Caracterização de estruturas de óxido de estanho modificado como sensores de gases

Pós-graduação em Química - IQ

Tin oxide nanoparticle formation using a surface modifying agent

This work presents results concerning the preparation of redispersible tin oxide nanoparticles achieved by using Tiron molecule ((OH)(2)C(6)H(2) (SO(3)Na)(2)) as surface modifying agent. The adsorption isotherm measurements show that an amount of 10 wt.% of Tiron is need to recover the SnO(2) nanoparticles surface with a monolayer. These nanoparticles can be easily redispersed in tetramethyl ammonium hydroxide at pH greater than or equal to11 until a powder concentration of 12 vol.% of tin. Under these conditions, hydrodynamic particle size is about 7 nm and increases until 52 nm at pH 6 due to the aggregation phenomenon. The time evolution of the viscoelastic properties indicates that the suspensions at pH 12.5, containing 12 vol.% tin oxide and 10 wt.% of surface modifier are kinetically stable. After thermal treatment at different temperature the powder characterisation evidences that the presence of Tiron monolayer at the nanoparticles surface increases the thermal stability of the porous texture and prevent the micropore size growth. This set of results contributes to satisfy the demand for more controlled synthesis of nanoparticles with high thermal stability as required for fabrication of ultrafiltration ceramic membranes. (C) 2004 Elsevier Ltd. All rights reserved.

Corrosion protection of fluorzirconate glasses coated by a layer of surface modified tin oxide nanoparticles

The protection efficiency against water corrosion of fluorozirconate glass, ZBLAN, dip-coated by nanocrystalline tin oxide film containing the organic molecule Tiron® was investigated by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). The chemical bonding structure of the surface region and morphology were studied before and after two water exposure periods of 5 and 30 min. The results of the analysis for the as-grown sample revealed a SnO1.6 phase containing carbon and sulfur, related to Tiron®, and traces of elements related to ZBLAN (Zr, F, Ba). This fact and the clear evidence of the presence of tin oxifluoride specie (SnOxF y) indicates a diffusion of the glass components into the porous coating. After water exposure, the increase of the oxygen concentration accompanied by a strong increase of Zr, F, Ba and Na content is interpreted as filling of the nanopores of the film by glass compounds. The formation of a compact protective layer is supported by the morphological changes observed by AFM. © 2005 Elsevier B.V. All rights reserved.

Surface-enhanced resonance Raman scattering: Single-molecule detection in a Langmuir-Blodgett monolayer

Surface-enhanced resonance Raman scattering (SERRS) is used for single-molecule detection from spatially resolved 1-mum(2) sections of a Langmuir-Blodgett (LB) monolayer deposited onto a Ag film. The target molecule, his (benzimidazo) thioperylene (BZP), is dispersed in an arachidic acid monomolecular layer containing one BZP molecule per mum(2) which is also the probing area of the Raman microscope. For concentrated samples (attomole quantities in the field of view), average SERRS, surface-enhanced fluorescence (SEF), and Raman imaging, including line mapping and global images at different temperatures, were recorded. Single-molecule SERRS spectra, obtained using an LB monolayer, present changes in bandwidth and relative intensities, highlighting the properties of single-molecule SERRS that are lost in average SERRS measurements of mixed LB monolayers obtained at the same temperatures. Also, the dilute system phenomenon of blinking is discussed with regard to results obtained from LB monolayers. The dilution process used in the single-molecule LB SERRS work is independently supported by fluorescence results obtained from very dilute solutions with monomer concentrations down to 10(-12) M.

Fast dynamics in the optical storage with Langmuir-Blodgett films of a diazocrown ether molecule

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Expression of nonclassical molecule human leukocyte antigen-G in oral lesions

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Morphological evolution of tin oxide nanobelts after phase transition

This article reports a study of the thermal stability and morphological changes in tin oxide nanobelts grown in the orthorhombic SnO phase. The nanobelts were heat-treated in a differential scanning calorimetry (DSC) furnace at 800 degrees C for I It in argon, oxygen, or synthetic air atmospheres. The samples were then characterized by DSC, X-ray diffraction (XRD), high resolution transmission electron microscopy (HRTEM), and high resolution field emission scanning electron microscopy (FE-SEM). The results confirmed that the orthorhombic SnO phase is thermodynamically unstable, causing the belts to transform into the SnO2 phase when heat-treated. During the phase transition, if oxygen is available in the furnace atmosphere, nanofibers grow at the edge of nanobelts at about 50 degrees of the belts' growth direction, while particles grow on the belt surface in the absence of oxygen. Although the decomposition process reduces the nanobelt cell volume by 22%, most belts remain monocrystalline after the heat treatment. The results confirm that phase transition is a decomposition process, which explains the morphological changes in the belts based on metallic tin generated in the process.

Crystallization and preliminary X-ray diffraction analysis of a Lys49-phospholipase A(2) complexed with caffeic acid, a molecule with inhibitory properties against snake venoms

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nitric oxide in plants: a brief discussion on this multifunctional molecule

Diversos estudos vêm sendo realizados com a finalidade de aumentar o conhecimento sobre a ocorrência e a atividade do óxido nítrico (ON) nas plantas. Nesse sentido, a presente revisão objetivou abordar alguns aspectos referentes ao on nas plantas, tais como propriedades químicas, vias de síntese, efeitos fisiológicos, ação antioxidante, transdução do sinal, interação com hormônios vegetais e expressão gênica. Nos últimos anos, muitos avanços têm sido obtidos em relação à síntese de on e seus efeitos fisiológicos nas plantas. Porém, os mecanismos moleculares que fundamentam seus efeitos permanecem pouco compreendidos. É sinalizada uma investigação em detalhes sobre as estreitas interações entre ON, Ca2+, ADP-ribose cíclica (cADPR) e proteínas quinases. Além disso, ainda não foi possível identificar uma enzima vegetal que apresente atividade semelhante à da óxido nítrico sintase (NOS). A elucidação de tais aspectos representa um desafio para futuros trabalhos.

Tetrachlorocarbonyliridates: Water-Soluble Carbon Monoxide Releasing Molecules Rate-Modulated by the Sixth Ligand

A new family of compounds is presented as potential carbon monoxide releasing molecules (CORMs). These compounds, based on tetrachlorocarbonyliridate(III) derivatives, were synthesized and fully characterized by X-ray diffraction, electrospray mass spectrometry, IR. NMR, and density functional theory calculations. The rate of CO release was studied via the myoglobin assay. The results showed that the rate depends on the nature of the sixth ligand, trans to CO, and that a significant modulation on the release rate can be produced by changing the ligand. The reported compounds are soluble in aqueous media, and the rates of CO release are comparable with those for known CORMs, releasing CO at a rate of 0.03-0.58 mu M min(-1) in a 10 mu M solution of myoglobin and 10 mu M of the complexes.

Effect of tartrate content on aging and deposition condition of copper-tin electrodeposits from a non-cyanide acid bath

The effect of the presence of tartrate additive on the chemical stability of a Cu-Sn acid bath was evaluated. It was observed that this additive hinders decomposition of the Cu/Sn deposition bath with storage time, since the decrease in electrochemical efficiency was attenuated. In addition, it was observed that optimal galvanostatic deposition with or without tartrate occurs at approximately 11 mA cm(-2). However, in the presence of tartrate the deposition charge was lower, leading to lower energy consumption. SEM analysis showed that the tartrate added to the plating bath caused a marked change in the morphology of the Cu/Sn films obtained gal vanostatic ally. (C) 2002 Elsevier B.V. B.V. All rights reserved.

A Model Coupling Vibrational and Rotational Motion for the DNA Molecule

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Statistics and kinetics of single-molecule electron transfer dynamics in complex environments: A simulation model study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Positronium impact excitation of hydrogen molecule to B-1 Sigma(+)(u) and b(3)Sigma(+)(u) states

Calculation for the electronic excitation of the ground state of H-2 to B (1) Sigma(u)(+) and b(3) Sigma(u)(+) states by positronium- (Ps) atom impact has been carried out using the first Born approximation considering discrete Ps excitations up to n = 6 and Ps ionization in the final state. To include the effect of electron exchange, we propose an alternative approximation scheme in the light of the Rudge approach, which takes into account the composite nature of the Ps-atom projectile.

Positronium scattering by a hydrogen molecule including exchange

We perform a three-positronium (Ps) state [Ps(ls,2s,2p)] coupled-channel calculation of Ps-H-2 scattering including the effect of electron exchange. At medium energies, higher excitations and ionization of Ps are treated within the framework of the first Born approximation. In both cases exchange is included using a recently proposed nonlocal model exchange potential which is free of non-orthogonality problems common in the usual antisymmetrization scheme. The present total cross sections at low and medium energies are in encouraging agreement with experiment.