Microwave synthesis of YAG : Eu by sol-gel methodology

Yttrium-aluminum oxides are interesting compounds and they have been extensively used as host for lasers and phosphors, due to their stable physical and chemical properties. The fabrication of yttrium-aluminum garnet (YAG) has been investigated thoroughly. Single-crystal YAG is expensive and to produce it a new way has been investigated. This process consists of modifying the methodology of reagents mixture and the process of heating them. The microwave irradiation is used to heat-treat the oxide mixture. The traditional synthesis of YAG powders occurs through the reaction of aluminum and yttrium powders at high temperatures. With this work we investigated the preparation of YAG by non-hydrolytic sol-gel route as an alternative methodology to obtain yttrium-aluminum matrix from inorganic precursors (yttrium and aluminum chloride). The preparation of the gel was carried out in an oven-dried glassware. The AlCl3, YCl3 and ethanol were reacted in reflux under argon atmosphere. Europium III chloride was added as a structural probe. The powder was dried and heat-treated in modified microwaves. The samples were pre-treated at 50 and 800 C during I h and then heated in microwaves for 30 s, 2 and 4 min. The formation process and structure of the powders were studied by means of X-ray diffraction (XRD), photoluminescence (PL) and transmission electronic microscopy (TEM). XRD presents only picks corresponding to the YAG phase and confirmed by TEM. PL date showed that the YAG phase was formed in 2 min with the samples pre-treated at 50 C. For the samples pretreated at 800 degrees C, the YAG phase appears in 30s. The excitation spectra present a maximum of 394 nm corresponding to the L-5(6) level and emission spectra of Eu III ion present bands characteristic transitions arising from the D-5(0) -> F-7(J) (J= 1, 2, 3, 4) monifolds excited at their maximum. The magnetic dipole D-5(0) -> F-7(1) transition presents more intensity than the electric dipole D-5(0) -> F-7(2) transition. This methodology showed efficiency in obtaining YAG phase. (c) 2006 Elsevier B.V. All rights reserved.

Resistência de união de um sistema adesivo irradiado com laser Nd:YAG em dentina tratada com laser de Er:YAG

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Penetration of 35% hydrogen peroxide into the pulp chamber in bovine teeth after LED or Nd:YAG laser activation

This aim of the present study was to evaluate the pulp chamber penetration of 35% hydrogen peroxide activated by LED (light-emitting diode) or Nd:YAG laser in bovine teeth, after an in-office bleaching technique. Forty-eight bovine lateral incisors were divided into four groups, acetate buffer was placed into the pulp chamber and bleaching agent was applied as follows: for group A (n = 12), activation was performed by LED; for group B (n = 12), activation was performed by Nd:YAG laser (60 mJ, 20 Hz); group C (n = 12) received no light or laser activation; and the control group (n = 12) received no bleaching gel application or light or laser activation. The acetate buffer solution was transferred to a glass tube and Leuco Crystal Violet and horseradish peroxidase were added, producing a blue solution. The optical density of this solution was determined spectrophotometrically and converted into microgram equivalents of hydrogen peroxide. The results were analysed using ANOVA and Tukey's test (5%). It was verified that the effect of activation was significant, as groups activated by LED or laser presented greater hydrogen peroxide penetration into the pulp chamber (0.499 +/- 0.622 microg) compared with groups that were not (0.198 +/- 0.218 microg). There was no statistically significant difference in the penetration of hydrogen peroxide into the pulp chamber between the two types of activation (LED or laser). The results suggest that activation by laser or LED caused an increase in hydrogen peroxide penetration into the pulp chamber.

Crystal structure of mature 2S albumin from Moringa oleifera seeds

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)