Pulsed Nd:YAG laser seam welding of AISI 316L stainless steel thin foils

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effects of laser beam energy on the pulsed Nd:YAG laser welding of thin sheet corrosion resistant materials

The aim of this study was to value the possibility to join, for pulsed Nd:YAG laser welding, thin foils lap joints for sealing components in corrosive environment. Experimental investigations were carried out using a pulsed neodymium: yttrium aluminum garnet laser weld to examine the influence of the pulse energy in the characteristics of the weld fillet. The pulse energy was varied from 1.0 to 2.5 J at increments of 0.25 J with a 4 ms pulse duration. The base materials used for this study were AISI 316L stainless steel and Ni-based alloys foils with 100 mu m thickness. The welds were analyzed by electronic and optical microscopy, tensile shear tests and micro hardness. The results indicate that pulse energy control is of considerable importance to thin foil weld quality because it can generate good mechanical properties and reduce discontinuities in weld joints. The ultimate tensile strength of the welded joints increased at first and then decreased as the pulse energy increased. In all the specimens, fracture occurred in the top foil heat-affected zone next to the fusion line. The microhardness was almost uniform across the parent metal, HAZ and weld metal. A slight increase in the fusion zone and heat-affected zone compared to those measured in the base metal was observed. This is related to the microstructural refinement in the fusion zone, induced by rapid cooling of the laser welding. The process appeared to be very sensitive to the gap between couples.

Influência da energia de soldagem em uniões de lâminas finas através de laser pulsado de Nd:YAG

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Soldagem em laminas finas de hastelloy c-276 por laser pulsado Nd:YAG

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Pulsed Nd:YAG laser welding of Ni-alloy Hastelloy C-276 foils

In this study a pulsed Nd:YAG laser was used to join Hastelloy C-276 thin foil with 100 microns thickness. Pulse energy was varied from 1.0 to 2.25 J at small increments of 0.25 J with a 4 ms pulse duration. The macro and microstructures of the welds were analyzed by optical and electronic microscopy, tensile shear test and microhardness. Sound laser welds without discontinuities were obtained with 1.5 J pulse energy. Results indicate that using a precise control of the pulse energy, and so a control of the dilution rate, it is possible to weld Hastelloy C-276 thin foil by pulsed Nd: YAG laser. (C) 2012 Published by Elsevier B. V. Selection and/or review under responsibility of Bayerisches Laserzentrum GmbH

Application of pulsed Nd:YAG laser in thin foil microwelding

Experimental investigations were carried out using a Nd:YAG laser operating in pulsed mode for welding a lap joint between thin foil and thick sheet. The pulse energy was varied from 1.5 to 3.0 J at increments of 0.25 J with a 4 ms pulse duration. The base material used for this study was AISI 316L foils with 100 mu m thickness and sheet with 3.0 mm thickness. The welds were analysed by optical and electronic microscopy, tensile shear tests and micro hardness. The results indicate that pulse energy control is of considerable importance to join thin foil and thick sheet with good quality. The ultimate tensile strength of the welded joints increased at first and then decreased as the pulse energy increased. The process appeared to be very sensitive to the gap between couples. Large voids delimited by the molten zone boundary were observed in joints welded with high pulse energy.