Evaluation of the pH, calcium release and antibacterial activity of MTA Fillapex

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

pH, Calcium Ion Release, and Setting Time of an Experimental Mineral Trioxide Aggregate-based Root Canal Sealer

Introduction: An experimental mineral trioxide aggregate sealer (MTAS) has been developed for use as a root canal sealer. The aim of this study was to evaluate the setting time, pH, and calcium ion release of MTAS compared with white Portland cement (CPB-40; Votorantin Cimentos, Camargo Correa SA, Pedro Leopoldo, MG, Brazil), white MTA Angelus (MTA; Angelus, Londrina, PR, Brazil), and AH Plus (Dentsply DeTrey, Konstanz, Germany). Methods: For the evaluation of setting time, each material was analyzed using Gilmore-type needles. Polyethylene tubes with the materials were immersed in distilled water for the measurement of pH (digital pH meter) and calcium release (atomic absorption spectrophotometry). The evaluations were performed at 3, 6, 12, 24, and 48 hours and 7, 14, and 28 days. Data were analyzed by analysis of variance and the Tukey test at 5% significance level. Results: MTAS showed higher calcium release at all experimental periods, a greater increase in pH up to 48 hours and the longest setting time. Conclusions: MTAS presented favorable properties for its indication as a root canal sealer. (J Endod 2011;37:844-846)

Evaluation of pH and Calcium Ion Release of Calcium Hydroxide Pastes Containing Different Substances

Introduction: The objective of this study was to evaluate the pH and calcium ion release of calcium hydroxide pastes associated with different substances. Methods: Forty acrylic teeth with simulated root canals were divided into 4 groups according to the substance associated to the calcium hydroxide paste: chlorhexidine (CHX) in 2 formulations (1% solution and 2% gel), Casearia sylvestris Sw extract, and propylene glycol (control). The teeth with pastes and sealed coronal accesses were immersed in 10 mL deionized water. After 10 minutes, 24 hours, 48 hours, and 7, 15, and 30 days, the teeth were removed to another container, and the liquid was analyzed. Calcium ion release was measured by atomic absorption spectrophotometry, and pH readings were made with a pH meter. Data were analyzed statistically by analysis of variance and Tukey test (alpha = 0.05). Results: Calcium analysis revealed significant differences (P < .05) for 1% CHX solution and 2% CHX gel at 10 minutes. After 24 hours, 2% CHX gel x Control and 2% CHX gel x 1% CHX solution differed significantly (P < .05). After 48 hours, there were significant differences (P < .05) for 2% CHX gel x Control and Extract x Control. No differences (P > .05) were observed among groups in the other periods. Regarding the pH, there were significant differences (P < .05) for 2% CHX gel x Control and 2% CHX gel x 1% CHX solution after 48 hours and for 2% CHX gel x Control after 15 days. In the other periods, no differences (P > .05) were observed among groups. Conclusions: All pastes behaved similarly in terms of pH and calcium ion release in the studied periods. (J Endod 2009;35:1274-1277)

Evaluation of pH and Calcium Ion Release of Root-end Filling Materials Containing Calcium Hydroxide or Mineral Trioxide Aggregate

Introduction: To evaluate calcium ion release and pH of Sealer 26 (S26) (Dentsply, Rio de Janeiro, RJ, Brazil), white mineral trioxide aggregate (MTA), Endo CPM Sealer (CPM1) (EGEO SRL Bajo licencia MTM Argentina SA, Buenos Aires, Argentina), Endo CPM Sealer in a thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE). Methods: Material samples (n = 10) were placed in polyethylene tubes and immersed in 10 mL of distilled water. After 3, 6,12,24, and 48 hours and 7,14, and 28 days, the water pH was determined with a pH meter, and calcium release was assessed by atomic absorption spectrophotometry. An empty tube was used as the control group. Results: The control group presented a pH value of 6.9 at all studied periods and did not show the presence of calcium ion. S26 presented greater hydroxyl ion release up to 12 hours (p < 0.05). From 24 hours until 28 days, S26, MTA, CPM1, and CPM2 had similar results. in ail periods, ZOE presented the lowest hydroxyl ion release. CPM1, followed by CPM2, released the most calcium ions until 24 hours (p < 0.05). Between 48 hours and 7 days, CPM1 and CPM2 had the highest release. A greater calcium ion release was observed for CPM2, followed by CPM1 at 14 days and for S26, CPM1, and CPM2 at 28 days. ZOE released the least calcium ions in all periods. Conclusion: Sealer 26, MTA, and Endo CPM sealer at normal or thicker consistency release hydroxyl and calcium ions. Endo CPM sealer may be an alternative as root-end filling material. (J Endod 2009;35:1418-1421)

Effects of coronal leakage on concentration of hydrogen ions and calcium hydroxide release of several calcium hydroxide pastes over different periods of time

Purpose: To evaluate the effects of coronal leakage on concentration of hydrogen ions (pH) and calcium release of several calcium hydroxide pastes, over different periods of time. Material and Methods: Fifty extracted human mandibular central incisors (n=10) were instrumented up to the F2 instrument and assigned to the following intracanal dressing: G1- Calen, G2- Calen with 0.4% chlorhexidine (CHX), G3- Calcium hydroxide with camphorated paramonochlorophenol (CPMC) and glycerin, G4- Calen, but temporary filling material maintained during all test (positive control) and G5- Root canal without intracanal dressing (negative control). All groups were immersed in distilled water for 7 days. In sequence, the temporary filling materials were removed, except in controls groups. All specimens were individually mounted on a specific device and only its root again immersed in distilled water. Concentration of hydrogen ions and calcium release by calcium hydroxide pastes in distilled water were evaluated in 24h, 7, 14 and 28 days. The results were submitted to ANOVA test (p = 0.05). After 28 days, root canals from experimental groups were examined in SEM. Results: G1, G2, G3 and G4 presented similar pH values and calcium release and did not differ from each other (p>0.05), up to 7 days. After this time G1, G2 and G3 presented values lower values than G4 (p<0.05). In SEM analysis, calcium hydroxide residues were observed in all experimental groups. Conclusions: After 7 days, coronal leakage decreased the concentration of hydrogen ions and calcium ion release provided by all calcium hydroxide pastes.

Effect of Ultrasonic Activation on pH and Calcium Released by Calcium Hydroxide Pastes in Simulated External Root Resorption

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Macrophage suppression following phagocytosis of apoptotic neutrophils is mediated by the S100A9 calcium-binding protein

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effects of calcium hydroxide addition on the physical and chemical properties of a calcium silicate-based sealer

Recently, various calcium silicate-based sealers have been introduced for use in root canal filling. The MTA Fillapex is one of these sealers, but some of its physicochemical properties are not in accordance with the ISO requirements. Objective: The aim of this study was to evaluate the flowability, pH level and calcium release of pure MTA Fillapex (MTAF) or containing 5% (MTAF5) or 10% (MTAF10) calcium hydroxide (CH), in weight, in comparison with AH Plus sealer. Material and Methods: The flowability test was performed according to the ISO 6876: 2001 requirements. For the pH level and calcium ion release analyses, the sealers were placed individually (n=10) in plastic tubes and immersed in deionized water. After 24 hours, 7 and 14 days, the water in which each specimen had been immersed was evaluated to determine the pH level changes and calcium released. Flowability, pH level and calcium release data were analyzed statistically by the ANOVA test (alpha=5%). Results: In relation to flowability: MTAF>AH Plus>MTAF5>MTAF10. In relation to the pH level, for 24 h: MTAF5=MTAF10=MTAF>AH Plus; for 7 and 14 days: MTAF5=MTAF10>MTAF>AH Plus. For the calcium release, for all periods: MTAF>MTAF5=MTAF10>AH Plus. Conclusions: The addition of 5% CH to the MTA Fillapex (in weight) is an alternative to reduce the high flowability presented by the sealer, without interfering in its alkalization potential.

Influence of the addition of calcium hydroxide powder on some physical and chemical properties of the sealer MTA fillapex

Objective: This study evaluated the flow, pH and calcium release of MTA Fillapex (G1) or Fillapex plus 10% in weight of calcium hydroxide powder (G2), compared to AH Plus (G3) and Sealapex (G4). Materials and methods:The flow test was performed according to ISO 6876:2001 requirements. The sealers were placed into plastic tubes and immersed in deionized water. After 24 hours, 7, 14 and 28 days, the water of each tube was removed and tested to evaluate the pH values and the level of released calcium. Calcium release values were analyzed statistically by Kruskal Wallis and Dunn tests and pH values analyzed by ANOVA and Tukey tests (? = 5%). Results:G1 presented higher flow among all sealers. The addition of 10% calcium hydroxide into MTA Fillapex reduced the flow (p < 0.05) but, in a level, that is lower than the one recommended for ISO norms. G2 and G4 presented pH values and calcium release higher than G3 (p < 0.05) in all periods. G1 presented pH value higher than G3 (p < 0.05), except in 7 days period (p > 0.05). G4 presented higher pH values than G1 and G2, but the calcium release was similar for all periods (p > 0.05). G3 presented lower calcium release among all groups (p < 0.05). Conclusion: The addition of 10% calcium hydroxide in MTA Fillapex caused reduction in flow and no negative interference in pH and/or calcium release. However, the obtained flow is different from ISO requirements. Clinical relevance: MTA Fillapex presents levels of flow above the ISO norms. The addition of calcium hydroxide is a suggestion for solving this problem, but the impact of these procedures should be carefully evaluated.

The association of chlorhexidine digluconate and calcium chloride to use as vehicle of a silicate calcium-based cement

Objective: The purpose of this study was to evaluate the influence of the addition of 2% chlorhexidine digluconate (CHX) associated with 5% calcium chloride (CaCl2 ) on antimicrobial activity, setting time, pH and calcium release of gray mineral trioxide aggregate (GMTA). Materials and Methods: GMTA powder was mixed with water, 2% CHX alone or 2% CHX combined with 5% CaCl2 . Antimicrobial activity was determined against Enterococcus faecalis (ATCC 29212) strains by agar diffusion test. Data obtained were submitted to kruskal wallis tests. Analysis of the setting time was evaluated by American society for testing and materials C266-03 requirements. The pH and calcium release analysis were evaluated, in 24 h, 7, 14 and 28 days using pH meter equipment and atomic absorption spectrophotometer, respectively. Data obtained were analyzed by ANOVA, in 5% significance level. Results: Significant differences were seen (P < 0.01) among the zones of bacterial growth inhibition produced by 5% CaCl2 + 2% CHX combination against E. faecalis when compared with water (P < 0.05). Regarding the setting time, that combination had the shortest setting time (P < 0.05). All associations were alkaline and released calcium. No statistical difference was observed between the experimental groups at the different periods of analysis (P > 0.05). Conclusion: Combination of 5% CaCl2 + 2% CHX reduced the setting time and enhanced the antimicrobial activity of GMTA without changing the pH and calcium release.

Impact of the in situ formed salivary pellicle on enamel and dentine erosion induced by different acids

Objective. To investigate and compare the protective impact of the in situ formed salivary pellicle on enamel and dentine erosion caused by different acids at pH 2.6. Methods. Bovine enamel and dentine samples were exposed for 120 min in the oral cavity of 10 healthy volunteers. Subsequently, enamel and dentine pellicle-covered specimens were extraorally immersed in 1 ml hydrochloric, citric or phosphoric acid (pH 2.6, 60 s, each acid n=30 samples). Pellicle-free samples (each acid n=10) served as controls. Calcium release into the acid was determined by atomic absorption spectroscopy. The data were analysed by two-way ANOVA and Tukey's test (alpha=0.05). Results. Pellicle-covered samples showed significantly less calcium loss compared to pellicle-free samples in all acid groups. The mean (SD) pellicle protection (% reduction of calcium loss) was significantly better for enamel samples [60.9 (5.3)] than for dentine samples [30.5 (5.0)], but revealed no differences among the acids. Conclusion. The efficacy of the in situ pellicle in reducing erosion was 2-fold better for enamel than for dentine. Protection of the pellicle was not influenced by the kind of acid when enamel and dentine erosion was performed at pH 2.6.

Evaluation of the physical and chemical properties of two commercial and three experimental root-end filling materials

Objective. The aim of this study was to evaluate the pH, calcium release, setting time, and solubility of two commercially available mineral trioxide aggregate (MTA) cements (white MTA Angelus and MTA Bio), and of three experimental cements (light-cured MTA, Portland cement with 20% bismuth oxide and 5% calcium sulfate, and an epoxy resin-based cement).Study design. For evaluation of pH and calcium ion release, polyethylene tubes with 1.0 mm internal diameter and 10.0 mm length were filled with the cements and immediately immersed in flasks containing 10 mL deionized water. After 3, 24, 72, and 168 hours, the tubes were removed and the water from the previous container was measured for its pH and calcium content with a pH meter and an atomic absorption spectrophotometer. For analysis of the setting time, Gilmore needles weighing 100 g and 456.5 g were used, in accordance with the American Society for Testing and Materials specification no. C266-03. Solubility of each cement was also tested.Results. All the cements were alkaline and released calcium ions, with a declining trend over time. After 3 hours, Portland cement + bismuth oxide and MTA Bio had the highest pH and light-cured MTA the lowest. After 1 week, MTA Bio had the highest pH and light-cured MTA and epoxy resin-based cement the lowest. Regarding calcium ion release, after 3 hours, Portland cement + bismuth oxide showed the highest release. After 1 week, MTA Bio had the highest. Epoxy resin-based cement and light-cured MTA had the lowest calcium release in all evaluation periods. Regarding setting times, white MTA Angelus and MTA Bio had the shortest, Portland cement + bismuth oxide had an intermediate setting time, and the epoxy resin-based cement had the longest. The materials that showed the lowest solubility values were the epoxy resin-based cement, Portland cement + bismuth oxide, and light-cured MTA. The highest solubility values were presented in white MTA Angelus and MTA Bio.Conclusions. The white MTA Angelus and MTA Bio had the shortest setting times, higher pH and calcium ion release, and the highest solubility. In contrast, the epoxy resin-based cement and light-cured MTA showed lower values of solubility, pH, and calcium ion release. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2010; 110: 250-256)

Evaluation of the propylene glycol association on some physical and chemical properties of mineral trioxide aggregate

Duarte MAH, Alves de Aguiar K, Zeferino MA, Vivan RR, Ordinola-Zapata R, Tanomaru-Filho M, Weckwerth PH, Kuga MC. Evaluation of the propylene glycol association on some physical and chemical properties of mineral trioxide aggregate. International Endodontic Journal, 45, 565570, 2012. Abstract Aim To evaluate the influence of propylene glycol (PG) on the flowability, setting time, pH and calcium ion release of mineral trioxide aggregate (MTA). Methodology Mineral trioxide aggregate was mixed with different proportions of PG, as follows: group 1: MTA + 100% distilled water (DW); group 2: MTA + 80% DW and 20% PG; group 3: MTA + 50% DW and 50% PG; group 4: MTA + 20% DW and 80% PG; group 5: MTA + 100% PG. The ANSI/ADA No. 57 was followed for evaluating the flowability and the setting time was measured by using ASTM C266-08. For pH and calcium release analyses, 50 acrylic teeth with root-end cavities were filled with the materials (n = 10) and individually immersed in flasks containing 10 mL deionized water. After 3 h, 24 h, 72 h and 168 h, teeth were placed in new flasks and the water in which each specimen was immersed had its pH determined by a pH metre and the calcium release measured by an atomic absorption spectrophotometer with a calcium-specific hollow cathode lamp. Data were analysed by using one-way anova test for global comparison and by using Tukeys test for individual comparisons. Results The highest value of flowability was observed with MTA + 20% DW and 80% PG and the lowest values were found with MTA + 100% DW. They were significantly different compared to the other groups (P < 0.05). The presence of PG did not affect the pH and calcium release. The MTA + 100% PG favoured the highest (P < 0.05) pH and calcium release after 3 h. Increasing the PG proportion interfered (P < 0.05) with the setting time; when used at the volume of 100% setting did not occur. Conclusion The addition of PG to MTA-Angelus increased its setting time, improved flowability and increased the pH and calcium ion release during the initial post-mixing periods. The ratio of 80% DW 20% PG is recommended.

Physico-chemical properties of MTA and a novel experimental cement

Aim: To evaluate the release of calcium ions, pH and conductivity of a new experimental dental cement (EC) and to compare them with those of mineral trioxide aggregate (MTA-Angelus). Methodology: Five samples of each cement were prepared using plastic tubes 1 mm in diameter and 10 mm long. Each sample was sealed in a test tube containing 10 mL deionized water which was analysed after 24, 48, 72, 96, 192, 240 and 360 h for pH, electrical conductivity and calcium release. The concentration of calcium ions was obtained through atomic absorption spectroscopy technique. The data were analysed statistically using the analysis of variance (ANOVA) and the Student's test (t-test). Results: The pH of the storage solutions was not affected by the material and the interaction of material with time (P > 0.05). However, the time of immersion was significant (P < 0.01) for both materials. For the electric conductivity and calcium release, the interaction of material with time was statistically significant (P < 0.01), indicating that EC and MTA-Angelus did not behave in a similar manner. Conclusions: The experimental cement released calcium and increased the pH of the storage solutions in a similar manner to MTA-Angelus. However, EC showed significantly higher calcium release than commercial MTA-Angelus after 24 h. © 2005 International Endodontic Journal.

Effect of different radiopacifying agents on the physicochemical properties of white portland cement and white mineral trioxide aggregate

Introduction: The aim of this study was to evaluate the pH, calcium ion release, setting time, and solubility of white mineral trioxide aggregate (WMTA) and white Portland cement (WPC) combined with the following radiopacifying agents: bismuth oxide (BO), calcium tungstate (CT), and zirconium oxide (ZO). Methods: Fifty acrylic teeth with root-end filling material were immersed in ultrapure water for measurement of pH and calcium release (atomic absorption spectrophotometry) at 3, 24, 72, and 168 hours. For evaluation of setting time, each material was analyzed according to the American Society for Testing and Materials guidelines 266/08. The solubility test was performed according to American National Standards Institute/American Dental Association specification no. 57/2000. Solubility, setting time, and pH values were compared by using analysis of variance and Tukey test, and the values of calcium release were compared by the Kruskal-Wallis and Miller tests. The significance level was set at 5%. Results: The pH and calcium release were higher at 3 and 24 hours. WPC was the material with the higher values for both properties. WMTA had the greatest solubility among all materials (P <.05). All radiopacifiers increased the setting time of WPC, and WMTA had the shortest setting time among all materials (P < .05). Conclusions: All materials released calcium ions. Except for WPC/CT at 168 hours, all materials promoted an alkaline pH. On the basis of the obtained results, ZO and CT can be considered as potential radiopacifying agents to be used in combination with Portland cement. Copyright © 2012 American Association of Endodontists.