Influence of surface sealant on the translucency of composite resin: effect of immersion time and immersion media

This study evaluated the effect of surface sealant on the translucency of composite resin immersed in different solutions. The study involved the following materials: Charisma, Fortify and coffee, Coca-Cola®, tea and artificial saliva as solutions. Sixty-four specimens (n = 8) were manufactured and immersed in artificial saliva at 37 ± 1 °C. Samples were immersed in the solutions for three times a day and re-immersed in artificial saliva until the translucency readings. The measurements were carried out at nine times: T1 - 24 hours after specimen preparation, T2 - 24 hours after immersion in the solutions, T3 - 48 hours and T4 to T9 - 7, 14, 21, 30, 60 and 90 days, respectively, after immersion. The translucency values were measured using a JOUAN device. The results were subjected to ANOVA and Tukey's test at 5%. The surface sealant was not able to protect the composite resin against staining, the coffee showed the strongest staining action, followed by tea and regarding immersion time, a significant alteration was noted in the translucency of composite resin after 21 days.

Effect of the composite surface sealant application moment on marginal sealing of compactable composite resin restoration

An analysis was carried out to observe whether the application or not of a composite surface sealant (CSS), as well the moment for CSS application were able to reduce marginal microleakage in compactable composite resin restoration. All the preparations were restored with a compactable composite resin. The restored teeth were randomly assessed. G1 (control group): finished and polished; G2: finished, polished, etched and cover with CSS; G3: immediately after the restoration done the CSS was applied, then finished and polished; G4: CSS applied immediately after the restoration was done, the finished and polished, etched, and covered with CSS. The specimens were isolated with nail polish, thermocycled, immersed in aqueous solution of silver nitrate, and followed in a photo developing solution. The microleakage scores obtained from the occlusal and cervical walls were analyzed with the Kruskall-Wallis nonparametric test. No microleakage was found at the enamel margins. Comparing the microleakage scores at dentin/cementum margins (p < 0.05) it was found that G3 (p = 0.0162) and G4 (p = 0.0187) were able to reduce microleakage when compared with group G2. However the results were not statistically different from the control group. The application of CSS was not able to completely eliminate marginal microleakage at the dentin/cementum margins.

Fluorescence Intensity of Composite Layering Combined with Surface Sealant Submitted to Staining Solutions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In vitro evaluation of surface roughness of 4 resin composites after the toothbrushing process and methods to recover superficial smoothness.

OBJECTIVE: This study evaluated the efficiency of repolishing, sealing with surface sealant, and the joining of both in decreasing the surface roughness of resin-based composites after a toothbrushing process. METHOD AND MATERIALS: Ten specimens of each composite (Alert, Z100, Definite, and Prodigy Condensable), measuring 2 mm in thickness and 4 mm in diameter, were made and submitted to finishing and polishing processes on both sides of the specimens using the Sof-Lex system. The specimens were then subjected to toothbrushing (30,000 cycles), and surface roughness (Ra) was analyzed with a Surfcorder SE 1700 profilometer. The upper surface of each composite was etched with 37% phosphoric acid, and the surface-penetrating sealant Protect-it was applied on 1 surface. The roughness of these surfaces was again measured. On the other side, the surface of the specimen was repolished, and the efficiency of this procedure was measured using the profilometer. The surface roughness resulting from the joining of the 2 methods was verified by applying, in the final stage, the surface-penetrating sealant on the repolished surface. Data were analyzed with analysis of variance and Tukey test (P <.05). RESULTS: Results showed that the lowest surface roughness values were obtained for Definite, Z100, and Prodigy Condensable after the repolishing process and after the repolishing plus sealing. For Alert, the joining of repolishing plus sealing promoted the lowest values of surface roughness. CONCLUSION: Of the resin-based composites, Alert demonstrated the highest values of surface roughness in all the techniques tested.

Abrasion resistance of direct and indirect resins as a function of a sealant veneer

Abrasive wear is one of the most common type of wear that not only affect teeth, as also dental restorations. Thus to investigate one of the etiological factors as tooth brushing procedure is clinical relevant in order to select the best material combination that may prevent damage of resin dental restoration's abrasion. This study evaluated the influence of tooth brushing on mass loss and surface roughness of direct Venus (Vs) and indirect Signum (Sg) resin composites, with and without a surface sealant, Fortify (F). Twenty-four specimens were prepared with each resin composite, using their proprietary curing units, according to manufacturer's instructions. All the specimens were polished and ultrasonically cleaned in distilled water for 5 minutes. Half of the specimens of each resin (n = 12) were covered with F (Vs F and Sg F ), except for the control (C) specimens (Vs C and Sg C ), which were not sealed. Mass loss (ML) as well as surface roughness (Ra ) was measured for all the specimens. Then, the specimens were subjected to toothbrush-dentifrice abrasion, using a testing machine for 67.000 brushing strokes, in an abrasive slurry. After brushing simulation, the specimens were removed from the holder, rinsed thoroughly and blot dried with soft absorbent paper. The abrasion of the material was quantitatively determined with final measurements of ML and surface roughness, using the method described above. ML data were analyzed by two-way analysis of variance (ANOVA) and the analysis indicated that resin composites were not statistically different; however, the specimens sealed with F showed higher ML. Ra mean values of the groups Vs F and Sg F significantly increased. Tooth brushing affects mainly the roughness of the direct and indirect resin composites veneered with a sealant.

COLOR STABILITY of SEALED COMPOSITE RESIN RESTORATIVE MATERIALS AFTER ULTRAVIOLET ARTIFICIAL AGING and IMMERSION IN STAINING SOLUTIONS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Artificial Aging on the Roughness and Microhardness of Sealed Composites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência do selante de superfície em propriedades físicas e mecânicas de resinas compostas submetidas a envelhecimentos artificiais

Pós-graduação em Odontologia - FOA

Avaliação da influência do selante de superfície sobre a translucidez de resina composta. Efeito de tempos e soluções

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo da dureza e da resistência à compressão de resinas compostas para dentes posteriores após a imersão em água destilada. Efeito da aplicação de selante superficial

Novos compósitos têm surgido no mercado especificamente destinados à confecção de restaurações estéticas posteriores. Entretanto, embora tais materiais apresentem resultados iniciais animadores, há a necessidade de comprovações adicionais para que possam ser utilizados com segurança. Resinas compostas posteriores são submetidas a estresses complexos de compressão e abrasão durante a mastigação e a aplicação de selantes superficiais tem sido relatada como forma de aumentar a resistência ao desgaste destes materiais. O presente trabalho teve como propósito avaliar a dureza e a resistência à compressão das resinas compostas Alert (Jeneric/Pentron), Ariston (Vivadent), Definite (Degussa), P60 (3M), Solitarie (Kulzer), Surefil (Dentsply) e Z100 (3M) após 90 dias de imersão em água destilada, recobertas com selante Protect It (Jeneric/Pentron) e submetidas à ciclagem mecânica (10.000 ciclos, 600N, 5Hz). Os ensaios de dureza (n=8) foram realizados em aparelho Wolpert, com diamante Vickers e peso de 50gf aplicado por 30 segundos, antes e após períodos de imersão de 30, 60 e 90 dias. Os ensaios de resistência à compressão (n=8) foram realizados somente após 90 dias, em corpos-de-prova cilíndricos medindo 8mm de altura por 4mm de diâmetro. Apenas os espécimes destinados à compressão foram ciclados mecanicamente. Os ensaios foram realizados em máquina MTS 810, equipada com célula de carga de 10kN (ciclagem) e 100kN (compressão) e velocidade de 0,5mm/min. Após análise de variância (p<0,05), os resultados mostraram, previamente à imersão, maiores valores de dureza para os materiais Z100 (74,253VHN) e Ariston (71,308VHN). A seguir, com valor semelhante à resina Ariston, mas inferior à resina Z100, apresentou-se o material Surefil (69,969VHN)...(Resumo completo, clicar acesso eletrônico abaixo)

Measurement of sealant surface area by clinical/computerized analysis: 11-year results.

OBJECTIVE: To analyze the clinical behavior of 2 pit and fissure sealants through clinical/computerized evaluation. METHOD AND MATERIALS: Occlusal sealants were placed on maxillary and mandibular first and second premolars according to a split-mouth design. All premolars were sealed with either Concise (3M Espe) or Prisma Shield (Caulk/Dentsply) sealant agents. A hematoxylin-based staining solution was applied on the occlusal surface 7 days, 18 months, 36 months, and 11 years after occlusal sealing to allow checking of the sealant material on the surface. At each analysis time all occlusal surfaces were photographed, and the photographs corresponding to each time period were analyzed with SigmaScan 4.0 Software. The alterations of the sealed area of each sealant were analyzed with the software and recorded. Next, the measurements of the areas were tabulated and analyzed according to each period. Analysis of variance (ANOVA), with parts subdivided into time, and the t test, with a significance level of 5%, were used. RESULTS: The greatest sealed area was maintained by the sealant Concise. However, over the course of 11 years, all sealants began to show the same level of alteration in sealed area. CONCLUSION: The sealing materials showed alteration in sealed area over time, but they were efficient in controlling caries lesion formation on premolar pits and fissures.

Effect of fluid resins on the surface roughness and topography of resin composite restorations analyzed by atomic force microscope

The aim of the study was to verify the influence of surface sealants on the surface roughness of resin composite restorations before and after mechanical toothbrushing, and evaluate the superficial topography using atomic force microscope. Five surface sealers were used: Single Bond, Opti Bond Solo Plus, Fortify, Fortify Plus and control, without any sealer agent. The lowest values of surface roughness were obtained for control, Single Bond and Fortify groups before toothbrushing. Fortify and Fortify Plus were the sealer agents that support the abrasive action caused by the toothbrushing although Fortify Plus group remained with high values of surface roughness. The application of specific surface sealants could be a useful clinical procedure to maintain the quality of resin-based composite restorations. (C) 2010 Elsevier Ltd. All rights reserved.