Influence of annealing on X-ray diffraction of natural alexandrite

In this work we present results of X-ray diffraction using powder method, on natural alexandrite samples from Minas Gerais State (Brazil), as a function of a sequence of annealing. From these measurements we determine lattice parameters before (a = 9.405 Angstrom, b = 5.471 Angstrom, c = 4.409 Angstrom) and after annealing, and its structure is confirmed as orthorhombic. Measurements done after an annealing of 15 minutes at 700 degreesC and for 5 hours at 1000 degreesC indicate the migration of atoms present in the sample through different phases, which were also identified by Microprobe Analysis (WDS). However we have verified that such migration does not modify the structure. X-ray diffraction measurements have been carried out in conjunction with optical absorption in the UV-Vis as a function of annealing. (C) 2002 International Centre for Diffraction Data.

Annealing effects on optical properties of natural alexandrite

Natural alexandrite (BeAl2O4:Cr3+) crystals are investigated as regards the effects of annealing on their optical properties. Optical absorption spectra are measured from the ultraviolet (190 nm) to the near infrared (900 nm), for a sample subjected to consecutive annealing processes, where time and temperature are varied. Besides this, luminescence spectra are simultaneously obtained for this sample, excited with a Kr+ laser source, tuned on an ultraviolet multi-line mode (337.5, 350.7 and 356.4 nm). We observe from absorption as well as from emission data that annealing mainly influences the distribution of Cr3+ and Fe3+ ions, located on sites of a mirror plane (C-s symmetry), which are responsible for the optical properties of alexandrite. The results obtained lead to the conclusion that annealing induces a modification of the population of Cr3+ on C-s sites as well as on sites located on an inversion plane (C-i). Annealing could improve the optical properties of this material, as regards its application as a tunable laser.

Thermal annealing-induced electric dipole relaxation in natural alexandrite

Electrical properties of natural alexandrite (BeAl2O4:Cr3+) are investigated by the thermally stimulated depolarization current (TSDC) technique. Samples are submitted to consecutive annealing processes and TSDC is carried out after each annealing, yielding bands with different parameters. These bands are fitted by a continuous distribution of relaxation parameters: activation energy and pre-exponential factor of the Arrhenius equation. It has been observed that annealing influences the dipole relaxation behavior, since it promotes a modification of Fe3+ and C3+ impurity distributions on sites of distinct symmetry: Al-1 and Al-2. In order to have a reference for comparison, TSDC is also carried out on a synthetic alexandrite sample, where the only impurity present is Cr3+ ion.

TL, EPR and optical absorption studies on natural alexandrite compared to natural chrysoberyl

The TL, optical absorption (OA) and EPR properties of natural Brazilian alexandrite and chrysoberyl have been investigated. The TL measurements for natural alexandrite show five peaks between 100 and 450°C, with their emission spectrum having 370 and/or 570 nm components. The intensity of the 320°C TL peak was found to be enhanced with pre-annealing treatment, more prominently above 600°C. The OA and EPR measurements showed that this kind of heat treatment induces the Fe2→ Fe3+ conversion in the natural sample. Chrysoberyl samples exhibited the TL peaks at the same temperatures as alexandrite samples, but the glow curves were more than 200 times less intense than alexandrite ones.

Light-induced electric dipole relaxation in synthetic and natural alexandrite

We present results of thermally stimulated depolarization current (TSDC) measurements in synthetic and natural alexandrite, which show TSDC bands related to the presence of electric dipoles in both types of samples. Synthetic material shows a wide TSDC band with a peak at 179 K, which can be fitted by two distinct relaxing dipole distributions. For natural alexandrite the TSDC band has a maximum around 195 K and can be fitted by three different distributions. Both samples present one of the calculated curves with a peak about 179 K, with activation energy of 0.57 eV and constant relaxation time of 1 × 10-14 sec. Photo-induced TSDC shows that TSDC bands can also be generated by simultaneous application of light and an electric field at 77 K.

Cr+3 distribution in Al1 and Al2 Sites of alexandrite (BeAl2O4: Cr3+) induced by annealing, investigated by optical spectroscopy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Temperature Dependent Luminescence Spectra of Synthetic and Natural Alexandrite

Results of photoluminescence measurements for natural and synthetic alexandrite (BeAl2O4:Cr3+) are presented, where the samples are excited by the 488 nm line of an Ar+ laser, at different temperatures. The main issue is the analysis of the Cr3+ transition in the chrysoberyl matrix (BeAl2O4), with major technological application as active media for laser action. Results indicate anomalous behavior of Cr3+ transition depending on the measurement temperature. A simple model to explain the phenomena is suggested.

Investigação das propriedades ópticas e elétricas em alexandrita natural e sintética