Relationship between the surface chemical composition of implants and contact with the substrate

The purpose of the study was to use scanning electron microscopy and energy dispersive x-ray spectrometry to assess possible morphologic and chemical changes after performing double-insertion and pullout tests of implants of different shapes and surface treatments. Four different types of implants were used—cylindrical machined-surface implants, cylindrical double-surface–treated porous implants, cylindrical surface-treated porous implants, and tapered surface-treated porous implants—representing a total of 32 screws. The implants were inserted into synthetic bone femurs, totaling 8 samples, before performing each insertion with standardized torque. After each pullout the implants were analyzed by scanning electron microscopy and energy dispersive x-ray spectrometry using a universal testing machine and magnified 35 times. No structural changes were detected on morphological surface characterization, only substrate accumulation. As for composition, there were concentration differences in the titanium, oxygen, and carbon elements. Implants with surface acid treatment undergo greater superficial changes in chemical composition than machined implants, that is, the greater the contact area of the implant with the substrate, the greater the oxide layer change. In addition, prior manipulation can alter the chemical composition of implants, typically to a greater degree in surface-treated implants.

Persistence of endodontic methacrylate-based cement residues on dentin adhesive surface treated with different chemical removal protocols

The aim of this study was to evaluate the persistence of methacrylate-based cement residues on the dentin, after dentin surface cleaning with ethanol or acetone, with or without previous application of a dentin adhesive. Forty bovine crown fragments were obtained and the dentin surface was washed with 1.0 mL of 2.5% sodium hypochlorite (NaOCl), followed by 0.1 mL of 17% ethylenediaminetetraacetic acid application for 3 min, and final irrigation with 2.5% NaOCl. The specimens were air dried and resin-based cement was rubbed onto the dentine surface with a microbrush applicator. In 20 specimens, previously to cement, a dentin adhesive was applied in all surfaces. After 15 min, the surface was scrubbed with a cotton pellet and moistened with ethanol or acetone, compounding the following groups: G199.5% ethanol and G2acetone, without previous use of dentin adhesive; G399.5% ethanol and G4acetone, with previous use of dentin adhesive. The dentin surface was scrubbed until the cement residues could not be visually detected. Sections were then processed for scanning electron microscopy and evaluated at 500x magnification and scores were attributed to each image according to the area covered by residual sealer, and data were subjected to KruskalWallis at 5% significance. The lower residue presence was observed in G3 (P = 0.005). All surface presented cement residues when acetone was used as cleaning solution (P = 0.0005). The cleaning solutions were unable to completely remove the cement residues from both surfaces. The ethanol used after previous application of the dentin adhesive promoted the lower presence of residues.

Effects of Dextrose and Lipopolysaccharide on the Corrosion Behavior of a Ti-6Al-4V Alloy with a Smooth Surface or Treated with Double-Acid-Etching

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bone apposition and surface treatment in dental implants: histomorphometric pilot evaluation in rabbits

The surface of dental implants is an important factor for osseointegration process and different methods of surface treatment have been described. Objective: To investigate the bone apposition in implant surface treated with sandblasting and acid-etching. Material and methods: Ten rabbits were selected and received one implant treated with method I in the left tibia and one implant treated with method II in the right tibia. Then, twenty implants were divided in two groups, according to methods of sandblasting and acid-etching (method I and method II). After 7, 14, 30, 45 and 60 days, tibias were retrieved and submitted to histotechnical procedures. The percentages of bone–implant contact (BIC) and bone area between threads (BABT) were determined throughout histomorphometric analysis and bone apposition was detected in implants of both groups. Results: In BABT measurements, an increase was observed after 45 and 60 days in the method II, compared to method I and no differences were found after 7, 14 and 30 days. In BIC measurements, an increase was detected with method II at 45 days when compared to method I. No differences between groups in BIC values were observed after 7, 14, 30 and 60 days. Conclusion: Our data demonstrated that implants treated with the method II presented increase in the contact between bone and implant after 45 days compared to method I. Moreover, with concern to bone area between threads, it was observed an increased in the method II after 45 and 60 days. However, both groups can be successfully used as a therapeutic strategy to rehabilitation of edentulous patients. Then, further experiments are needed to evaluate, in depth, the putative differential role of each surface treatment.

Longevity of dental implants in type IV bone: a systematic review

Bone quality and quantity are important factors with regard to the survival rate of dental implants. The aim of this study was to conduct a systematic review of dental implants inserted in low-density bone and to determine the survival rate of dental implants with surface treatments over time. A systematic review of the literature was undertaken by two independent individuals; the Medline/PubMed database was searched for the period July 1975 to March 2013. Relevant reports on bone quality and osseointegration of dental implants were selected. The search retrieved 1018 references, and after inclusion and exclusion criteria were applied, 19 studies were selected for review. A total of 3937 patients, who had received a total of 12,465 dental implants, were analyzed. The survival rates of dental implants according to the bone density were: type I, 97.6%; type II, 96.2%; type III, 96.5%; and type IV, 88.8%. The survival rate of treated surface implants inserted in low-density bone was higher (97.1%) than that of machined surface implants (91.6%). Surface-treated dental implants inserted in low-density bone have a high survival rate and may be indicated for oral rehabilitation. However, more randomized studies are required to better evaluate this issue.

Influence of cyclosporin A on quality of bone around integrated dental implants: a radiographic study in rabbits

To evaluate the influence of cyclosporin A (CsA) administration on bone around integrated dental implants assessed by a bone quality index and by quantitative subtraction radiography.A total of 36 machine surface commercial implants were placed in 18 adult rabbits. After a 3-month healing period without any disturbance, the animals were randomly divided into three groups of six animals each. Group A was sacrificed at this time. CsA was injected subcutaneously in an immunosuppressive dose of 10 mg/kg/day in a test group (Group T), and a Group B served as a control, receiving only vehicle. After 3 months of cyclosporin administration, the animals of both Groups B and T were sacrificed. Radiographs were obtained at implant surgery and at the day of sacrifice with a CMOS sensor. Bone quality around the implants was compared between the groups using a bone quality index and quantitative subtraction radiography.The bone analysis showed that in Group T, the bone quality changed dramatically from a dense cortical to a loose trabecular bone structure (P < 0.0001, chi(2) test) while in Groups A and B there were no significant differences. Quantitative digital subtraction radiography showed significantly (P < 0.05) lower gray shade values (radiographic density) in a region of bone formation around the implants in Group T (118 +/- 12) than in Groups A (161 +/- 6) and B (186 +/- 10).Within the limits of this study, CsA administration has a negative effect on the quality of bone around integrated dental implant.

Argon-based atmospheric pressure plasma enhances early bone response to rough titanium surfaces

This study investigated the effect of an Argon-based atmospheric pressure plasma (APP) surface treatment operated chairside at atmospheric pressure conditions applied immediately prior to dental implant placement in a canine model. Surfaces investigated comprised: rough titanium surface (Ti) and rough titanium surface + Argon-based APP (Ti-Plasma). Surface energy was characterized by the Owens-Wendt-Rabel-Kaelble method and chemistry by X-ray photoelectron spectroscopy (XPS). Six adult beagles dogs received two plateau-root form implants (n = 1 each surface) in each radii, providing implants that remained 1 and 3 weeks in vivo. Histometric parameters assessed were bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). Statistical analysis was performed by Kruskall-Wallis (95% level of significance) and Dunn's post-hoc test. The XPS analysis showed peaks of Ti, C, and O for the Ti and Ti- Plasma surfaces. Both surfaces presented carbon primarily as hydrocarbon (C?C, C?H) with lower levels of oxidized carbon forms. The Ti-Plasma presented large increase in the Ti (+11%) and O (+16%) elements for the Ti- Plasma group along with a decrease of 23% in surface-adsorbed C content. At 1 week no difference was found in histometric parameters between groups. At 3 weeks significantly higher BIC (>300%) and mean BAFO (>30%) were observed for Ti-Plasma treated surfaces. From a morphologic standpoint, improved interaction between connective tissue was observed at 1 week, likely leading to more uniform and higher bone formation at 3 weeks for the Ti-Plasma treated implants was observed. (C) 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part A 2012.

Biocompatilibidade in vivo de implantes de titânio submetidos ao processo biomimético

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Processo de reparo ósseo diante de três tipos de superfície de titânio: análise histomorfométrica e por microscopia eletrônica de varredura associada ao EDS: estudo experimental

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Repair of composites: Effect of laser and different surface treatments

Objectives: This study investigated the repairs of resin composite restorations after using different surface treatments.Design: Eighty four truncated cones of Filtek Z350 were prepared and thermo-cycled (20,000 cycles). Surfaces were roughened with diamond bur and etched with 37% phosphoric acid. Those cones were divided into 7 groups (N=12): 1) Prime&Bond 2.1; 2) aluminum oxide sandblasting+Prime&Bond 2.1; 3) Er:YAG laser treatment+Prime&Bond 2.1; 4) 9.6% hydrofluoric acid for 2 min-Fsilane coupling agent.; 5) silane coupling agent; 6) auto-polymerized acrylic monomer+Prime&Bond 2.1; 7) Adper Scothbond SE. Teflon device was used to fabricate inverted truncated cones of repair composite over the surface-treated. The bonded specimens were stressed to failure under tension. The data were analyzed with oneway ANOVA and Tukey tests.Results: Mean repair strengths (SD, in MPa) were, Group-2: 18.8a; Group-1: 18.7a; Group-6: 13.4ab; Group-7: 9.5bc; Group-3: 7.5bcd; Group-4: 5.2cd; Group-5: 2.6d.Conclusions: The use of diamond bur and a conventional adhesive and the use of aluminum oxide sandblasting prior to adhesive provided a simple and cost-effective solutions to composite repair. Er:YAG laser, silane alone, 9.6% hydrofluoric acid plus silane or a self-etching adhesive results in inferior composite repair strengths. (C) 2015 Elsevier Ltd. All rights reserved.

Effect of Airborne-Particle Abrasion and Mechanico-Thermal Cycling on the Flexural Strength of Glass Ceramic Fused to Gold or Cobalt-Chromium Alloy

Purpose: To evaluate the effect of airborne-particle abrasion and mechanico-thermal cycling on the flexural strength of a ceramic fused to cobalt-chromium alloy or gold alloy.Materials and Methods: Metallic bars (n = 120) were made (25 mm x 3 mm x 0.5 mm): 60 with gold alloy and 60 with Co-Cr. At the central area of the bars (8 mm x 3 mm), a layer of opaque ceramic and then two layers of glass ceramic (Vita VM13, Vita Zahnfabrick) were fired onto it (thickness: 1 mm). Ten specimens from each alloy group were randomly allocated to a surface treatment [(tungsten bur or air-particle abrasion (APA) with Al(2)O(3) at 10 mm or 20 mm away)] and mechanico-thermal cycling (no cycling or mechanically loaded 20,000 cycles; 10 N distilled water at 37 degrees C and then thermocycled 3000 cycles; 5 degrees C to 55 degrees C, dwell time 30 seconds) combination. Those specimens that did not undergo mechanico-thermal cyclingwere stored inwater (37 degrees C) for 24 hours. Bond strength was measured using a three-point bend test, according to ISO 9693. After the flexural strength test, failure types were noted. The data were analyzed using three factor-ANOVA and Tukey's test (alpha = 0.05).Results: There were no significant differences between the flexural bond strength of gold and Co-Cr groups (42.64 +/- 8.25 and 43.39 +/- 10.89 MPa, respectively). APA 10 and 20 mm away surface treatment (45.86 +/- 9.31 and 46.38 +/- 8.89 MPa, respectively) had similar mean flexural strength values, and both had significantly higher bond strength than tungsten bur treatment (36.81 +/- 7.60 MPa). Mechanico-thermal cycling decreased the mean flexural strength values significantly for all six alloy-surface treatment combinations tested when compared to the control groups. The failure type was adhesive in the metal/ceramic interface for specimens surface treated only with the tungsten bur, and mixed for specimens surface treated with APA 10 and 20 mm.Conclusions: Considering the levels adopted in this study, the alloy did not affect the bond strength; APA with Al(2)O(3) at 10 and 20 mm improved the flexural bond strength between ceramics and alloys used, and the mechanico-thermal cycling of metal-ceramic specimens resulted in a decrease of bond strength.

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resin

Effect of the addition of silanated silica on the mechanical properties of microwave heat-cured acrylic resinObjectives: The purpose of this study was to evaluate the flexural strength and Vickers hardness of a microwave energy heat-cured acrylic resin by adding different concentrations of silane surface-treated nanoparticle silica.Methods: Acrylic resin specimens with dimensions of 65 x 10 x 2.5 mm were formed and divided into five experimental groups (n = 10) according to the silica concentration added to the acrylic resin mass (weight %) prior to polymerisation : G1, without silica; G2, 0.1% silica; G3, 0.5% silica; G4, 1.0% silica; and G5, 5.0% silica. The specimens were submitted to a three-point flexural strength test and to the Vickers hardness test (HVN). The data obtained were statistically analysed by ANOVA and the Tukey test (alpha = 0.05).Results: Regarding flexural strength, G5 differed from the other experimental groups (G1, G2, G3 and G4) presenting the lowest mean, while G4 presented a significantly higher mean, with the exception of group G3. Regarding Vickers hardness, a decrease in values was observed, in which G1 presented the highest hardness compared with the other experimental groups.Conclusion: Incorporating surface-treated silica resulted in direct benefits in the flexural strength of the acrylic resin activated by microwave energy; however, similar results were not achieved for hardness.

Reimplante dentário tardio após o tratamento da superfície radicular com hipoclorito de sódio e fluoreto de sódio: análise histomorfométrica em ratos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influência da espessura da cerâmica, do tempo de fotopolimerização e do cimento resinoso na resistência de união à microtração de uma cerâmica vítrea cimentada à dentina humana

Pós-graduação em Odontologia Restauradora - ICT