Resistência mecânica da madeira de eucalyptus saligna unidas por adesivo poliuretano para diferentes acabamentos de superfície

Pós-graduação em Engenharia Mecânica - FEG

Fresamento de Eucalyptus grandis

The process of milling wood is widely used in operations such as planing and manufacturing frames . Machines like planers , desengrossadeiras , routers , moldureiras and machining centers employ the milling process for cutting wood . In this work the process of milling CNC machining center of Eucalyptus grandis was studied because this is very much used in furniture , but without consistent studies on this process . This work a CNC machining center brand TECH Z1 for analysis of surface quality ( Ra ) in relation to the variation of cutting speed and feed in concordant and discordant tangential milling and face milling was used . We used Eucalyptus grandis . Four forward speeds ( 3, 5 , 7, and 9 m / min ) for four shear rates ( 5,9; 8,4; 10,9 and 13,4 m/s ) were used. Was used for testing a cutter finishing top speed steel with helical teeth 16mm in diameter . 6 repetitions for each test condition were performed . From the results it was observed that the best results for roughness Vc = 10,9 m / s were obtained for the milling concordant with the forward speed Vf = 7 m / min. As for Vf = 5 m / min the best finish was achieved with Vc = 8,4 m /s in discordant for milling . The feedrate and cutting influenced the roughness . The senses of concordant and discordant and cut the top and the top had a significant difference in roughness

Lixamento do Pinus elliotti com carbeto de silício e óxido de aluminio

The Sanding is a complex process involving many variables that affect the quality of the part produced, working mainly in the timber industry in the production of panels (MDF, MDP, HDF, etc...) and furniture. However, these industries use the sanding process empirically, not optimizing it. The aim of this study was to compare the behavior of sandpaper white aluminum oxide (OA-white) and Black silicon carbide (SiC-black), analyzing variables in the process as: strength, power, emission, vibration, wear particle size of sanding, and its consequences on the surface finish of the workpiece. Made the process of plane grinding samples of Pinus elliottii, processed in parallel to the fibers, which were sanded with sandpaper grain OA white and black 3-SiC abrasive conditions (new, moderately eroded and severely eroded) grain sizes in 3 (80, 100, and 120 mesh). 6 replicates was performed for each condition tested. Each trial was captured output variables of the sanding process: strength, power, emission and vibration. With two stages totaling 108 trials. After the sanded samples, it has the same surface quality by raising the surface roughness Ra. Through experiment, it can be concluded that abrasives OA-white tended to have higher strength, power, emissions and less vibration in the sanding process, compared to the SiC-black. However, surface finish exhibited similar to the particle size of 80 to 100 mesh, worn abrasive conditions. However, the particle size of 120 mesh, obtained by the roughness of sandpaper OA-bank was higher compared to SiC-black to all conditions of sandpaper due to its toughness

Efeitos da variação do teor de umidade da madeira no processo de lixamento

The process of sanding wood is little known and industries use it in a practical way without having studied their best conditions before. There are few studies involving this type of machining. On this basis, this paper studied the effects of varying moisture content of the wood surface quality after the sanding process. It was used a sanding machine with flat horizontal cut parallel to the fibers, using: 02 different species (Pinus elliottii and Corymbia citriodora); 01 sanding abrasive (aluminum oxide) and 03 different particle size abrasives ( P80 , P100 and P120 ) . Initially, the pieces were acclimatized ( 2 ± 7% , 12% and 17% ± 2 ± 2 ) and subsequently passed by the sanding process, and therefore, the surface roughness was analyzed. For each condition, were performed 06 repetitions totaling 54 trials for each species. We analyzed the effects of wood moisture by capturing the power sanding, rougheness, acoustic emission and maximum temperature during the sanding process. The variation of moisture content produced changes in the surface quality of the finished parts, and these changes were more marked in Pinus than Corymbia. During the sanding process of the specimens with 7 % and 12 % humidity, there was a lower noise emission, power consumption and heating surface. When checking the roughness of these parts after this process, it was observed that the surface quality of them were superior in the parts sanded containing 17 % moisture