Investigation of electrical properties of tantalum doped SnO2 varistor system

Ta2O5 doped SnO2 varistor systems containing 0.5 mol% ZnO and 0.5 mol% Coo were prepared by mixed oxide method. Considering that ZnO and Coo oxides are densification additives only the SnO(2)center dot ZnO center dot CoO ceramics cannot exhibit electrical nonlinearity. A small amount of Ta2O5 improves the nonlinear properties of the samples greatly. The height and width of the defect barriers were calculated. It was found that samples doped with 0.05 mol% Ta2O5 exhibit the highest density (98.5%), the lowest electric breakdown field (E-b = 1100 V/cm) and the highest coefficient of nonlinearity (alpha = 11.5). The effect of Ta2O5 dopant could be explained by the substitution of Ta5+ by Sn4+. A grain-boundary defect barrier model for the SnO(2)center dot ZnO center dot CoO center dot Ta2O5 varistor system was also introduced. (c) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Mechanical damping of the snoek peak in tantalum - Oxygen system

Interstitial solutes in body-centered cubic metals, such as oxygen in tantalum, produce ideally Snoek effects when they are in solutions enough diluted. However, for higher concentration of these solutes, more complex relaxation process can occur, as interaction between interstitial solutes and dislocations. Anelastic relaxation measurements were carried out in polycrystalline tantalum samples, using torsion pendulum inverted, operating between 300 K and 680 K and oscillation frequencies in the hertz bandwidth, for three different experimental sample conditions: as received sample, annealed and annealed followed by a treatment in an oxygen atmosphere. These measurements have revealed the following behavior: the intensity of the internal friction peak associated to matrix-interstitial interaction Ta-O decreased between the first run and the next runs, and this phenomenon did not occur for the others conditions. The variation of relaxation strength of Ta-O peak, with number of runs is due to a decrease of an amount of oxygen in solid solution, which can be associated with the precipitation of new phases in Ta sample and with the trapping of oxygen atoms by dislocations.

Thermal and structural properties of tantalum alkali-phosphate glasses

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Wear resistance of experimental titanium alloys for dental applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Color tunability of intense upconversion emission from Er3+-Yb3+ co-doped SiO2-Ta2O5 glass ceramic planar waveguides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Stress induced ordering due to interstitial elements in Nb and Ta by frequency analysis

It is well known that the interstitial elements present in solid solution in metals interact with the matrix by a relaxation process known as stress induced ordering. Traditionally this relaxation process is observed in the internal friction measurements. It is a common practice that researchers present the results of the frequency together with internal friction without giving any analysis. In this work we apply an expression which relates the variation of frequency with temperature and analyse the experimental results cited in the literature of the relaxation process due to the stress induced ordering of oxygen and nitrogen present in niobium and tantalum.

Influence of Ta2O5 on the electrical properties of ZnO- and CoO-doped SnO2 varistors

SnO2-based varistors doped with 0.5% cobalt, 0.5% zinc and various tantalum amounts were prepared by the solid-state route. Experimental evidence shows that small quantities of Ta2O5 improve the nonlinear properties of the samples significantly. It was found that samples doped with 0.05 mol% Ta2O5 exhibit the highest density (98.5%), the lowest electric breakdown field (E-b = 1050 V/cm) and the highest coefficient of nonlinearity (alpha = 11.5). The effect of Ta2O5 dopant could be explained by the substitution of Ta5+ by Sn4+. (C) 2004 Elsevier Ltd and Techna S.r.l. All rights reserved.

Crystallographic, dielectric and optical properties of SrBi2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (PvTi/SiO2/Si), n-type (100)-oriented and p-type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P-r values of 6.24 muC/cm(2) and 31.5 kV/cm for the film annealed at 800 degreesC. The film deposited onto fused silica and treated at 700 degreesC presented around 80 % of transmittance.

Structural and Spectroscopic Properties of Luminescent Er3+-Doped SiO2-Ta2O5 Nanocomposites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Crystallographic, dielectric and optical properties of SrBi 2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (Pt/Ti/SiO 2 /Si), n -type (100)-oriented and p -type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P r values of 6.24 μC/cm 2 and 31.5 kV/cm for the film annealed at 800 C. The film deposited onto fused silica and treated at 700 C presented around 80% of transmittance. © 2002 Taylor & Francis.

Spectroscopic properties of Tm3+ doped fluoroindate glass

Optical absorption and fluorescence were investigated in Tm3+ doped fluoroindate glass. The spectroscopic parameters for transitions in the 4f11 configuration were determined. The fluorescence study revealed the origin of the frequency upconversion process as well as allowed to quantify the interaction between Tm3+ ions.

Histological analysis of the osseointegration of Ti-30Ta dental implants after surface treatment

Metallic biomaterials are used to reinforce or to restore the form and function of hard tissues. Implants and prosthesis are used to replace shoulders, knees, hips and teeth. When these materials are inserted in bone several biological reactions happen. This process can be associated to surface properties (topography, roughness and surface energy). In this work, the influence of biomimetic surface treatment in the osseointegration of Ti-30Ta dental implants was evaluated. Ingots were obtained from titanium and tantalum by using an arc-melting furnace. They were submitted to heat treatment at 1,100°C for 1 h, cooled in water and cold worked by swaging. Then, screw-shaped implants (2.0 mm diameter by 2.5 mm length) were manufactured and they were implanted in a rat's femur. Animals were divided into two groups: untreated (control group) and treated (biomimetic surface treatment). They were sacrificed 30 days after implantation. For histological analysis, implants with surrounding tissue were removed and immersed in formaldehyde. Samples were embedded in polymethyl methacrylate and after polymerization, cut with a saw, polished and mounted on glass slides. The results obtained suggest that biomimetic surface treatment was able to promote an increase osseointegration on the surface of dental implants. © Springer-Verlag Berlin Heidelberg 2013.

Crescimento da nanoapatita na liga Ti-30Ta, para aplicações odontológicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação de filmes finos ferroelétricos de SrBi2'('TA IND.1-x''NB IND.x)ÍND.2 'O IND.9' puro e dopado com tungstênio, obtidos pelo método dos precursores poliméricos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ensaio de citotoxicidade osteoblástica em amostras porosas das ligas Ti-6Al-4V, Ti-13Nb-13Zr, Ti-35Nb, Ti-35Nb-7Zr-5Ta e TiCP

Pós-graduação em Biopatologia Bucal - ICT