials and Methods: MTA Angelus, PC + 30% zirconium oxide (Zr), or 30% niobium oxide (Nb) associated with 10 or 20% of CaO were evaluated. Gilmore needles were used to evaluate initial and final setting time. Compressive strength was evaluated after the periods of 24 hours and 21 days. pH was analyzed after 3, 12, 24 hours, 7, 14, 21 days. Solubility and flow tests were performed based on the ISO 6876. The data obtained were submitted to analysis of variance and Tukey tests (P ≤ 0.05). Results: The associations with 10% CaO showed greater strength that the associations with 20% CaO. The shortest initial setting time was observed for the association PC + Zr + 20% CaO and MTA. All the cements presented alkaline pH. The flow of all cements was similar. The highest solubility was found in the associations with 20% CaO. Conclusion: The addition of CaO to PC favored the alkaline property and the PC + Zr + 20% CaO presented setting time similar to MTA.

Addition of Chlorhexidine Gluconate to a Glass Ionomer Cement: A Study on Mechanical, Physical and Antibacterial Properties

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of water immersion and ultraviolet weathering on mechanical and viscoelastic properties of polyphenylene sulfide-carbon fiber composites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Foaming of EVA/starch blends: Characterization of the structure, physical properties, and biodegradability

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)