Microstructure evolution during warm deformation of low carbon steel with dispersed cementite

The microstructure evolution and mechanical behavior during large strain of a 0.16%C-Mn steel has been investigated by warm torsion tests. These experiments were carried out at 685°C at equivalent strain rate of 0.1 s . The initial microstructure composed of a martensite matrix with uniformly dispersed fine cementite particles was attained by quenching and tempering. The microstructure evolution during tempering and straining was performed through interrupted tests. As the material was reheated to testing temperature, well-defined cell structure was created and subgrains within lath martensite were observed by TEM; strong recovery took place, decreasing the dislocation density. After 1 hour at the test temperature and without straining, EBSD technique showed the formation of new grains. The flow stress curves measured had a peculiar shape: rapid work hardening to a hump, followed by an extensive flow-softening region. 65% of the boundaries observed in the sample strained to ε = 1.0 were high angle grain boundaries. After straining to ε = 5.0, average ferrite grain size close to 1.5 μm was found, suggesting that dynamic recrystallization took place. Also, two sets of cementite particles were observed: large particles aligned with straining direction and smaller particles more uniformly dispersed. The fragmentation or grain subdivision that occurred during reheating and tempering time was essential for the formation of ultrafine grained microstructure.

Grãos ultrafinos por laminação a morno e recozimento intercrítico

Grain refinement of low carbon steel via the warm deformation of martensite during torsion testing was investigated. At the beginning of straining, laths with high dislocation density were observed. After large deformations, a ferrite matrix with grain size close to 1μm and dispersed cementite particles were attained.

Efeitos dos tratamentos térmicos de normalização, resfriamento rápido e alívio de tensões no aço ASTM A-516 grau 70, utilizado na fabricação de vasos de pressão

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização microestrutural e mecânica de trilhos ferroviários soldados de topo por caldeamento

Pós-graduação em Engenharia Mecânica - FEIS

Second Phase Precipitation in Ultrafine-grained Ferrite Steel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Aplicação de cavacos de titânio para produção de revestimentos resistentes ao desgaste

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)