Effect of microwave disinfection on the bond strength of denture teeth to acrylic resins

During microwave disinfection, the dentures are exposed to water at high temperature and this may affect the bond between the denture teeth and the acrylic resin from which dentures are made. In this study, a shear test was used to evaluate the effect of microwave disinfection (650W/6 min) on the bond strength of two types of denture teeth to three acrylic resins, with different polymerization methods. The specimens were submitted to the shear tests (0.5 mm/min) after: immersion in water (37 degrees C) for 48 h or 8 days (controls); two or seven cycles of microwave disinfection (test groups). Data (MPa) were analyzed using three-way ANOVA and Tukey HSD test (alpha = 0.05). Microwave disinfection did not adversely affect the bond strength of all tested materials with the exception of QC-20 bonded to SR Vivodent PE, for which a significant reduction was recorded after seven cycles of irradiation. (C) 2007 Elsevier Ltd. All rights reserved.

Microstructural, dielectric and ferroelectric properties of calcium-modified lead titanate thin films derived by chemical processes

Ferroelectric Pb1-xCaxTiO3 (x = 0.24) thin films were formed on a Pt/Ti/SiO2/Si substrate by the polymeric precursor method using the dip-coating technique for their deposition. Characterization of the films bq X-ray diffraction showed a perovskite single phase with a tetragonal structure after annealing at 700 degreesC. Atomic force microscopy (AFM) analyses showed that the film had a smooth and crack-free surface with low surface roughness. In addition, the PCT thin film had a granular structure with an 80 nm grain size. The thickness of the films observed by the scanning electron microscopy (SEM) is 550 nm and there is a good adhesion between the film and substrate. For the electrical measurements metal-ferroelectric-metal of the type capacitors were obtained, where the thin films showed good dielectric and ferroelectric properties. The dielectric constant and dissipation factor at 1 kHz and measured at room temperature were found to be 457 and 0.03. respectively. The remanent polarization and coercive field for the: deposited films were P-r = 17 muC/cm(2) and E-c = 75 kV/cm, respectively. Moreover. The 550-nm-thick film showed a current density in the order of 10(-8) A/cm(2) at the applied voltage of 2 V. The high values of the thin film's dielectric properties are attributed to its excellent microstructural quality and the chemical homogeneity obtained by the polymeric precursor method. (C) 2001 Elsevier science Ltd. All rights reserved.

Spatial choice is biased by chemical cues from conspecifics in the speckeled worm eel Myrophis punctatus

A enguia mirongo-mirim Myrophis punctatus vive em agrupamentos de alta densidade populacional e comumente se enterra ou permanece sob o substrato. Esses comportamentos podem levar a marcas químicas no subtrato e podem, portanto, modular o uso do espaço nessa espécie. Neste estudo, testamos a hipótese de que a preferência espacial da enguia mirongo-mirim é influenciada pela presença de odor do animal coespecífico no subtrato. Mostramos que as enguias evitam a área que contém tal odor, indicando que as decisões de ocupação espacial podem ser influenciadas por pistas químicas de coespecíficos. As enguias claramente detectaram o odor de um animal coespecífico e essa percepção poderia ser um indicativo da presença de um coespecífico enterrado no substrato. Visto que elas evitam uma área contendo tal odor, sugerimos que isso poderia ser uma resposta para evitar invadir o território de um animal residente.

Physical environment modulates the behavioral responses induced by chemical stimulation of dorsal periaqueductal gray in mice

In order to investigate the relationship between behaviors elicited by chemical stimulation of the dorsal periaqueductal gray (dorsal PAG) and spontaneous defensive behaviors to a predator, the excitatory amino acid D,L-homocysteic acid (5 nmol in 0.1 mu l), was infused into the dorsal PAG and behavioral responses of mice were evaluated in two different situations, a rectangular novel chamber or the Mouse Defense Test Battery (MDTB) apparatus. During a 1-min period following drug infusion, more jumps were made in the chamber than in the MDTB runway but running time and distance traveled were significantly higher in the runway. Animals were subsequently tested using the standard MDTB procedure (anti-predator avoidance, chase and defensive threat/attack). No drug effects on these measures were significant. In a further test in the MDTB apparatus, the pathway of the mouse during peak locomotion response was blocked 3 times by the predator stimulus (anesthetized rat) to determine if the mouse would avoid contact. Ninety percent of D,L-homocysteic treated animals made direct contact with the stimulus (rat), indicating that D,L-homocysteic-induced running is not guided by relevant (here, threat) stimuli. These results indicate that running as opposed to jumping is the primary response in mice injected with D,L-homocysteic into the dorsal PAG when the environment enables flight. However, the lack of responsivity to the predator during peak locomotion suggests that D,L-homocysteic-stimulation into the dorsal PAG does not induce normal antipredator flight. (c) 2006 Published by Elsevier B.V.

Pressure-induced electrical and structural anomalies in Pb1-xCaxTiO3 thin films grown at various oxygen pressures by chemical solution route

Lead calcium titanate (Pb1-xCaxTiO3 or PCT) thin films have been thermally treated under different oxygen pressures, 10, 40 and 80 bar, by using the so-called chemical solution deposition method. The structural, morphological, dielectric and ferroelectric properties were characterized by x-ray diffraction, FT-infrared and Raman spectroscopy, atomic force microscopy and polarization-electric-field hysteresis loop measurements. By annealing at a controlled pressure of around 10 and 40 bar, well-crystallized PCT thin films were successfully prepared. For the sample submitted to 80 bar, the x-ray diffraction, Fourier transformed-infrared and Raman data indicated deviation from the tetragonal symmetry. The most interesting feature in the Raman spectra is the occurrence of intense vibrational modes at frequencies of around 747 and 820 cm(-1), whose presence depends strongly on the amount of the pyrochlore phase. In addition, the Raman spectrum indicates the presence of symmetry-breaking disorder, which would be expected for an amorphous (disorder) and mixed pyrochlore-perovskite phase. During the high-pressure annealing process, the crystallinity and the grain size of the annealed film decreased. This process effectively suppressed both the dielectric and ferroelectric behaviour. Ferroelectric hysteresis loop measurements performed on these PCT films exhibited a clear decrease in the remanent polarization with increasing oxygen pressure.

Structural transition on Pb1-xSrxTiO3 produced by chemical method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of strontium addition on ferroelectric phase transition of PZT thin films prepared by chemical route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Changes in roughness of denture base and reline materials by chemical disinfection or microwave irradiation: Surface roughness of denture base and reline materials

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Interfacial concentrations of chloride and bromide in zwitterionic micelles with opposite dipoles: Experimental determination by chemical trapping and a theoretical description

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

SrZrO3 powders obtained by chemical method: Synthesis, characterization and optical absorption behaviour

Strontium zirconate (SrZrO3) powders have been synthesized by the polymeric precursor method after heat treatment at different temperatures for 2 h in oxygen atmosphere. The decomposition of precursor powder was followed by thermogravimetric analysis, X-ray diffraction (XRD) and Fourier transform Raman (FT-Raman). The UV-vis absorption spectroscopy measurements suggested the presence of intermediary energy levels in the band gap of structurally disordered powders. XRD, Rietveld refinement and FT-Raman revealed that the powders are free of secondary phases and crystallizes in the orthorhombic structure. (C) 2007 Elsevier Masson SAS. All rights reserved.

Dielectric properties of Ca(Zr0.05Ti0.95)O-3 thin films prepared by chemical solution deposition

Ca(Zr0.05Ti0.95)O-3 (CZT) thin films were grown on Pt(1 1 1)/Ti/SiO2/Si(1 0 0) substrates by the soft chemical method. The films were deposited from spin-coating technique and annealed at 928 K for 4 h under oxygen atmosphere. CZT films present orthorhombic structure with a crack free and granular microstructure. Atomic force microscopy and field-emission scanning electron microscopy showed that CZT present grains with about 47 nm and thickness about 450 nm. Dielectric constant and dielectric loss of the films was approximately 210 at 100 kHz and 0.032 at 1 MHz. The Au/CZT/Pt capacitor shows a hysteresis loop with remnant polarization of 2.5 mu C/cm(2), and coercive field of 18 kV/cm, at an applied voltage of 6 V. The leakage current density was about 4.6 x 10(-8) A/cm(2) at 3 V. Dielectric constant-voltage curve is located at zero bias field suggesting the absence of internal electric fields. (c) 2006 Elsevier B.V. All rights reserved.

SrBi2(Ta0.5Nb0.5)(2)O-9 : W thin films obtained by chemical solution deposition: Morphological and ferroelectric characteristics

The effect of tungsten (W6+) ion substituting on dielectric and ferroelectric behavior in SrBi2(Ta0.5Nb0.5)(2)O-9 (SBTN) thin films prepared by polymeric precursor method was investigated at room temperature. The addition of W6+ ion in the SBTN lattice was evaluated by X-ray diffraction (XRD), microstructural and dielectrical properties. An increase in the grain size is evident when tungsten is introduced in the SBTN lattice. Substitution of tungsten until 10% on B site leads to introduce space charge polarization into the system, resulting in an appreciable decrease in both dielectric constant and tangent loss. The morphology of the thin films investigated by atomic force microscopy leads to an increase in the grain size after tungsten addition. Fatigue resistance was noted with increase in tungsten addition. (C) 2007 Elsevier B.V. All rights reserved.

Piezoresponse behavior of niobium doped bismuth ferrite thin films grown by chemical method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Comparison of oxidation efficiency of disperse dyes by chemical and photoelectrocatalytic chlorination and removal of mutagenic activity

Degradation of Disperse Orange 1, Disperse Red 1 and Disperse Red 13 dyes has been performed using electrochemical oxidation on Pt electrode, chemical chlorination and photoelectrochemical oxidation on Ti/TiO(2) thin film electrodes in NaCl or Na(2)SO(4) medium. 100% discoloration was obtained for all tested methods after 1 h of treatment. Faster color removal was obtained by photoelectrocatalytic oxidation in 0.1 mol L(-1) NaCl pH 4.0 under UV light and an applied potential of +1.0V (vs SCE reference electrode), which indicates also values around 60% of TOC removal. The conventional chlorination method and electrochemical oxidation on Pt electrode resulted in negligible reduction of TOC removal. All dyes showed positive mutagenic activity in the Salmonella/microsome assay with the strain TA98 in the absence and presence of S9 (exogenous metabolic activation). Nevertheless, there is complete reduction of the mutagenic activity after 1 h of photoelectrocatalytic oxidation, suggesting that this process would be good option to remove disperse azo dyes from aqueous media. (C) 2008 Elsevier Ltd. All rights reserved.

Optical and structural properties of GaAs/GaInP quantum wells grown by Chemical Beam Epitaxy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)